CN103774145A - Method for covering metal foil on copper-cladded plate - Google Patents
Method for covering metal foil on copper-cladded plate Download PDFInfo
- Publication number
- CN103774145A CN103774145A CN201410071238.3A CN201410071238A CN103774145A CN 103774145 A CN103774145 A CN 103774145A CN 201410071238 A CN201410071238 A CN 201410071238A CN 103774145 A CN103774145 A CN 103774145A
- Authority
- CN
- China
- Prior art keywords
- copper
- weight
- liquid
- clad plate
- covering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of circuit board processing. The artificial processing of the circuit board has the defect that used covering liquid is often hard to clean or the covering capability is poor. In order to overcome the defects in the prior art, the invention provides a manufacturing method of composite liquid for covering a metal foil on a copper-cladded plate. The composite liquid disclosed by the invention can effectively cover the metal foil on the copper-cladded plate and is easy to be removed from the surface of the copper-cladded plate. In order to overcome the defects in the prior art, the adopted technical scheme is as follows: the method for covering the metal foil on the copper-cladded plate comprises the following steps: (1) preparing liquid for covering the metal foil from oil paint, formic acid and liquid paraffin; and (2) dipping the liquid obtained by the first step by using a writing brush and drawing the part above the metal foil needing to be reserved on the copper-cladded plate.
Description
Technical field
The invention belongs to circuit card manufacture field.Especially copper-clad plate is drawn and is used liquid field.
Background technology
The technology of existing large-scale processing circuit card is very ripe, still, under many circumstances, still needs artificial circuit card, such as processing, maintenance power distribution cabinet circuit card used, such as small scale in circuitry test, such as DIY fan processing circuit board.Artificial circuit card, the normal covering liquid that adopts covers in the tinsel (this tinsel is often made of copper) of copper-clad plate, after stand-by corrosive fluid (usually using liquor ferri trichloridi) corrosion, with the coverture on solvent cleaning copper-clad plate surface, thereby expose copper (metal) paper tinsel that needs reservation.Covering liquid used usually has the defect that is difficult to cleaning or covering power deficiency, this all may make circuit card form flaw, such as: the part that should not corrode has been corroded, for another example: this place cleaning up does not clean up,, this place needs soldered elements.These flaws may cause fault.Also there is a kind of so method: stick in copper-clad plate with scotch tape, then, go out the part that will retain with graduating with cutter, tear and do not need the part that retains, then, the tinsel on corrosion copper-clad plate surface.Use scotch tape to paste as tectal method bothers very much.
Summary of the invention
In order to overcome the deficiencies in the prior art, the present invention proposes a kind of manufacture method of the composite fluid for copper-clad plate covering metal paper tinsel, and the composite fluid that the present invention discloses can effectively hide the tinsel in copper-clad plate, and is easy to remove from copper-clad plate surface.
The present invention for the technical scheme that solves prior art deficiency and adopt is:
1, for the manufacture method of the composite fluid of copper-clad plate covering metal paper tinsel, step is:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
2, for the composite fluid of copper-clad plate covering metal paper tinsel, it is characterized in that: this composite fluid is adopted with the following method and made:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
3, for the pen of copper-clad plate covering metal paper tinsel, it is characterized in that:, inject and describe circuit liquid used for filling the pen of correction fluid originally, and this liquid is adopted with the following method and made:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
4, a kind of in copper-clad plate covering metal paper tinsel method, the steps include:
The first step, the liquid of configuration covering metal paper tinsel, collocation method is:
A, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
B, in mixture described in a step, adding parts by weight is 4 formic acid, and mixes,
C, in the mixture described in b step, adding parts by weight is 5 whiteruss, and mixes.
Second step, dips in the first step gained liquid with writing brush, is depicted in the tinsel top that copper-clad plate need to retain.
5, in copper-clad plate, a kind of method of covering metal paper tinsel, the steps include:
The first step, the liquid of configuration covering metal paper tinsel, collocation method is:
A, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
B, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
C, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
Second step, injects the liquid of the first step configuration in the pen that is originally used for filling correction fluid, makes the pen for copper-clad plate covering metal paper tinsel,
The 3rd step is described with the pen described in second step, and is depicted in the tinsel top that copper-clad plate need to retain in copper-clad plate.
The liquid that the present invention is disclosed, the beneficial effect having is: 1, the ability that hides copper-clad plate is strong, and corrosive fluid can not permeate tectum, and 2, tectum is easily cleared up.
Embodiment
The manufacture method that is used for the composite fluid of copper-clad plate covering metal paper tinsel, step is:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
Paint described in this specification sheets is all from Xinjiang Red Hill coating company limited, and institute makes to paint package dimensioning following information:
Product are by name: prepared alkyd paint, and operative norm: Q/XHS015-2011, model C 03-1, packed weight: 400 grams, color: white.
Formic acid (chemical formula HCOOH, molecular formula CH described in this specification sheets
2o
2, popular name formic acid) and be anhydrous formic acid.Various equivalent modifications should be known paint, formic acid, ethanol certain danger, should under suitable environment, operate.
