CN103821032A - Preparation method for aluminum-plated paper packaging material for cigarettes - Google Patents
Preparation method for aluminum-plated paper packaging material for cigarettes Download PDFInfo
- Publication number
- CN103821032A CN103821032A CN201210466760.2A CN201210466760A CN103821032A CN 103821032 A CN103821032 A CN 103821032A CN 201210466760 A CN201210466760 A CN 201210466760A CN 103821032 A CN103821032 A CN 103821032A
- Authority
- CN
- China
- Prior art keywords
- percent
- packaging material
- release coating
- paper packaging
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for an aluminum-plated paper packaging material for cigarettes. The preparation method comprises the following steps: (1) coating a polyester thin film with stripping coating, wherein the stripping coating layer consists of the components in percentage by weight: 18-22 percent of cellulose acetate resin, 7-9 percent of bi-chloride-vinyl resin, 24-26 percent of acrylic resin, 1.5-2.5 percent of polypropylene wax, 1-2 percent of dioctyl phthalate, 0.5-1.5 percent of a titanate coupling agent, 0.2-0.4 percent of 2-hydroxy-4-methoxybenzophenone, 0.1-0.2 percent of dibutyltin dilaurate and the balance of butanone; (2) performing vacuum aluminum plating; (3) adhering composite paper; (4) performing stripping to obtain the aluminum-plated paper packaging material for the cigarettes.
Description
Technical field
The present invention relates to field of packaging material, relate in particular to the preparation method of a kind of cigarette with aluminized paper packaging material.
Background technology
Vacuum aluminium-plated paper is the packaging material that are applied in recent years packaging industry, it has good metal-like, be applicable to the processing of embossing machine, high-speed crosscutting machine, there is lucifuge, every advantages such as wet, degradables, alternative aluminized plastic film, the thin composite of fine aluminium, because it is few by aluminium amount, have broad prospects, be now widely used in the field such as packing and decorating and brand mark of cigarette, food, medicine.At present, the vacuum aluminium-plated paper with coloring effect all adopts front upper color method, its process is on polyester film, to coat an easy release coating of being made up of NC Nitroncellulose, after on easy release coating, carry out vacuum aluminum-coated, paste again a compound ply of paper and form semi-finished product, then polyester film peeled off away and obtained finished product vacuum aluminium-plated paper, its coloring pigment is added in easy release coating.The vacuum aluminium-plated paper that this process is made has the following disadvantages: while peeling off due to polyester film, make the nitrocellulose element coating on aluminized paper top layer become coarse, aluminized paper poor surface smoothness, lacks gloss; Front coloring process makes product aberration be difficult to control; Due to the ability of the anti-organic solvent of NC Nitroncellulose, the adaptability of the aluminized paper surface printing of making is poor, cannot carry out large area printing.
Summary of the invention
The object of the invention is to propose the preparation method of a kind of cigarette with aluminized paper packaging material, these packaging material, by the improvement to release coating material, make the aluminized paper package material surface of preparation highly polished, and printing adaptability is strong.
For reaching this object, the present invention by the following technical solutions:
Cigarette is used a preparation method for aluminized paper packaging material, and the method comprises the steps:
1) on polyester film, apply release coating, and dry at 142-146 ℃, so that formation thickness is the easy release coating of 1.9-2.0g/ square metre; The composition of wherein said release coating is by weight percentage: cellulose acetate resin 18-22%, binary vinyl chloride-vinyl acetate resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling agent 0.5-1.5%, ESCALOL 567 0.2-0.4%, dibutyl tin laurate 0.1-0.2%, surplus is butanone;
2) under vacuum environment by spraying plating after metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
3) adhesive coating paste a compound ply of paper on the aluminium film of the transfer membrane of aluminizing is dried at 60-90 ℃, then normal temperature cooling curing, forms compound semi-finished product;
4) polyester film out, is obtained to cigarette and uses aluminized paper packaging material with certain pulling force phased separation from compound semi-finished product.
