CN103773224A - 一种耐高温非膨胀型防火防腐涂料及其制备方法 - Google Patents

一种耐高温非膨胀型防火防腐涂料及其制备方法 Download PDF

Info

Publication number
CN103773224A
CN103773224A CN201310493676.4A CN201310493676A CN103773224A CN 103773224 A CN103773224 A CN 103773224A CN 201310493676 A CN201310493676 A CN 201310493676A CN 103773224 A CN103773224 A CN 103773224A
Authority
CN
China
Prior art keywords
expansion type
high temperature
resistant non
type fire
temperature resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310493676.4A
Other languages
English (en)
Inventor
王旭莹
杨帆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd
Original Assignee
JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd filed Critical JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310493676.4A priority Critical patent/CN103773224A/zh
Publication of CN103773224A publication Critical patent/CN103773224A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温非膨胀型防火防腐涂料及其制备方法，将正硅酸乙酯、中空玻璃微珠、玻璃鳞片、硅烷偶联剂、正丁醇和助剂直接加入搅拌釜中进行混合搅拌，搅拌速度800－1000r/min，搅拌时间30－45min，即可，本涂料可兼顾防火和防腐双重功能，从而解决了化工企业高温装置防火防腐难的问题，有效避免了因高温液体泄漏带来的火灾危害，能够更好地保护公共财产免受损害。

Description

一种耐高温非膨胀型防火防腐涂料及其制备方法
技术领域
本发明涉及一种涂料及其制备方法，特别涉及一种耐高温非膨胀型防火防腐涂料及其制备方法，属于涂料技术领域。
背景技术
目前市面上的涂料一般仅具有防腐功能或仅具有防火功能，较少有防火和防腐功能兼具的涂料。近年来阿克苏诺贝尔公司开发出了兼具防火和防腐功能二合一的功能性涂料，但该涂料在使用上也存在一定的局限性，例如针对高温装置上使用时涂料往往不耐高温而导致脱落或焦化，从而失去了防腐的效果。现有技术中的涂料仍多采用普通有机耐高温树脂作为主要原料，而普通有机耐高温树脂的所耐受高温通常仅在600℃左右，即使配合良好的耐高温材料通常也只能达到700℃左右。由于高温装置本身就容易在外界因素的影响下出现燃烧现象，特别是炼钢厂锅炉中的铁水、炼油厂的导热油等，而他们的泄漏往往是是导致火灾的主要因素。因而需要探索一种性能优良的可兼顾防火和防腐双重功能的涂料。
发明内容
本发明的目的在于克服现有技术中的缺陷，提供一种耐高温非膨胀型防火防腐涂料及其制备方法，所述涂料可兼顾防火和防腐双重功能，从而有效地避免了因高温液体泄漏带来的火灾危害。
本发明是通过以下技术方案予以实现的。
一种耐高温非膨胀型防火防腐涂料，其组成成分以质量份计为：
Figure BDA0000397929810000021
上述的一种耐高温非膨胀型防火防腐涂料，其中，所述正硅酸乙酯为正硅酸乙酯-32，购买于常州市武进恒业化工有限公司。
上述的一种耐高温非膨胀型防火防腐涂料，其中，所述中空玻璃微珠的粒径范围分别为10－200um、10－100um和10－250um；堆积密度分别为0.14－0.16g/cm3、0.18－0.20g/cm3和0.08－0.10g/cm3。
上述的一种耐高温非膨胀型防火防腐涂料，其中，所述硅烷偶联剂为硅烷偶联剂KH-55O，购买于道康宁公司。
上述的一种耐高温非膨胀型防火防腐涂料，其中，所述正丁醇的质量百分比浓度为95%。
上述的一种耐高温非膨胀型防火防腐涂料，其中，所述助剂为分散剂HX-4030，购买于华夏助剂有限公司。
上述的一种耐高温非膨胀型防火防腐涂料的制备方法，制备方法如下：将正硅酸乙酯、中空玻璃微珠、玻璃鳞片、硅烷偶联剂、正丁醇和助剂直接加入搅拌釜中进行混合搅拌，搅拌速度800－1000r/min，搅拌时间30－45min。
本发明所述防火防腐涂料可兼顾防火和防腐的双重功能，所述涂料1mm的厚度即可达到2小时的防火时限，同时具有较强的防腐蚀性能，从而解决了化工企业高温装置防火防腐难的问题，有效地避免了因高温液体泄漏带来的火灾危害，更好地保护了公共财产免受损害。所述涂料与底材的附着力好，附着力在1.2MPa以上，从而避免了由于附着力差而导致的涂料早期失效问题。由于涂料与底材之间有很好的附着力同时涂层自身具有良好的机械性能，如耐磨损性等，使得该涂料可以在钢结构吊装之前进行施工，即进行工厂或者在现场吊装场地上进行施工。
具体实施方式
以下通过具体实施例对本发明的具体实施方式作进一步详细的说明。
实施例1
一种耐高温非膨胀型防火防腐涂料的制备方法，制备方法如下：将40份的正硅酸乙酯-32、20份的中空玻璃微珠、10份的玻璃鳞片、5份的硅烷偶联剂KH-55O、5份的分散剂HX-4030和20份的正丁醇直接加入搅拌釜中进行混合搅拌，搅拌速度800r/min，搅拌时间30min。
实施例2
一种耐高温非膨胀型防火防腐涂料的制备方法，制备方法如下：将50份的正硅酸乙酯-32、23份的中空玻璃微珠、12份的玻璃鳞片、8份的硅烷偶联剂KH-55O、8份的分散剂HX-4030和22份的正丁醇直接加入搅拌釜中进行混合搅拌，搅拌速度900r/min，搅拌时间40min。
实施例3
一种耐高温非膨胀型防火防腐涂料的制备方法，制备方法如下：将55份的正硅酸乙酯-32、25份的中空玻璃微珠、15份的玻璃鳞片、10份的硅烷偶联剂KH-55O、10份的分散剂HX-4030和25份的正丁醇直接加入搅拌釜中进行混合搅拌，搅拌速度1000r/min，搅拌时间45min。
将本发明所述耐高温非膨胀型防火防腐涂料进行各项性能检测，数据如下表1：
表1本发明所述耐高温非膨胀型防火防腐涂料性能检测数据
Figure BDA0000397929810000041
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。