It is to be noted that weight ratio of the present invention is also referred to as mass ratio.Be that parts by weight also can be called mass fraction.Mix the mode that can adopt stirring, also can adopt the mode of rocking in sealed vessel that packs into.
For the composite fluid of copper-clad plate covering metal paper tinsel, it is characterized in that: this composite fluid is adopted with the following method and made:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
3, for the pen of copper-clad plate covering metal paper tinsel, it is characterized in that:, inject and describe circuit liquid used for filling the pen of correction fluid originally, and this liquid is adopted with the following method and made:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
For clearly statement " originally for filling the pen of correction fluid ", this specification sheets provides concrete introduction.Correction fluid, is also opaquing fluid, is also correction pen, this is a kind of very common cultural goods, and it,, by being pressed in the word surface that needs modification, will be flowed out to white liquid, this liquid is dry very soon, can hide the word of wrongly writing, and can be at its other writing words in dry surface.Used in the present invention is not the liquid of using correction fluid inside, but utilizes the pen that takes up correction fluid (to can be regarded as container, device yet.）。
By the way, contriver attempts using correction fluid directly as the liquid of covering metal paper tinsel in copper-clad plate, find: covering power deficiency, liquor ferri trichloridi easily permeates in the thinner place of tectum, and, solidifying correction fluid after (become dry, hardening) has and much remains in copper-clad plate, is difficult to remove.
In copper-clad plate covering metal paper tinsel a method, the steps include:
The first step, the liquid of configuration covering metal paper tinsel, collocation method is:
A, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
B, in mixture described in a step, adding parts by weight is 4 formic acid, and mixes,
C, in the mixture described in b step, adding parts by weight is 5 whiteruss, and mixes.
Second step, dips in the first step gained liquid with writing brush, is depicted in the tinsel top that copper-clad plate need to retain.
In copper-clad plate, a kind of method of covering metal paper tinsel, the steps include:
The first step, the liquid of configuration covering metal paper tinsel, collocation method is:
A, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
B, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
C, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.
Second step, injects the liquid of the first step configuration in the pen that is originally used for filling correction fluid, makes the pen for copper-clad plate covering metal paper tinsel,
The 3rd step is described with the pen described in second step, and is depicted in the tinsel top that copper-clad plate need to retain in copper-clad plate.
Contriver also attempts using the mixture of raw spirit and paint (to refer to: in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mix,) come for copper-clad plate covering metal paper tinsel, discovery has the following advantages: 1, covering power is very strong, 2, do not need covering liquid (referring to the mixture of paint and raw spirit) completely to become dry and just can put in liquor ferri trichloridi and corrode.Find that there is following defect: be difficult for cleaning up simultaneously.
Concerning a lot of people, holding facile organic solvent is raw spirit, moreover in covering liquid, just there are raw spirit and paint, so, clean the paint becoming dry with raw spirit, be the method that is easy to expect, test shows: 1, if paint is enough sclerosis (being commonly called as exsiccation) not, when cleaning, paint easily pollutes hand, container and other environment.2, if enough sclerosis of paint, when cleaning, need a large amount of raw spirits, and, be spread across on ground, can leave trace, be difficult to cleaning.
The composite fluid that the present invention discloses, (note: this composite fluid is adopted with the following method and made:
The first step, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
Second step, in mixture described in the first step, adding parts by weight is 4 formic acid, and mixes,
The 3rd step, in the mixture described in second step, adding parts by weight is 5 whiteruss, and mixes.) have the following advantages:
Advantage 1, covering power is strong, and liquor ferri trichloridi can not permeate tectum.Contriver is in the environment of 25 degrees Celsius of room temperatures, describe many group lines on copper-clad plate surface with it, brushing amount (also can be used for characterizing brushing thickness) is every square metre 80 grams to 100 grams, describe rear placement 10 minutes---15 minutes, then put in the saturated liquor ferri trichloridi of 30 degrees Celsius and soak 20 minutes, then remove tectum, find that tinsel (Copper Foil) upper surface that coating cap rock hides is not etched.
Need having of explanation: copper-clad plate upper surface is not corroded, illustrate that tectum has good covering power, but, the side that does not represent copper-clad plate tinsel is not etched, various equivalent modifications should be known: liquor ferri trichloridi is put in copper-clad plate, should be by rocking the modes such as copper-clad plate, allow as early as possible iron trichloride corrode the tinsel that does not obtain covering, in order to avoid the side of the further attack metal paper tinsel of liquor ferri trichloridi.Various equivalent modifications also should be known, and the side of iron trichloride erosion copper-clad plate tinsel is less on circuit impact, because this working method is used for processing the wider circuit card of circuit, circuit side is etched, and is equal to the narrowed width of circuit a bit.In sum, because erosion time is not long, and less on width impact, the impact that tinsel side is etched is negligible.
