CN103725020A - 一种高固沥青基密封膏及其生产方法 - Google Patents
一种高固沥青基密封膏及其生产方法 Download PDFInfo
- Publication number
- CN103725020A CN103725020A CN201210390338.3A CN201210390338A CN103725020A CN 103725020 A CN103725020 A CN 103725020A CN 201210390338 A CN201210390338 A CN 201210390338A CN 103725020 A CN103725020 A CN 103725020A
- Authority
- CN
- China
- Prior art keywords
- compound
- good
- performed polymer
- production method
- asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及防水材料技术领域，具体的说是一种高固沥青基密封膏及，用羟基硅油与交联剂反应得到预聚体，预聚体在空气中接触大气中的湿气，与水发生水解反应。水解后生成的活性基团再与预聚体反应，生产一种网络结构，得到了一种较好的弹性物质。沥青和填充料的加入使得此密封膏具备了很好的水密性和气密性，防水密封效果优异，与沥青基卷材的相容性更好。这样此密封膏不但具备很好的强度和防水密封效果，而且在立面施工和高温环境下不易流淌，耐老化性能也好。
Description
技术领域
本发明涉及防水材料技术领域，具体的说是一种高固沥青基密封膏及生产方法。
背景技术
近年来，随着化工建材的不断发展，建筑防水密封材料的品种不断增多，除传统的塑料防水油膏、橡胶沥青防水油膏、桐油沥青防水油膏外，出现了性能优异的高分子嵌缝密封材料，如丙烯酸密封膏、聚硫密封材料、聚氨酯密封材料、硅酮密封材料等。这些已成为***推荐的新型防水密封材料。
建筑防水用密封材料主要用于建筑物人为设置的伸缩缝、沉降缝、建筑结构节点、构建间的结合部、门窗框四周、玻璃镶嵌部等、能起到气密性和水密性作用的材料。只要用于建筑物屋面、地下工程、幕墙装饰工程及其他部位的嵌缝密封防水，起到防水、防尘、隔音、保温等功能。近年来，随着人们对建筑工程质量和日常使用安全的高度重视，已成为各类建筑不可缺少的功能材料。
20世纪90年代来建筑防水密封材料的总趋势用量持续增加，产品向高功能的弹性体密封膏方向发展，由于环境保护对VOC（有机挥发物含量）的要求愈来愈高，溶剂型的密封膏将减少，一些低档油性防水密封材料使用比例下降，环保高性能的防水密封材料将受到市场的宠爱。
因此，针对上述情况而设计出具有优异的水密性和气密性、良好的耐久性且安全环保的一种高固沥青基密封膏及生产方法，正是发明人所要解决的问题。
发明内容
本发明的目的是提供一种高固沥青基密封膏及生产方法，其具有优异的水密性和气密性、良好的耐久性且安全环保，有非常高的实用价值。
本发明解决其技术问题所采用的技术方案是：一种高固沥青基密封膏，包含沥青、羟基硅油和交联剂、增塑剂、填充料、助剂及催化剂。
一种高固沥青基密封膏生产方法，方法包含以下步骤：
a. 将沥青、增塑剂、填充料及基料通过搅拌混合均匀，同时对以上混合材料进行加热及抽真空；
b. 在混合后的材料中加入交联剂脱水处理后反应成预聚体，然后对预聚体进行降温处理，降温处理后加入催化剂及助剂，对灌装在密封容器中，使用时从容器中挤出，接触大气中的湿气后，与空气中的水发生水解反应，生成带-0H的化合物；
c. 此化合物再与预聚体的高分子化合物反应，以上两步反应交替进行，交联成网络结构，形成性能优异的弹性体。
本发明的有益效果是：
1、优异的水密性和气密性：由于此密封膏为反应型密缝材料且含沥青组分，里面高分子化合物交联成网络结构，沥青填充在网络结构中，密封材料固化后表干后，水分子就很难通过此结构。
2、极强的粘附性：此密封膏和结构混凝土及沥青基的材料粘附性极强。牢固的粘结在结构结合部的表面，和沥青基自粘防水材料的粘附性可以融为一体，密不可分。
3、良好的耐久性：密封材料在大气中能经受一年四季的风吹日晒、雨雪冻融等恶劣环境条件考验。许多高分子材料在紫外线、臭氧、微生物、酸、碱、盐等环境中要抗老化，此外还要承受强风、地震及气温和日照变化而产生的构件变形及变位的外力作用。要求密封材料在这些因素作用下仍然保持良好的气密性和水密性，这就要求密封材料必须经受住长期压缩----拉伸震动疲劳作用，必须具备一定的抗拉强度。而此高分子密封材料分子结构交联成网络结构，本身具备较好的拉伸强度等力学物理性能指标。可以很好的适用环境造成的变质和损伤。
4、安全环保：此密封膏不含有毒溶剂，无有机挥发物，施工方便安全，对环境友好。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围，此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落在申请所附权利要求书所限定的范围。
一种高固沥青基密封膏，包含沥青、羟基硅油和交联剂、增塑剂、填充料、助剂及催化剂，加工该密封膏的方法抱哈以下步骤：a.将沥青、增塑剂、填充料及基料通过搅拌混合均匀，同时对以上混合材料进行加热及抽真空；b.在混合后的材料中加入交联剂脱水处理后反应成预聚体，然后对预聚体进行降温处理，降温处理后加入催化剂及助剂，对灌装在密封容器中，使用时从容器中挤出，接触大气中的湿气后，与空气中的水发生水解反应，生成带-0H的化合物；c.此化合物再与预聚体的高分子化合物反应，以上两步反应交替进行，交联成网络结构，形成性能优异的弹性体。
用羟基硅油与交联剂反应得到预聚体，预聚体在空气中接触大气中的湿气，与水发生水解反应。水解后生成的活性基团再与预聚体反应，生产一种网络结构，得到了一种较好的弹性物质。沥青和填充料的加入使得此密封膏具备了很好的水密性和气密性，防水密封效果优异，与沥青基卷材的相容性更好。这样此密封膏不但具备很好的强度和防水密封效果，而且在立面施工和高温环境下不易流淌，耐老化性能也好。
此高固沥青基密封膏不含有毒溶剂，对环境不造成污染，施工方便，安全环保，性能优异，耐候性好，很好的解决了沥青基防水材料搭接密封的问题。它的力学性能指标要远远高于普通的沥青基密封膏，由于组分中含有部分沥青，使得它与沥青基的卷材具有很好的相容性，且沥青的防水效果比其他物质更好。可以很好的解决沥青基自粘卷材的短边搭接及长边搭接的密封处理。使得搭接部位的防水更加可靠、安全。
Claims (2)
1.一种高固沥青基密封膏，包含沥青、羟基硅油和交联剂、增塑剂、填充料、助剂及催化剂。
2.一种高固沥青基密封膏生产方法，方法包含以下步骤：
a．将沥青、增塑剂、填充料及基料通过搅拌混合均匀，同时对以上混合材料进行加热及抽真空；
b．在混合后的材料中加入交联剂脱水处理后反应成预聚体，然后对预聚体进行降温处理，降温处理后加入催化剂及助剂，对灌装在密封容器中，使用时从容器中挤出，接触大气中的湿气后，与空气中的水发生水解反应，生成带-0H的化合物；
c．此化合物再与预聚体的高分子化合物反应，以上两步反应交替进行，交联成网络结构，形成性能优异的弹性体。