CN103773090A - 一种防腐蚀效果良好的玻璃钢复合涂层材料及其制备方法 - Google Patents

一种防腐蚀效果良好的玻璃钢复合涂层材料及其制备方法 Download PDF

Info

Publication number
CN103773090A
CN103773090A CN201410016878.4A CN201410016878A CN103773090A CN 103773090 A CN103773090 A CN 103773090A CN 201410016878 A CN201410016878 A CN 201410016878A CN 103773090 A CN103773090 A CN 103773090A
Authority
CN
China
Prior art keywords
parts
reinforced plastic
composite coating
coating material
plastic composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410016878.4A
Other languages
English (en)
Inventor
张庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Baoyi Amusement Equipment Co Ltd
Original Assignee
Wuhu Baoyi Amusement Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Baoyi Amusement Equipment Co Ltd filed Critical Wuhu Baoyi Amusement Equipment Co Ltd
Priority to CN201410016878.4A priority Critical patent/CN103773090A/zh
Publication of CN103773090A publication Critical patent/CN103773090A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防腐蚀效果良好的玻璃钢复合涂层材料，其特征在于，由下列重量份的原料制成：E-12环氧树脂30-34、苯乙烯9-12、α-甲基苯乙烯6-10、有机硅树脂12-14、聚四氟乙烯2-3、硅烷偶联剂KH-5501-2、四丁基溴化铵2-5、二丙二醇二丙烯酸酯15-18、短切玻璃纤维25-29、陶瓷粉5-8、过氧化甲乙酮10-13、KJP-1002环氧树脂固化剂2-4、凡士林3-5、四丁基溴化铵2-5、二丙二醇二丙烯酸酯2-4、助剂1-2；本发明添加助剂，使材料具有良好的物理性能以及机械性能；该材料具有良好的防腐蚀效果，质轻、无毒，生产工艺简单，成本低，适合工业化生产。

Description

一种防腐蚀效果良好的玻璃钢复合涂层材料及其制备方法
技术领域
本发明涉及一种复合涂层材料及其制备方法，特别是一种防腐蚀效果良好的玻璃钢复合涂层材料及其制备方法。
背景技术
玻璃钢材料是由玻璃纤维增强材料嵌入已固化的热固性树脂中或被其包裹形成复合结构的材料。目前市场上生产使用的玻璃钢材料多采用树脂浸润玻璃布材料来成型。该方法浸润效果好，所制备的玻璃纤维含量高。但由于受玻璃布体积和形状的限制，使其特别不适应用于诸如管接头、三通管件、弯头管件等不易均匀受压的产品。另外，该方法制备的玻璃钢材料其耐冲击性能差，且层合面容易发生分层。为了解决上述问题，有研究者将玻璃纤维切割成玻璃纤维粉，然后将玻璃纤维粉投入到由环氧树脂、增塑剂等组成的混合液中，再在球磨机中搅拌均匀加入填料、固化剂，由此制备成一种不含玻璃布铺层的玻璃钢材料。该方法所提供的玻璃钢材料虽然克服了玻璃布本身所导致的缺陷，但由于玻璃纤维被切割成粉状，因而其纤维本身所特有的物理特性亦被大大削弱。
发明内容
本发明的目的是提供一种防腐蚀效果良好的玻璃钢复合涂层材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种防腐蚀效果良好的玻璃钢复合涂层材料，由下列重量份的原料制成：E-12环氧树脂30-34、苯乙烯9-12、α-甲基苯乙烯6-10、有机硅树脂12-14、聚四氟乙烯2-3、硅烷偶联剂KH-550 1-2、四丁基溴化铵2-5、二丙二醇二丙烯酸酯15-18、短切玻璃纤维25-29、陶瓷粉5-8、过氧化甲乙酮10-13、KJP-1002环氧树脂固化剂2-4、凡士林3-5、四丁基溴化铵2-5、二丙二醇二丙烯酸酯2-4、助剂1-2；
所述助剂由下列重量份的原料制成：铁粉10-13、醋酸锌5-7、轻烧氧化镁4-6、麦饭石3-4、滑石粉3-5、泥炭2-3、二缩三丙二醇二丙烯酸酯2-3、吗啉1-2、抗坏血酸2-3、碳化硅3-4、壳聚糖1-2、丙烯酸甲酯3-4；制备方法是将铁粉、泥炭、麦饭石、轻烧氧化镁放入煅烧炉中，在550-570℃下煅烧4-5小时，取出，与滑石粉、抗坏血酸、碳化硅、壳聚糖混合，研磨至得到300-400目粉末，然后，再加入二缩三丙二醇二丙烯酸酯、吗啉、抗坏血酸、丙烯酸甲酯混合，继续研磨40-50分钟，至充分分散，再加入其它剩余成分，继续研磨30-45分钟后，在1400-1600转/分下搅拌15-30分钟，即得助剂。
本发明所述防腐蚀效果良好的玻璃钢复合涂层材料，由以下具体步骤制成：
（1）将E-12环氧树脂、苯乙烯、α-甲基苯乙烯、有机硅树脂、聚四氟乙烯、硅烷偶联剂KH-550放入反应釜中边搅拌边加热至熔融状态，得到A料；
（2）将短切玻璃纤维放入球磨机中磨碎，与陶瓷粉、醋酸锌、四丁基溴化铵、二丙二醇二丙烯酸酯进行混合，搅拌13-16分钟，得到B料；
（3）将A料与B料混合，加入助剂以及其余剩余成分，在450-600转/分的速度下搅拌20-25分钟，浇注、固化即可。
本发明的优点为：本发明添加助剂，使材料具有良好的物理性能以及机械性能；该材料具有耐酸、耐碱、耐高温、使用寿命长等特点，而且具有良好的防腐蚀效果，质轻、无毒，生产工艺简单，成本低，适合工业化生产。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种防腐蚀效果良好的玻璃钢复合涂层材料，由下列重量份（公斤）的原料制成：E-12环氧树脂30、苯乙烯9、α-甲基苯乙烯6、有机硅树脂12、聚四氟乙烯2、硅烷偶联剂KH-550 1、四丁基溴化铵2、二丙二醇二丙烯酸酯15、短切玻璃纤维25、陶瓷粉5、过氧化甲乙酮10、KJP-1002环氧树脂固化剂2、凡士林3、四丁基溴化铵2、二丙二醇二丙烯酸酯2、助剂1；
所述助剂由下列重量份（公斤）的原料制成：铁粉10、醋酸锌5、轻烧氧化镁4、麦饭石3、滑石粉3、泥炭2、二缩三丙二醇二丙烯酸酯2、吗啉1、抗坏血酸2、碳化硅3、壳聚糖1、丙烯酸甲酯3；制备方法是将铁粉、泥炭、麦饭石、轻烧氧化镁放入煅烧炉中，在550-570℃下煅烧4-5小时，取出，与滑石粉、抗坏血酸、碳化硅、壳聚糖混合，研磨至得到300-400目粉末，然后，再加入二缩三丙二醇二丙烯酸酯、吗啉、抗坏血酸、丙烯酸甲酯混合，继续研磨40-50分钟，至充分分散，再加入其它剩余成分，继续研磨30-45分钟后，在1400-1600转/分下搅拌15-30分钟，即得助剂。
本发明所述防腐蚀效果良好的玻璃钢复合涂层材料，由以下具体步骤制成：
（1）将E-12环氧树脂、苯乙烯、α-甲基苯乙烯、有机硅树脂、聚四氟乙烯、硅烷偶联剂KH-550放入反应釜中边搅拌边加热至熔融状态，得到A料；
（2）将短切玻璃纤维放入球磨机中磨碎，与陶瓷粉、醋酸锌、四丁基溴化铵、二丙二醇二丙烯酸酯进行混合，搅拌13-16分钟，得到B料；
（3）将A料与B料混合，加入助剂以及其余剩余成分，在450-600转/分的速度下搅拌20-25分钟，浇注、固化即可。
本发明实施例的玻璃钢材料的拉伸强度为243 Mpa。

