CN103757913A - 一种阻燃的无纺布的制备方法 - Google Patents
一种阻燃的无纺布的制备方法 Download PDFInfo
- Publication number
- CN103757913A CN103757913A CN201310751316.XA CN201310751316A CN103757913A CN 103757913 A CN103757913 A CN 103757913A CN 201310751316 A CN201310751316 A CN 201310751316A CN 103757913 A CN103757913 A CN 103757913A
- Authority
- CN
- China
- Prior art keywords
- nonwoven fabric
- parts
- fire
- preparation
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种阻燃的无纺布的制备方法,包括以下步骤:(1)取聚丙烯材质的无纺布,将其室温下浸泡于水中1h~2h;(2)配制无纺布涂层,取硼酸锌粉末为6份~9份,膨润土为3~6份,聚磷酸铵为5~7份,硫酸铝为3~6份,ABS树脂为15份~18份;(3)加热后,将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀;(4)将加热后的涂层液涂布在无纺布的外表面,无纺布外涂层厚度为0.7mm~0.9mm,室温下晾干;(5)晾干后将无纺布保存,即为制备得到的阻燃的无纺布。
Description
技术领域
本发明涉及一种无纺布的制备方法,特别是涉及一种具有阻燃性能的无纺布的制备方法。
背景技术
无纺布的材质多为聚丙烯,因为其纤维无固定结构,不是经过纺织制成的,因此被称为无纺布。无纺布的应用较多,如被制作为口罩、台布、幕墙材料等。这些材质在应用中,有时需要具备较好的阻燃性能,若无纺布的阻燃性能较弱,在遇到明火时,有可能会发生燃烧的现象,危害人们的人身安全。提高无纺布的阻燃性能,需要对无纺布进行特殊的加工和处理,如采用一些阻燃物质附着于无纺布上,增强无纺布的阻燃性能。但是如何大范围的提高无纺布的阻燃性能,仍然有待研究。
发明内容
要解决的技术问题:普通的无纺布材料多为聚丙烯制备而成,在遇到明火时易燃,阻燃性能较差的问题。
技术方案:本发明公开了一种阻燃的无纺布的制备方法,包括以下步骤:(1)取聚丙烯材质的无纺布,将其室温下浸泡于水中1h~2h;(2)配制无纺布涂层,取硼酸锌粉末为6份~9份,膨润土为3~6份,聚磷酸铵为5~7份,硫酸铝为3~6份,ABS树脂为15份~18份;(3)加热后,将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀;(4)将加热后的涂层液涂布在无纺布的外表面,无纺布外涂层厚度为0.7mm~0.9mm,室温下晾干;(5)晾干后将无纺布保存,即为制备得到的阻燃的无纺布。
其中,无纺布中聚丙烯的含量优选为75wt%~85wt%。所述的硼酸锌粉末优选为6份。无纺布外涂层厚度优选为0.8mm~0.9mm。所述涂层中,ABS树脂的含量为优选为18份。
有益效果:本方法制备得到的无纺布具有良好的阻燃效果,测试阻燃性能的方法为GB/T5455-1997,本发明的无纺布阻燃等级为B1和B2级。
具体实施方式
实施例1
(1)取聚丙烯材质的无纺布,将其室温下浸泡于水中2h;(2)配制无纺布涂层,取硼酸锌粉末为9kg,膨润土为6kg,聚磷酸铵为5kg,硫酸铝为3kg,ABS树脂为15kg;(3)加热后,将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀;(4)将加热后的涂层液涂布在无纺布的外表面,无纺布外涂层厚度为0.9mm,室温下晾干;(5)晾干后将无纺布保存,即为制备得到的阻燃的无纺布。
实施例2
(1)取聚丙烯材质的无纺布,将其室温下浸泡于水中1h;(2)配制无纺布涂层,取硼酸锌粉末为6kg,膨润土为3kg,聚磷酸铵为6kg,硫酸铝为4kg,ABS树脂为18kg;(3)加热后,将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀;(4)将加热后的涂层液涂布在无纺布的外表面,无纺布外涂层厚度为0.8mm,室温下晾干;(5)晾干后将无纺布保存,即为制备得到的阻燃的无纺布。
实施例3
(1)取聚丙烯材质的无纺布,将其室温下浸泡于水中2h;(2)配制无纺布涂层,取硼酸锌粉末为7kg,膨润土为5kg,聚磷酸铵为7kg,硫酸铝为6kg,ABS树脂为17kg;(3)加热后,将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀;(4)将加热后的涂层液涂布在无纺布的外表面,无纺布外涂层厚度为0.7mm,室温下晾干;(5)晾干后将无纺布保存,即为制备得到的阻燃的无纺布。
对本发明的无纺布的阻燃性能进行了试验,试验方法为GB/T5455-1997,实施例1、实施例2、实施例3的无纺布的阻燃等级如下。
实施例1 | 实施例2 | 实施例3 | |
阻燃等级 | B1 | B2 | B1 |
如表中所述,本发明的实施例1、实施例2、实施例3的无纺布的阻燃等级都较高,具有良好的阻燃性能,具有不易燃烧的特点。
Claims (5)
1. 一种阻燃的无纺布的制备方法,其特征在于包括以下步骤:(1)取聚丙烯材质的无纺布,将其室温下浸泡于水中1h~2h;(2)配制无纺布涂层,取硼酸锌粉末为6份~9份,膨润土为3~6份,聚磷酸铵为5~7份,硫酸铝为3~6份,ABS树脂为15份~18份;(3)加热后,将硼酸锌粉末、膨润土、聚磷酸铵、硫酸铝、ABS树脂混合均匀;(4)将加热后的涂层液涂布在无纺布的外表面,无纺布外涂层厚度为0.7mm~0.9mm,室温下晾干;(5)晾干后将无纺布保存,即为制备得到的阻燃的无纺布。
2. 根据权利要求1所述的一种阻燃的无纺布的制备方法,其特征在于无纺布中聚丙烯的含量为75wt%~85wt%。
3. 根据权利要求1所述的一种阻燃的无纺布的制备方法,其特征在于所述的硼酸锌粉末为6份。
4. 根据权利要求1所述的一种阻燃的无纺布的制备方法,其特征在于无纺布外涂层厚度为0.8mm~0.9mm。
5. 根据权利要求1所述的一种阻燃的无纺布的制备方法,其特征在于所述的ABS树脂为18份。