Also need the chlamydate thickness of explaining.Contriver does not have directly to measure the thickness covering, because the thickness of coating liquid is difficult to directly measure.
Advantage 2, just can decoat without solvent cleaning tectum, and is easy to remove clean.In room temperature is the environment of 25 degrees Celsius, last 10 minutes to 20 minutes from being applied to immersion liquor ferri trichloridi, the time being immersed in liquor ferri trichloridi is lasted approximately 15 minutes, after taking out from liquor ferri trichloridi, tectum is softer and form mantle, scrapes off gently and just can remove totally with pocket knife.Or: from liquor ferri trichloridi, take out after copper-clad plate, be shelved on normal temperature environment (approximately 25 degrees Celsius) and last approximately 50 minutes, tectum can form film, pries open tectal one jiao with pocket knife, tears and just can peel off tectum completely with hand.Or: from liquor ferri trichloridi, take out after copper-clad plate, be shelved on normal temperature environment (approximately 25 degrees Celsius) and last approximately 80 minutes, tectum can form harder film, sticks on cover surface with scotch tape, presses adhesive tape (pressure applying is the every square centimeter of 10----20 newton that exerts pressure) with hand, adhesive tape and tectum are fitted tightly, then, tear adhesive tape, now, adhesive tape is bonding tectum, overburden stripping copper-clad plate.And, from liquor ferri trichloridi, take out after copper-clad plate, being shelved on normal temperature environment (approximately 25 degrees Celsius) lasted after three days, still can adopt any one method in following two kinds of methods to peel off tectum: 1, first pry open tectal one jiao with pocket knife, then tear with hand the film that tectum forms, 2, the film forming with tape stripping tectum.The adhesive tape that contriver adopts is " capable " board adhesive tape, and its trade name is: 30029 stationery adhesive tapes, and width is 12mm, the 30029th, the numbering of adhesive tape producer to these commodity.
Contriver only mixes with raw spirit and paint, adopts multiple proportioning, and the method that the tectum forming all can not be used described in passage is removed or remove clean.And find: the tectum being only mixed with raw spirit and paint is difficult peeling off extremely.
The whiteruss that contriver adopts is: the whiteruss that the trade name that Guangdong, Taishan City emigrant's reagent plastics company limited produces is " whiteruss ", and lot number: 20121001, and label has " chemical pure " printed words.
Also need having of explanation: not contradiction of poor adhesive force and good sealing effect, for example: scotch tape sealing effectiveness is fine, still, poor adhesive force-----can tear off with hand.
Also it should be noted that: poor adhesive force does not represent can self falling, for example: scotch tape poor adhesive force, still, up-to-standard scotch tape sticks on smooth finish surface can self falling.
Only paint and raw spirit are encased in to script for filling the pen of correction fluid, following three kinds of situations easily occur: 1, when the shared weight ratio of raw spirit is excessive, the wayward thickness of trace drawing, because mobility is excellent.2, when the shared weight ratio of raw spirit is too small, be difficult for from originally flowing out for the pen that fills correction fluid.3, even the proportioning of careful debugging paint and raw spirit, under normal temperature laboratory, place and exceed half a year, also easily stop up nib----mouth that liquid flows out stopped up, and this blockage is difficult to overcome, once stop up, stop up and be difficult to eliminate, use raw spirit to soak nib and be also difficult to eliminate stop up.
But, the disclosed composite fluid of the present invention is encased in originally for filling the pen of correction fluid, overcome above-mentioned three kinds of deficiencies, tool has the following advantages: mobility is suitable, is easy to control trace (also can be understood as person's handwriting) thickness, also easily allow liquid flow out from nib, under normal temperature laboratory, place and exceed half a year, although also can stop up once in a while written phenomenon,, the housing of peeling off nib place with fingernail, just can normally use.
Only paint and raw spirit are encased in to script for filling the pen of correction fluid, stop up once there is nib, the written housing forming cannot be deducted with fingernail, because the housing sticking power forming is too strong.
Use originally for filling the pen perfusion this liquid of the present invention of correction fluid, also have a benefit: there is a spherical weight this pen the inside, before use, can allow this bead stirred liq by the mode of hand-held concussion, play the effect mixing.
The metal level of copper-clad plate surface coverage of the present invention is Copper Foil.
The liquid that the present invention discloses is for copper-clad plate, and the beneficial effect bringing is: be easy to remove clean tectum.
Claims (1)
1. a method for covering metal paper tinsel in copper-clad plate, the steps include:
The first step, the liquid of configuration covering metal paper tinsel, collocation method is:
A, in the raw spirit that is 50 at parts by weight, adding parts by weight is 20 paint, and mixes,
B, in mixture described in a step, adding parts by weight is 4 formic acid, and mixes,
C, in the mixture described in b step, adding parts by weight is 5 whiteruss, and mixes,
Second step, dips in the first step gained liquid with writing brush, is depicted in the tinsel top that copper-clad plate need to retain,
The above right of request protection.