CN103724698A - O-ring produced through reclaimed Buna-N rubber - Google Patents
O-ring produced through reclaimed Buna-N rubber Download PDFInfo
- Publication number
- CN103724698A CN103724698A CN201310683814.5A CN201310683814A CN103724698A CN 103724698 A CN103724698 A CN 103724698A CN 201310683814 A CN201310683814 A CN 201310683814A CN 103724698 A CN103724698 A CN 103724698A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- raw material
- buna
- reclaimed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an O-ring produced through reclaimed Buna-N rubber, which is prepared from the following raw materials in parts by weight: 30-40 parts of reclaimed Buna-N rubber, 40-50 parts of natural rubber, 20-30 parts of coarse whiting, 5-8 parts of antimonous oxide, 1-2 parts of DPOP, 2-4 parts of a vulcanizing agent moca, 0.2-0.4 part of methyl 2,2-dithienylglycolate, 0.1-0.2 part of magnetic powder, 1-2 parts of red lead, 2-3 parts of a silane coupling agent KH570, 1-2 parts of an accelerant BF1 and 30-40 parts of modified filler. According to the invention, the reclaimed Buna-N rubber is adopted to produce products, the waste material is changed into things of wealth, resources are saved, reuse of waste is realized and the obtained product is excellent in all the mechanical performances.
Description
Technical field
The present invention relates to field of rubber materials, is exactly a kind of O type circle that utilizes the fine regenerated rubber of fourth to produce.
Background technology
O RunddichtringO O type circle (O-rings) is that a kind of cross section is circular rubber seal, because its cross section is O type, therefore be called O RunddichtringO, is also O type circle.Start to appear in the middle of the 19th century, with it, make at that time the sealing element of steamer cylinder.
O RunddichtringO is applicable to be contained in various mechanical means, in the temperature, pressure of regulation and different liquids and gases medium, under static or kinestate, seals.On lathe, boats and ships, automobile, aerospace equipment, metallurgical machinery, chemical machinery, engineering machinery, building machinery, mining machinery, petroleum machinery, plastics machinery, agricultural machine and all kinds of instrument, widely applying various types of sealing elements.O RunddichtringO is mainly used in static seal and reciprocating movement sealing.While being used for rotatablely moving sealing, only limit to low speed rotary seal.O RunddichtringO is generally arranged in the groove that cylindrical or inner circle upper section are rectangle and seals.O RunddichtringO still plays excellent sealing, cushioning effect at environment such as oil resistant, soda acid, mill, chemical erosions.Therefore, O RunddichtringO is most popular a kind of sealing member in hydraulic and pneumatic transmission system.
Summary of the invention
The object of the present invention is to provide a kind of O type circle that utilizes the fine regenerated rubber of fourth to produce.
Above-mentioned purpose realizes by following scheme:
A kind of O type circle that utilizes the fine regenerated rubber of fourth to produce, it is characterized in that: it is that raw material by following weight parts makes: the fine regenerated rubber 30-40 of fourth, natural rubber 40-50, water-ground limestone 20-30, antimonous oxide 5-8, the different monooctyl ester 1-2 of phosphorous acid hexichol one, vulcanizing agent moca 2-4,2,2-dithienyl methyl glycolate 0.2-0.4, magnetic 0.1-0.2, tri-lead tetroxide 1-2, silane coupling agent KH570 2-3, accelerant B F 1-2, modified filler 30-40;
Described modified filler is made by the raw material of following weight parts:
Magnesium hydroxide 10-20, epoxy soybean oil 1-2, oxidation inhibitor 1135 1-2,, silane coupling agent KH560 1.5-2.5, oxidation inhibitor 1046 1-2, antioxidant 1010 1-2, lipid acid 0.8-1.5, citric acid 1-2, potter's clay 15-18, tremolite powder 10-20, blast-furnace slag 10-20;
The preparation method of described modified filler is:
By after blast-furnace slag fragmentation, with deionized water, steep after 5-7 hour, filtering drying, then ground granulated blast furnace slag and tremolite powder after drying are mixed, at 870-950 ℃, calcine 1-2 hour, take out cooling after, after all the other raw material blendings, add appropriate water, under 1500-1600 rev/min, stir after 10-20 minute, ovendry power is broken into powder, crosses after 400-500 mesh sieve, obtains.
Described a kind of O type circle that utilizes the fine regenerated rubber of fourth to produce, is characterized in that:
Preparation method is: first the fine regenerated rubber of fourth, natural rubber, magnetic, tri-lead tetroxide are put into Banbury mixer at 100-110 ℃ mixing completely after, again by after gained sizing material and all the other raw material blendings, put into mill at 120-130 ℃ by weight mixing completely after, reprocessing moulding and get final product.