Beneficial effect of the present invention is:
(1) release coating excellent performance, surface smoothness is high, and vacuum aluminium coated layer shifts very abundant;
(2) good film flexibility, be difficult for be full of cracks, quick-fried look, and fairly good with aluminium lamination adhesive force, ink printing adaptability is high;
(3) the PET basement membrane stripping down, can again be coated with repeatedly and utilize, and has reduced production cost.
The specific embodiment
Embodiment mono-
Cigarette is used a preparation method for aluminized paper packaging material, and the method comprises the steps:
1) on polyester film, apply release coating, and dry at 142 ℃, so that formation thickness is the easy release coating of 2g/ square metre; The composition of wherein said release coating is by weight percentage: cellulose acetate resin 18-22%, binary vinyl chloride-vinyl acetate resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling agent 0.5-1.5%, ESCALOL 567 0.2-0.4%, dibutyl tin laurate 0.1-0.2%, surplus is butanone;
2) under vacuum environment by spraying plating after metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
3) adhesive coating paste a compound ply of paper on the aluminium film of the transfer membrane of aluminizing is dried at 60 ℃, then normal temperature cooling curing, forms compound semi-finished product;
4) polyester film out, is obtained to cigarette and uses aluminized paper packaging material with certain pulling force phased separation from compound semi-finished product.
Embodiment bis-
Cigarette is used a preparation method for aluminized paper packaging material, and the method comprises the steps:
1) on polyester film, apply release coating, and dry at 146 ℃, so that formation thickness is the easy release coating of 1.9g/ square metre; The composition of wherein said release coating is by weight percentage: cellulose acetate resin 18-22%, binary vinyl chloride-vinyl acetate resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling agent 0.5-1.5%, ESCALOL 567 0.2-0.4%, dibutyl tin laurate 0.1-0.2%, surplus is butanone;
2) under vacuum environment by spraying plating after metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
3) adhesive coating paste a compound ply of paper on the aluminium film of the transfer membrane of aluminizing is dried at 90 ℃, then normal temperature cooling curing, forms compound semi-finished product;
4) polyester film out, is obtained to cigarette and uses aluminized paper packaging material with certain pulling force phased separation from compound semi-finished product.
Embodiment tri-
Cigarette is used a preparation method for aluminized paper packaging material, and the method comprises the steps:
1) on polyester film, apply release coating, and dry at 144 ℃, so that formation thickness is the easy release coating of 1.95g/ square metre; The composition of wherein said release coating is by weight percentage: cellulose acetate resin 18-22%, binary vinyl chloride-vinyl acetate resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling agent 0.5-1.5%, ESCALOL 567 0.2-0.4%, dibutyl tin laurate 0.1-0.2%, surplus is butanone;
2) under vacuum environment by spraying plating after metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
3) adhesive coating paste a compound ply of paper on the aluminium film of the transfer membrane of aluminizing is dried at 75 ℃, then normal temperature cooling curing, forms compound semi-finished product;
4) polyester film out, is obtained to cigarette and uses aluminized paper packaging material with certain pulling force phased separation from compound semi-finished product.
Claims (1)
1. cigarette, by a preparation method for aluminized paper packaging material, is characterized in that, the method comprises the steps:
1) on polyester film, apply release coating, and dry at 142-146 ℃, so that formation thickness is the easy release coating of 1.9-2.0g/ square metre; The composition of wherein said release coating is by weight percentage: cellulose acetate resin 18-22%, binary vinyl chloride-vinyl acetate resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling agent 0.5-1.5%, ESCALOL 567 0.2-0.4%, dibutyl tin laurate 0.1-0.2%, surplus is butanone;
2) under vacuum environment by spraying plating after metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
3) adhesive coating paste a compound ply of paper on the aluminium film of the transfer membrane of aluminizing is dried at 60-90 ℃, then normal temperature cooling curing, forms compound semi-finished product;
4) polyester film out, is obtained to cigarette and uses aluminized paper packaging material with certain pulling force phased separation from compound semi-finished product.