CN103830962B - 一种堇青石复合陶瓷滤芯及其制备方法 - Google Patents

一种堇青石复合陶瓷滤芯及其制备方法 Download PDF

Info

Publication number
CN103830962B
CN103830962B CN201410073935.2A CN201410073935A CN103830962B CN 103830962 B CN103830962 B CN 103830962B CN 201410073935 A CN201410073935 A CN 201410073935A CN 103830962 B CN103830962 B CN 103830962B
Authority
CN
China
Prior art keywords
hour
filter core
cordierite
add
active charcoal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410073935.2A
Other languages
English (en)
Other versions
CN103830962A (zh
Inventor
张庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Baoyi Amusement Equipment Co Ltd
Original Assignee
Wuhu Baoyi Amusement Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Baoyi Amusement Equipment Co Ltd filed Critical Wuhu Baoyi Amusement Equipment Co Ltd
Priority to CN201410073935.2A priority Critical patent/CN103830962B/zh
Publication of CN103830962A publication Critical patent/CN103830962A/zh
Application granted granted Critical
Publication of CN103830962B publication Critical patent/CN103830962B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种堇青石复合陶瓷滤芯，其特征在于，由下列重量份的原料制备制成：堇青石13-15、莫来石9-11、粗孔硅胶6-8、蒙脱石4-7、活性氧化铝8-10、硫酸钙3-5、二甲基硅油2-3、海藻酸钠3-4、棕榈纤维3-5、尿素2-3、改性椰壳活性炭5-7、水适量；本发明添加粗孔硅胶，吸附性能高、热稳定性好、化学性质稳定、有较高的机械强度；添加棕榈纤维，增加了滤芯的韧性，同时具有多孔的性能，提高了过滤吸附性能；添加改性椰壳活性炭，空隙发达、吸附性能好、强度高、易再生、经济耐用；使用寿命长，耐腐蚀，可用作空气吸附过滤。