Beneficial effect of the present invention is: the present invention utilizes the fine regenerated rubber of fourth to produce product, turns waste into wealth, and economizes on resources, and when realizing the recycling of waste, the every mechanical property of products obtained therefrom is excellent.
Embodiment
A kind of O type circle that utilizes the fine regenerated rubber of fourth to produce, it is that raw material by following weight kg makes: the fine regenerated rubber 35 of fourth, natural rubber 50, water-ground limestone 30, antimonous oxide 8, the different monooctyl ester 2 of phosphorous acid hexichol one, vulcanizing agent moca 4,2,2-dithienyl methyl glycolate 0.4, magnetic 0.1, tri-lead tetroxide 1, silane coupling agent KH570 2, accelerant B F 2, modified filler 40;
Described modified filler is made by the raw material of following weight kg:
Magnesium hydroxide 20, epoxy soybean oil 1, oxidation inhibitor 1,135 2,, silane coupling agent KH560 1.8, oxidation inhibitor 1,046 2, antioxidant 1010 1.8, lipid acid 1.5, citric acid 2, potter's clay 18, tremolite powder 20, blast-furnace slag 20;
The preparation method of described modified filler is:
By after blast-furnace slag fragmentation, with deionized water, steep after 6 hours, filtering drying, then ground granulated blast furnace slag and tremolite powder after drying are mixed, at 950 ℃, calcine 2 hours, take out cooling after, after all the other raw material blendings, add appropriate water, under 1500 revs/min, stir after 20 minutes, ovendry power is broken into powder, crosses after 500 mesh sieves, obtains.
Described a kind of O type circle that utilizes the fine regenerated rubber of fourth to produce,
Preparation method is: first the fine regenerated rubber of fourth, natural rubber, magnetic, tri-lead tetroxide are put into Banbury mixer at 106 ℃ mixing completely after, again by after gained sizing material and all the other raw material blendings, put into mill at 127 ℃ by weight mixing completely after, reprocessing moulding and get final product.
Performance test:
Tensile strength: 15.1 MPa;
Elongation at break: 524%;
Oil-proofness: 100 ℃ * 70h of 20# machine oil, elongation at break conservation rate 77.4%, tensile strength conservation rate 79.8%;
Resistance to ozone: 26 ℃, 24h, ozone concn 0.026%, without cracking;
Ageing-resistant: 120 ℃, 150h, tensile strength conservation rate 88.9%, elongation at break conservation rate 88.1%;
The cold-resistant coefficient (32 ℃) 0.54 of compression.
Claims (2)
1. an O type circle that utilizes the fine regenerated rubber of fourth to produce, it is characterized in that: it is that raw material by following weight parts makes: the fine regenerated rubber 30-40 of fourth, natural rubber 40-50, water-ground limestone 20-30, antimonous oxide 5-8, the different monooctyl ester 1-2 of phosphorous acid hexichol one, vulcanizing agent moca 2-4,2,2-dithienyl methyl glycolate 0.2-0.4, magnetic 0.1-0.2, tri-lead tetroxide 1-2, silane coupling agent KH570 2-3, accelerant B F 1-2, modified filler 30-40;
Described modified filler is made by the raw material of following weight parts:
Magnesium hydroxide 10-20, epoxy soybean oil 1-2, oxidation inhibitor 1135 1-2,, silane coupling agent KH560 1.5-2.5, oxidation inhibitor 1046 1-2, antioxidant 1010 1-2, lipid acid 0.8-1.5, citric acid 1-2, potter's clay 15-18, tremolite powder 10-20, blast-furnace slag 10-20;
The preparation method of described modified filler is:
By after blast-furnace slag fragmentation, with deionized water, steep after 5-7 hour, filtering drying, then ground granulated blast furnace slag and tremolite powder after drying are mixed, at 870-950 ℃, calcine 1-2 hour, take out cooling after, after all the other raw material blendings, add appropriate water, under 1500-1600 rev/min, stir after 10-20 minute, ovendry power is broken into powder, crosses after 400-500 mesh sieve, obtains.
2. a kind of O type circle that utilizes the fine regenerated rubber of fourth to produce according to claim 1, is characterized in that:
Preparation method is: first the fine regenerated rubber of fourth, natural rubber, magnetic, tri-lead tetroxide are put into Banbury mixer at 100-110 ℃ mixing completely after, again by after gained sizing material and all the other raw material blendings, put into mill at 120-130 ℃ by weight mixing completely after, reprocessing moulding and get final product.