CN103821032A - 一种香烟用镀铝纸包装材料的制备方法 - Google Patents
一种香烟用镀铝纸包装材料的制备方法 Download PDFInfo
- Publication number
- CN103821032A CN103821032A CN201210466760.2A CN201210466760A CN103821032A CN 103821032 A CN103821032 A CN 103821032A CN 201210466760 A CN201210466760 A CN 201210466760A CN 103821032 A CN103821032 A CN 103821032A
- Authority
- CN
- China
- Prior art keywords
- percent
- packaging material
- release coating
- paper packaging
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种香烟用镀铝纸包装材料的制备方法,该方法包括如下步骤:1)在聚酯薄膜上涂覆剥离涂料,其中所述剥离涂层的组成以重量百分数计为:醋酸纤维素树脂18-22%,二元氯醋树脂7-9%,丙烯酸树脂24-26%,聚丙烯蜡1.5-2.5%,邻苯二甲酸二辛酯1-2%,钛酸酯偶联剂0.5-1.5%,2-羟基-4-甲氧基二苯甲酮0.2-0.4%,二月桂酸二丁基锡0.1-0.2%,余量为丁酮;2)真空镀铝;3)粘贴复合纸;4)剥离,得香烟用镀铝纸包装材料。
Description
技术领域
本发明涉及包装材料技术领域,尤其涉及一种香烟用镀铝纸包装材料的制备方法。
背景技术
真空镀铝纸是近年来应用于包装行业的包装材料,它具有较好的金属质感,适用于压纹机、高速横切机的加工,具有避光、隔湿、可降解等优点,可替代镀铝塑料薄膜、纯铝薄复合材料,由于其用铝量少,具有广阔的前景,现已被广泛用于香烟、食品、医药的包装装潢及商标标志等领域。目前,具有着色效果的真空镀铝纸都采用前上色法,其工艺方法是在聚酯薄膜上涂上一由硝基纤维素制成的易剥离涂层,后在易剥离涂层上进行真空镀铝,再粘贴复合一纸层形成半成品,然后将聚酯薄膜剥离出去而得到成品真空镀铝纸,其着色颜料加在易剥离涂层中。这种工艺方法制成的真空镀铝纸存在以下不足:由于聚酯薄膜剥离时使镀铝纸表层的硝基纤维素涂层变得粗糙,镀铝纸表面光洁度差,缺乏光泽;前上色工艺使产品色差难以控制;由于硝基纤维素抗有机溶剂的能力差,制成的镀铝纸表面印刷的适应性较差,无法进行大面积印刷。
发明内容
本发明的目的在于提出一种香烟用镀铝纸包装材料的制备方法,该包装材料通过对剥离涂层材料的改进,使得制备的镀铝纸包装材料表面光洁度高,印刷适应性强。
为达此目的,本发明采用以下技术方案:
一种香烟用镀铝纸包装材料的制备方法,该方法包括如下步骤:
1)在聚酯薄膜上涂覆剥离涂料,并在142-146℃下烘干,以便形成厚度为1.9-2.0g/平方米的易剥离涂层;其中所述剥离涂层的组成以重量百分数计为:醋酸纤维素树脂18-22%,二元氯醋树脂7-9%,丙烯酸树脂24-26%,聚丙烯蜡1.5-2.5%,邻苯二甲酸二辛酯1-2%,钛酸酯偶联剂0.5-1.5%,2-羟基-4-甲氧基二苯甲酮0.2-0.4%,二月桂酸二丁基锡0.1-0.2%,余量为丁酮;
2)在真空环境下将金属铝加热熔融后喷镀于上述易剥离涂层上,形成真空镀铝转移膜;
3)在镀铝转移膜的铝膜上涂覆胶粘剂并粘贴复合一纸层,在60-90℃下烘干,再常温冷却固化,形成复合半成品;
4)将聚酯薄膜用一定的拉力从复合半成品中逐步剥离出来,得香烟用镀铝纸包装材料。