Description

一种堇青石复合陶瓷滤芯及其制备方法
技术领域
本发明涉及一种过滤材料及其制备方法，特别是一种堇青石复合陶瓷滤芯及其制备方法。
背景技术
过滤材料用途极为广泛，主要应用于涂料、油墨、染料、塑料、制药、电镀、饮料、化妆品、橡胶、印刷、电子管生产、线路板生产、垃圾焚烧、化工生产等各领域内。最常见的有过滤材料用于空气调节***，现在环境大气污染十分严重，雾霾天气给人们带来了极大的危害，空气吸附过滤材料能将空气的各种有害颗粒物，如PM2.5吸附，防止进入人们的生活或工作环境，减少人体肺部对颗粒物等有害物质的吸入，提高人们的生活质量，减少疾病的发生。现有过滤材料主要有蜂窝陶瓷、滤纸、活性炭、钢丝网等。现有蜂窝陶瓷过滤材料原料、配方、功能都比较单一，不能满足技术不断发展的要求。
发明内容
本发明的目的是提供一种堇青石复合陶瓷滤芯及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种堇青石复合陶瓷滤芯，由下列重量份的原料制备制成：堇青石13-15、莫来石9-11、粗孔硅胶6-8、蒙脱石4-7、活性氧化铝8-10、硫酸钙3-5、二甲基硅油2-3、海藻酸钠3-4、棕榈纤维3-5、尿素2-3、改性椰壳活性炭5-7、水适量；
所述改性椰壳活性炭由以下重量份的原料制成：粉碎椰壳20-25、氧化锆5-8、微粉硅胶3-5；制备方法是将粉碎椰壳用热水洗涤，然后在常温下用50-60%磷酸溶液浸泡1-2小时；过滤，取滤渣在550-600℃的炭化炉中炭化1.5-2小时，取出；待温度降至室温时与氧化锆、微粉硅胶混合均匀，再加入60%氢氧化钠搅拌1-1.5小时，然后过滤取出；用蒸馏水清洗3-4次，烘干即得。
本发明所述一种堇青石复合陶瓷滤芯，由以下具体步骤制成：
（1）将尿素加入适量的水，加热至溶解；将棕榈纤维放入粉碎机中粉碎，将除二甲基硅油、水以外的其余剩余成分放入球磨机中，球磨3-4小时，与粉碎的棕榈纤维混合均匀得到混合粉末；
（2）将混合粉末加入到溶解的尿素中搅拌均匀，得到混合浆料，然后将混合的浆料真空去泡2-3小时；
（3）将去泡的浆料注入模具中，在室温中蒸发水分，自动晾干后脱模，得到滤芯生胚；
（4）将生胚送入隧道式炉中常压下烧结，先在200-260℃下焙烧10-12小时，然后缓慢升温至500-560℃下焙烧4-5小时，然后，再以6-8℃/分钟速率升温至1100-1180℃，烧结3-4小时，冷却后取出，放入清水中浸泡1-2天后，取出烘干。
本发明的有益效果是：本发明添加粗孔硅胶，吸附性能高、热稳定性好、化学性质稳定、有较高的机械强度；添加棕榈纤维，增加了了滤芯的韧性，同时具有多孔的性能，提高了过滤吸附性能；添加改性椰壳活性炭，空隙发达、吸附性能好、强度高、易再生、经济耐用；使用寿命长，耐腐蚀，可用作空气吸附过滤。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种堇青石复合陶瓷滤芯，由下列重量份（公斤）的原料制备制成：堇青石13、莫来石9、粗孔硅胶6、蒙脱石4、活性氧化铝8、硫酸钙3、二甲基硅油2、海藻酸钠3、棕榈纤维3、尿素2、改性椰壳活性炭5、水适量；
所述改性椰壳活性炭由以下重量份（公斤）的原料制成：粉碎椰壳20、氧化锆5、微粉硅胶3；制备方法是将粉碎椰壳用热水洗涤，然后在常温下用50-60%磷酸溶液浸泡1-2小时；过滤，取滤渣在550-600℃的炭化炉中炭化1.5-2小时，取出；待温度降至室温时与氧化锆、微粉硅胶混合均匀，再加入60%氢氧化钠搅拌1-1.5小时，然后过滤取出；用蒸馏水清洗3-4次，烘干即得。
本发明所述一种堇青石复合陶瓷滤芯，由以下具体步骤制成：
（1）将尿素加入适量的水，加热至溶解；将棕榈纤维放入粉碎机中粉碎，将除二甲基硅油、水以外的其余剩余成分放入球磨机中，球磨3-4小时，与粉碎的棕榈纤维混合均匀得到混合粉末；
（2）将混合粉末加入到溶解的尿素中搅拌均匀，得到混合浆料，然后将混合的浆料真空去泡2-3小时；
（3）将去泡的浆料注入模具中，在室温中蒸发水分，自动晾干后脱模，得到滤芯生胚；
（4）将生胚送入隧道式炉中常压下烧结，先在200-260℃下焙烧10-12小时，然后缓慢升温至500-560℃下焙烧4-5小时，然后，再以6-8℃/分钟速率升温至1100-1180℃，烧结3-4小时，冷却后取出，放入清水中浸泡1-2天后，取出烘干。
本发明样品主要技术参数为：废气净化处理装置的技术指标为：捕获的粉尘颗粒最小粒径范围0.5-10μm；处理气体最高温度550℃；捕集微尘效率≥99％；出口排放烟尘颗粒物浓度≤30mg/m3。

Claims (1)

1.一种堇青石复合陶瓷滤芯，其特征在于，由下列重量份的原料制备制成：堇青石13-15、莫来石9-11、粗孔硅胶6-8、蒙脱石4-7、活性氧化铝8-10、硫酸钙3-5、二甲基硅油2-3、海藻酸钠3-4、棕榈纤维3-5、尿素2-3、改性椰壳活性炭5-7、水适量；所述改性椰壳活性炭由以下重量份的原料制成：粉碎椰壳20-25、氧化锆5-8、微粉硅胶3-5；制备方法是将粉碎椰壳用热水洗涤，然后在常温下用50-60%磷酸溶液浸泡1-2小时；过滤，取滤渣在550-600℃的炭化炉中炭化1.5-2小时，取出；待温度降至室温时与氧化锆、微粉硅胶混合均匀，再加入60%氢氧化钠搅拌1-1.5小时，然后过滤取出；用蒸馏水清洗3-4次，烘干即得。
CN201410073935.2A 2014-03-03 2014-03-03 一种堇青石复合陶瓷滤芯及其制备方法 Active CN103830962B (zh)