CN103726313A - 防紫外线纯棉织物的整理方法 - Google Patents
防紫外线纯棉织物的整理方法 Download PDFInfo
- Publication number
- CN103726313A CN103726313A CN201310604309.7A CN201310604309A CN103726313A CN 103726313 A CN103726313 A CN 103726313A CN 201310604309 A CN201310604309 A CN 201310604309A CN 103726313 A CN103726313 A CN 103726313A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- ultraviolet
- cotton fabric
- pure cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防紫外线纯棉织物的整理方法,包括如下步骤:将5-6质量份油酸聚氧乙烯酯、10-15质量份2-(2'-羟基-5'-甲基苯基)苯并***、35-40质量份双(3,5-二叔丁基-4-羟基)苄基膦酸单乙酯和11-14质量份沸石混合,然后同时缓慢加入5-10质量份乙酸乙酯、10-15质量份氧化锌和2-3质量份聚丙烯酸钠分散剂,35-40分钟内投料完毕,继续混合1-2小时,制得防紫外线整理剂;将棉织物在含有65-70%防紫外线整理剂的浸渍液中浸轧处理,压力1-2MPa,带液率75-77%,烘干后将织物在100-110℃恒温4-5小时。本发明整理后纯棉织物防紫外线耐久性强,对纯棉织物有优良的防紫外作用,无毒安全。
Description
技术领域
本发明涉及防紫外线纯棉织物的整理方法。
背景技术
目前的防紫外线棉织物,其抗紫外线整理剂具有一定毒性,且防紫外线耐久性不理想。
发明内容
本发明的目的在于提供一种防紫外线纯棉织物的整理方法,其整理后纯棉织物防紫外线耐久性强,对纯棉织物有优良的防紫外作用,无毒安全。
为实现上述目的,本发明的技术方案是设计一种防紫外线纯棉织物的整理方法,包括如下步骤:
将5-6质量份油酸聚氧乙烯酯、10-15质量份2-(2'-羟基-5'-甲基苯基)苯并***、35-40质量份双(3,5-二叔丁基-4-羟基)苄基膦酸单乙酯和11-14质量份沸石混合,然后同时缓慢加入5-10质量份乙酸乙酯、10-15质量份氧化锌和2-3质量份聚丙烯酸钠分散剂,35-40分钟内投料完毕,继续混合1-2小时,制得防紫外线整理剂;
将棉织物在含有65-70%防紫外线整理剂的浸渍液中浸轧处理,压力1-2MPa,带液率75-77%,烘干后将织物在100-110℃恒温4-5小时。
本发明的优点和有益效果在于:提供一种防紫外线纯棉织物的整理方法,其整理后纯棉织物防紫外线耐久性强,对纯棉织物有优良的防紫外作用,无毒安全。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种防紫外线纯棉织物的整理方法,包括如下步骤:
将5质量份油酸聚氧乙烯酯、10质量份2-(2'-羟基-5'-甲基苯基)苯并***、35质量份双(3,5-二叔丁基-4-羟基)苄基膦酸单乙酯和11质量份沸石混合,然后同时缓慢加入5质量份乙酸乙酯、10质量份氧化锌和2质量份聚丙烯酸钠分散剂,35分钟内投料完毕,继续混合1小时,制得防紫外线整理剂;
将棉织物在含有65%防紫外线整理剂的浸渍液中浸轧处理,压力1MPa,带液率757%,烘干后将织物在100℃恒温4小时。
实施例2
一种防紫外线纯棉织物的整理方法,包括如下步骤:
将6质量份油酸聚氧乙烯酯、15质量份2-(2'-羟基-5'-甲基苯基)苯并***、40质量份双(3,5-二叔丁基-4-羟基)苄基膦酸单乙酯和14质量份沸石混合,然后同时缓慢加入10质量份乙酸乙酯、15质量份氧化锌和3质量份聚丙烯酸钠分散剂,40分钟内投料完毕,继续混合2小时,制得防紫外线整理剂;
将棉织物在含有70%防紫外线整理剂的浸渍液中浸轧处理,压力2MPa,带液率77%,烘干后将织物在110℃恒温5小时。
实施例3
一种防紫外线纯棉织物的整理方法,包括如下步骤:
将5。6质量份油酸聚氧乙烯酯、13质量份2-(2'-羟基-5'-甲基苯基)苯并***、37质量份双(3,5-二叔丁基-4-羟基)苄基膦酸单乙酯和13质量份沸石混合,然后同时缓慢加入8质量份乙酸乙酯、13质量份氧化锌和2.3质量份聚丙烯酸钠分散剂,38分钟内投料完毕,继续混合1.5小时,制得防紫外线整理剂;
将棉织物在含有68%防紫外线整理剂的浸渍液中浸轧处理,压力1.2MPa,带液率76%,烘干后将织物在105℃恒温4.5小时。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.防紫外线纯棉织物的整理方法,其特征在于,包括如下步骤:
将5-6质量份油酸聚氧乙烯酯、10-15质量份2-(2'-羟基-5'-甲基苯基)苯并***、35-40质量份双(3,5-二叔丁基-4-羟基)苄基膦酸单乙酯和11-14质量份沸石混合,然后同时缓慢加入5-10质量份乙酸乙酯、10-15质量份氧化锌和2-3质量份聚丙烯酸钠分散剂,35-40分钟内投料完毕,继续混合1-2小时,制得防紫外线整理剂;
将棉织物在含有65-70%防紫外线整理剂的浸渍液中浸轧处理,压力1-2MPa,带液率75-77%,烘干后将织物在100-110℃恒温4-5小时。