CN103785825B - 一种铅酸蓄电池的铅粉生产工艺 - Google Patents
一种铅酸蓄电池的铅粉生产工艺 Download PDFInfo
- Publication number
- CN103785825B CN103785825B CN201410020165.5A CN201410020165A CN103785825B CN 103785825 B CN103785825 B CN 103785825B CN 201410020165 A CN201410020165 A CN 201410020165A CN 103785825 B CN103785825 B CN 103785825B
- Authority
- CN
- China
- Prior art keywords
- lead
- lead powder
- apparent density
- production technology
- leady oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种铅酸蓄电池的铅粉生产工艺,使用两台铅粉机生产出两种氧化量以及视密度规格不同的铅粉,然后通过一台搅拌机将这两种铅粉进行混合搅拌均匀,两台铅粉机中,一台生产出的铅粉氧化量在70-76%之间,视密度在1.40-1.55g/cm3之间,另一台生产出的铅粉氧化量在74-80%之间,视密度在1.30-1.45g/cm3之间。本发明生产工艺制得的铅粉氧化量在70-80%之间,视密度在1.35-1.55g/cm3之间,用这种铅粉制作的蓄电池极板既能满足蓄电池的初期放电容量又能保证蓄电池的使用寿命。
Description
技术领域
本发明涉及铅酸蓄电池的铅粉生产工艺。
背景技术
现在生产的铅酸蓄电池极板使用的铅粉,是由一台或多台铅粉机,按照一种生产工艺生产同一规格(技术要求)的铅粉,铅粉氧化量一般在74±4%之间,视密度在1.35g/cm3左右,有时生产铅粉氧化量经常会出现波动,使生产出来的铅粉氧化量有时偏高;有时偏低不均匀,在使用中遇到氧化量偏高时做出的极板电池初期容量高,使用寿命短;如果遇到氧化量偏低时做出的极板电池初期容量低,达不到容量要求,在生产过程中使用这样的极板装配的电池一致性差,尤其是生产电动助力车用蓄电池,在化成过程中电池一致性差,影响配组,即使是配出电池组,蓄电池使用寿命也不会长。
发明内容
本发明所要解决的技术问题就是提供一种铅酸蓄电池的铅粉生产工艺,制得的铅粉氧化量,视密度比较稳定,均匀性好。
为解决上述技术问题,本发明采用如下技术方案:一种铅酸蓄电池的铅粉生产工艺,使用两台铅粉机生产出两种氧化量以及视密度规格不同的铅粉,然后通过一台搅拌机将这两种铅粉进行混合搅拌均匀。
优选的,两台铅粉机中,一台生产出的铅粉氧化量在70-76%之间,视密度在1.40-1.55g/cm3之间,另一台生产出的铅粉氧化量在74-80%之间,视密度在1.30-1.45g/cm3之间。
优选的,两种铅粉各占质量分数的50%进行混合搅拌均匀。
优选的,该铅酸蓄电池的铅粉生产工艺制得的铅粉氧化量在70-80%之间,视密度在1.35-1.55g/cm3之间。
优选的,每个极柱密封所用玻璃胶的注胶量为0.2-0.3g。
本发明生产工艺制得的铅粉氧化量在70-80%之间,视密度在1.35-1.55g/cm3之间,用这种铅粉制作的蓄电池极板既能满足蓄电池的初期放电容量又能保证蓄电池的使用寿命,更重要的是铅粉经过混合搅拌,铅粉的氧化量,视密度比较稳定,均匀性好,制作的极板一致性好,尤其是提高了电动助力车用蓄电池,在化成生产过程中电池的配组率,使电池的一致性得到提高。
具体实施方式
本发明的铅酸蓄电池的铅粉生产工艺仍然是使用现有生产工艺中使用的铅粉机,其使用两台铅粉机,一台铅粉机使用一种生产工艺,另一台铅粉机使用另一种生产工艺,通过控制铅粉机的工艺参数生产出两种规格(技术要求)的铅粉,一种铅粉氧化量控制在70-76%之间,视密度在1.40-1.55g/cm3之间,另一种铅粉氧化度在74-80%之间,视密度在1.30-1.45g/cm3之间,然后增加一台铅粉混合搅拌机,将这两种铅粉各加50%(质量分数)进行混合搅拌均匀,制得的铅粉氧化量在70-80%之间,视密度在1.35-1.55g/cm3之间。用这种铅粉制作的蓄电池极板,即能满足蓄电池的初期放电容量又能保证蓄电池的使用寿命,更重要的是铅粉经过混合搅拌,铅粉的氧化量,视密度比较稳定,均匀性好,制作的极板一致性好,尤其是提高了电动助力车用蓄电池,在化成生产过程中电池的配组率,使电池的一致性得到提高。
Claims (1)
1.一种铅酸蓄电池的铅粉生产工艺,其特征在于:使用两台铅粉机生产出两种氧化量以及视密度规格不同的铅粉,然后通过一台搅拌机将这两种铅粉进行混合搅拌均匀,两台铅粉机中,一台生产出的铅粉氧化量在70-76%之间,视密度在1.40-1.55 g/cm3之间,另一台生产出的铅粉氧化量在74-80%之间,视密度在1.30-1.45 g/cm3之间,两种铅粉各占质量分数的50%进行混合搅拌均匀,该铅酸蓄电池的铅粉生产工艺制得的铅粉氧化量在70-80%之间,视密度在1.35-1.55 g/cm3之间。