CN103820002A - Corrosion resistant coating for universal joint - Google Patents
Corrosion resistant coating for universal joint Download PDFInfo
- Publication number
- CN103820002A CN103820002A CN201410023423.5A CN201410023423A CN103820002A CN 103820002 A CN103820002 A CN 103820002A CN 201410023423 A CN201410023423 A CN 201410023423A CN 103820002 A CN103820002 A CN 103820002A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion resistant
- universal joint
- resistant coating
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides corrosion resistant coating for a universal joint, which comprises the following components in parts by mass: 100 parts of epoxy resin, 10-15 parts of ferric oxide, 15-20 parts of chloroethylene, 5-10 parts of zinc chrome, 1-5 parts of aluminum paste, 10-15 parts of ultrafine talcum powder, 10-15 parts of active manganese dioxide, 1-2 parts of a thixotropic agent, 12-18 parts of silicon dioxide, and 1-2 parts of a drier. The surface dry of a product takes 0.2-0.5 hour, the hard dry of the product takes 2-3 hours, the viscosity is 20-25, the fineness is not greater than 38 micrometers, the hardness is 0.5, the coating does not change within 6 hours at the temperature of 150 DEG C, and the product is corrosion resistant, high in impact strength and long in service life, and can be widely produced and constantly replaces the existing materials.
Description
Technical field
The application belongs to metallic paint field, relates in particular to a kind of universal joint corrosion resistant coating.
Background technology
So-called universal joint refers to devices such as utilizing ball-type and exports with the axle power of realizing different directions, and it is also on automobile one very vitals.Universal joint and transmission shaft combination, be called cardan gear.On the vehicle of front-mounted engine rear wheel drive, cardan gear is arranged between transmission output shaft and main reducing gear of drive axle input shaft; And the vehicle of front-mounted engine front-wheel drive has omitted transmission shaft, universal joint is arranged between not only responsible driving but also the front axle half shaft of being responsible for turning to and wheel; Between the variator and drive axle of engine behind front wheel rear wheel drive truck.When distant between variator and drive axle, transmission shaft should be divided into two sections of even multistages, and add intermediate support.Between the transfer gear of many shaft-driven automobiles and drive axle or between drive axle and drive axle.Due to the distortion of vehicle frame, can cause between two drive disk assemblies that between axis, mutual alignment changes.Be depicted as between engine and variator.
Epoxy resin is the organic high molecular compound that contains two or more epoxide groups in general reference molecule, and except indivedual, their relative molecular mass is not high.The molecular structure of epoxy resin is to contain active epoxide group in molecular chain as its feature, and epoxide group can be positioned at the end, centre of molecular chain or structure circlewise.Owing to containing active epoxide group in molecular structure, make them can form with polytype solidifying agent generation crosslinking reaction insoluble, the molten cancellated superpolymer of three-dimensional that has.And universal along with humanity concept, and the formation of novel harmonious society, design a kind of universal joint corrosion resistant coating and be very important.
Summary of the invention
the technical problem solving:
The application, for above-mentioned technical problem, provides a kind of universal joint corrosion resistant coating, solves existing universal joint coating long time of drying, not acid and alkali-resistance, the technical problem such as sticking power is low.
technical scheme:
A kind of universal joint corrosion resistant coating, be made up of following raw materials according, take mass fraction representation as 100 parts of epoxy resin; Ferric oxide 10-15 part; Perchloroethylene 15-20 part; Zinc-chrome yellow 5-10 part; Aluminum paste 1-5 part; Superfine talcum powder 10-15 part; Activated manganese dioxide 10-15 part; Thixotropic agent 1-2 part; Silica 1 2-18 part; Siccative 1-2 part.
As a preferred technical solution of the present invention: its composition is take mass fraction representation as 100 parts of epoxy resin; 12.5 parts of ferric oxide; 17.5 parts of perchloroethylenes; 8 parts of zinc-chrome yellows; 3 parts of aluminum pastes; 12 parts of superfine talcum powders; 13 parts of activated manganese dioxides; 1.5 parts of thixotropic agent; 5 parts of silica 1s; 1.5 parts of siccative.
As a preferred technical solution of the present invention: described siccative adopts dibutyl tin laurate.
beneficial effect:
A kind of universal joint of the present invention adopts above technical scheme compared with prior art with corrosion resistant coating, has following technique effect: 1, product surface drying 0.2-0.5h, does solid work 2-3h; 2, viscosity 20-25, fineness≤38 micron; 3, at 0.5,150 ℃ of hardness, 6h is unchanged; 4, product is corrosion-resistant, shock strength is high, long service life, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A kind of universal joint corrosion resistant coating, its composition is take mass fraction representation as 100 parts of epoxy resin; 10 parts of ferric oxide; 15 parts of perchloroethylenes; 5 parts of zinc-chrome yellows; 1 part of aluminum paste; 10 parts of superfine talcum powders; 10 parts of activated manganese dioxides; 1 part of thixotropic agent; 2 parts of silica 1s; 1 part of dibutyl tin laurate.
Product surface drying 0.5h, does solid work 3h; Viscosity 20, fineness≤40 micron; At 0.5,100 ℃ of hardness, 6h is unchanged.
embodiment 2:
A kind of universal joint corrosion resistant coating, its composition is take mass fraction representation as 100 parts of epoxy resin; 15 parts of ferric oxide; 20 parts of perchloroethylenes; 10 parts of zinc-chrome yellows; 5 parts of aluminum pastes; 15 parts of superfine talcum powders; 15 parts of activated manganese dioxides; 2 parts of thixotropic agent; 8 parts of silica 1s; 2 parts of dibutyl tin laurates.
Product surface drying 0.3h, does solid work 2.5h; Viscosity 22.5, fineness≤39 micron; At 0.5,120 ℃ of hardness, 6h is unchanged.
embodiment 3:
A kind of universal joint corrosion resistant coating, its composition is take mass fraction representation as 100 parts of epoxy resin; 12.5 parts of ferric oxide; 17.5 parts of perchloroethylenes; 8 parts of zinc-chrome yellows; 3 parts of aluminum pastes; 12 parts of superfine talcum powders; 13 parts of activated manganese dioxides; 1.5 parts of thixotropic agent; 5 parts of silica 1s; 1.5 parts of dibutyl tin laurates.
Product surface drying 0.2h, does solid work 2h; Viscosity 25, fineness≤38 micron; At 0.5,150 ℃ of hardness, 6h is unchanged.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, and therefore any change in implication and the scope suitable with claims of the present invention, all should think to be included in the scope of claims.
Claims (3)
1. a universal joint corrosion resistant coating, is characterized in that: its composition is take mass fraction representation as 100 parts of epoxy resin; Ferric oxide 10-15 part; Perchloroethylene 15-20 part; Zinc-chrome yellow 5-10 part; Aluminum paste 1-5 part; Superfine talcum powder 10-15 part; Activated manganese dioxide 10-15 part; Thixotropic agent 1-2 part; Silica 1 2-18 part; Siccative 1-2 part.
2. a kind of universal joint corrosion resistant coating according to claim 1, is characterized in that: its composition is take mass fraction representation as 100 parts of epoxy resin; 12.5 parts of ferric oxide; 17.5 parts of perchloroethylenes; 8 parts of zinc-chrome yellows; 3 parts of aluminum pastes; 12 parts of superfine talcum powders; 13 parts of activated manganese dioxides; 1.5 parts of thixotropic agent; 5 parts of silica 1s; 1.5 parts of siccative.
3. a kind of universal joint corrosion resistant coating according to claim 1, is characterized in that: described siccative adopts dibutyl tin laurate.