Claims (2)

1.一种防腐蚀效果良好的玻璃钢复合涂层材料，其特征在于，由下列重量份的原料制成：E-12环氧树脂30-34、苯乙烯9-12、α-甲基苯乙烯6-10、有机硅树脂12-14、聚四氟乙烯2-3、硅烷偶联剂KH-550 1-2、四丁基溴化铵2-5、二丙二醇二丙烯酸酯15-18、短切玻璃纤维25-29、陶瓷粉5-8、过氧化甲乙酮10-13、KJP-1002环氧树脂固化剂2-4、凡士林3-5、四丁基溴化铵2-5、二丙二醇二丙烯酸酯2-4、助剂1-2；
所述助剂由下列重量份的原料制成：铁粉10-13、醋酸锌5-7、轻烧氧化镁4-6、麦饭石3-4、滑石粉3-5、泥炭2-3、二缩三丙二醇二丙烯酸酯2-3、吗啉1-2、抗坏血酸2-3、碳化硅3-4、壳聚糖1-2、丙烯酸甲酯3-4；制备方法是将铁粉、泥炭、麦饭石、轻烧氧化镁放入煅烧炉中，在550-570℃下煅烧4-5小时，取出，与滑石粉、抗坏血酸、碳化硅、壳聚糖混合，研磨至得到300-400目粉末，然后，再加入二缩三丙二醇二丙烯酸酯、吗啉、抗坏血酸、丙烯酸甲酯混合，继续研磨40-50分钟，至充分分散，再加入其它剩余成分，继续研磨30-45分钟后，在1400-1600转/分下搅拌15-30分钟，即得助剂。
2.根据权利要求1所述防腐蚀效果良好的玻璃钢复合涂层材料，其特征在于，由以下具体步骤制成：
（1）将E-12环氧树脂、苯乙烯、α-甲基苯乙烯、有机硅树脂、聚四氟乙烯、硅烷偶联剂KH-550放入反应釜中边搅拌边加热至熔融状态，得到A料；
（2）将短切玻璃纤维放入球磨机中磨碎，与陶瓷粉、醋酸锌、四丁基溴化铵、二丙二醇二丙烯酸酯进行混合，搅拌13-16分钟，得到B料；
（3）将A料与B料混合，加入助剂以及其余剩余成分，在450-600转/分的速度下搅拌20-25分钟，浇注、固化即可。
CN201410016878.4A 2014-01-15 2014-01-15 一种防腐蚀效果良好的玻璃钢复合涂层材料及其制备方法 Pending CN103773090A (zh)