本发明的有益效果为:
(1)剥离涂层性能优异,表面光洁度高,真空镀铝层转移非常充分;
(2)涂层柔韧性好,不易龟裂、爆色,并且与铝层附着力相当好、油墨印刷适应性高;
(3)剥离下来的PET基膜,可以重新涂布多次利用,降低了生产成本。
具体实施方式
实施例一
一种香烟用镀铝纸包装材料的制备方法,该方法包括如下步骤:
1)在聚酯薄膜上涂覆剥离涂料,并在142℃下烘干,以便形成厚度为2g/平方米的易剥离涂层;其中所述剥离涂层的组成以重量百分数计为:醋酸纤维素树脂18-22%,二元氯醋树脂7-9%,丙烯酸树脂24-26%,聚丙烯蜡1.5-2.5%,邻苯二甲酸二辛酯1-2%,钛酸酯偶联剂0.5-1.5%,2-羟基-4-甲氧基二苯甲酮0.2-0.4%,二月桂酸二丁基锡0.1-0.2%,余量为丁酮;
2)在真空环境下将金属铝加热熔融后喷镀于上述易剥离涂层上,形成真空镀铝转移膜;
3)在镀铝转移膜的铝膜上涂覆胶粘剂并粘贴复合一纸层,在60℃下烘干,再常温冷却固化,形成复合半成品;
4)将聚酯薄膜用一定的拉力从复合半成品中逐步剥离出来,得香烟用镀铝纸包装材料。
实施例二
一种香烟用镀铝纸包装材料的制备方法,该方法包括如下步骤:
1)在聚酯薄膜上涂覆剥离涂料,并在146℃下烘干,以便形成厚度为1.9g/平方米的易剥离涂层;其中所述剥离涂层的组成以重量百分数计为:醋酸纤维素树脂18-22%,二元氯醋树脂7-9%,丙烯酸树脂24-26%,聚丙烯蜡1.5-2.5%,邻苯二甲酸二辛酯1-2%,钛酸酯偶联剂0.5-1.5%,2-羟基-4-甲氧基二苯甲酮0.2-0.4%,二月桂酸二丁基锡0.1-0.2%,余量为丁酮;
2)在真空环境下将金属铝加热熔融后喷镀于上述易剥离涂层上,形成真空镀铝转移膜;
3)在镀铝转移膜的铝膜上涂覆胶粘剂并粘贴复合一纸层,在90℃下烘干,再常温冷却固化,形成复合半成品;
4)将聚酯薄膜用一定的拉力从复合半成品中逐步剥离出来,得香烟用镀铝纸包装材料。
实施例三
一种香烟用镀铝纸包装材料的制备方法,该方法包括如下步骤:
1)在聚酯薄膜上涂覆剥离涂料,并在144℃下烘干,以便形成厚度为1.95g/平方米的易剥离涂层;其中所述剥离涂层的组成以重量百分数计为:醋酸纤维素树脂18-22%,二元氯醋树脂7-9%,丙烯酸树脂24-26%,聚丙烯蜡1.5-2.5%,邻苯二甲酸二辛酯1-2%,钛酸酯偶联剂0.5-1.5%,2-羟基-4-甲氧基二苯甲酮0.2-0.4%,二月桂酸二丁基锡0.1-0.2%,余量为丁酮;
2)在真空环境下将金属铝加热熔融后喷镀于上述易剥离涂层上,形成真空镀铝转移膜;
3)在镀铝转移膜的铝膜上涂覆胶粘剂并粘贴复合一纸层,在75℃下烘干,再常温冷却固化,形成复合半成品;
4)将聚酯薄膜用一定的拉力从复合半成品中逐步剥离出来,得香烟用镀铝纸包装材料。
Claims (1)
1.一种香烟用镀铝纸包装材料的制备方法,其特征在于,该方法包括如下步骤:
1)在聚酯薄膜上涂覆剥离涂料,并在142-146℃下烘干,以便形成厚度为1.9-2.0g/平方米的易剥离涂层;其中所述剥离涂层的组成以重量百分数计为:醋酸纤维素树脂18-22%,二元氯醋树脂7-9%,丙烯酸树脂24-26%,聚丙烯蜡1.5-2.5%,邻苯二甲酸二辛酯1-2%,钛酸酯偶联剂0.5-1.5%,2-羟基-4-甲氧基二苯甲酮0.2-0.4%,二月桂酸二丁基锡0.1-0.2%,余量为丁酮;
2)在真空环境下将金属铝加热熔融后喷镀于上述易剥离涂层上,形成真空镀铝转移膜;
3)在镀铝转移膜的铝膜上涂覆胶粘剂并粘贴复合一纸层,在60-90℃下烘干,再常温冷却固化,形成复合半成品;
4)将聚酯薄膜用一定的拉力从复合半成品中逐步剥离出来,得香烟用镀铝纸包装材料。