Claims (7)

1.一种耐高温非膨胀型防火防腐涂料，其特征在于，其组成成分以质量份计为：
正硅酸乙酯            40－55份
中空玻璃微珠          20－25份
玻璃鳞片              10－15份
硅烷偶联剂            5－10份
正丁醇                20－25份
助剂                  5－10份。
2.如权利要求1所述的一种耐高温非膨胀型防火防腐涂料，其特征在于，所述正硅酸乙酯为正硅酸乙酯-32。
3.如权利要求1所述的一种耐高温非膨胀型防火防腐涂料，其特征在于，所述中空玻璃微珠的粒径范围分别为10－200um、10－100um和10－250 um；堆积密度分别为0.14－0.16g/cm3、0.18－0.20g/cm3和0.08－0.10g/cm3。
4.如权利要求1所述的一种耐高温非膨胀型防火防腐涂料，其特征在于，所述硅烷偶联剂为硅烷偶联剂KH-55O。
5.如权利要求1所述的一种耐高温非膨胀型防火防腐涂料，其特征在于，所述正丁醇的质量百分比浓度为95%。
6.如权利要求1所述的一种耐高温非膨胀型防火防腐涂料，其特征在于，所述助剂为分散剂HX-4030。
7.如权利要求1所述的一种耐高温非膨胀型防火防腐涂料的制备方法，其特征在于，制备方法如下：将正硅酸乙酯、中空玻璃微珠、玻璃鳞片、硅烷偶联剂、正丁醇和助剂直接加入搅拌釜中进行混合搅拌，搅拌速度800－1000r/min，搅拌时间30－45min。
CN201310493676.4A 2013-10-18 2013-10-18 一种耐高温非膨胀型防火防腐涂料及其制备方法 Pending CN103773224A (zh)