CN103708705A - Silt curing agent and production method thereof - Google Patents
Silt curing agent and production method thereof Download PDFInfo
- Publication number
- CN103708705A CN103708705A CN201310710591.7A CN201310710591A CN103708705A CN 103708705 A CN103708705 A CN 103708705A CN 201310710591 A CN201310710591 A CN 201310710591A CN 103708705 A CN103708705 A CN 103708705A
- Authority
- CN
- China
- Prior art keywords
- parts
- curing agent
- sludge curing
- power
- gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a silt curing agent and a production method thereof. The silt curing agent comprises the following components according to the following ratios: 18-20 parts of fluorite, 20-23 parts of sodium carbonate, 7-9 parts of quartz sand, 40-50 parts of gypsum, 10-12 parts of quick lime, and 6-8 parts of limestone. The silt curing agent disclosed by the invention can be used in the curing of silt or sludge with high water content from a sewage treatment plant, produced in industrial production or natural environment, and is also applicable to rapid setting and rapid hardening of cement slurry, high in curing strength, not easy to crack and good in strength durability, and the cured silt or cement is applicable to the machining of building products or directly used as a building material of civil engineering such as roads, dams and the like, thus being energy-saving and environment-friendly. Moreover, in the curing process of the sludge, certain volume expansion also can be generated, thus being conducive to the improvement of structure compactibility of the building products.
Description
Technical field
The invention belongs to environmental technology field, be specially a kind of sludge curing agent and manufacture method thereof that makes mud be used as renewable resource.
Background technology
Along with the development of national economy, environmental pollution is day by day serious, and compared in the past, people have more urgent demand to environmental improvement, but along with the diversification of industrial development, source of pollution are also more complicated.
In municipal effluent, just have and come from the various sewage that residential building, unit, school, hospital and communal facility drainage mechanism are collected.And mud is as the fittings of sewage disposal, the composition of mostly cannot filtering in sewage or clearing up all precipitates and concentrates in mud, the techniques such as that the treatment process of mud mainly comprises is concentrated, dehydration, digestion, fermentation, mummification, after processing by sanitary landfill, water body dissolve, the mode such as burning disposal, compost treatment and soil utilization make mud can minimizing, resource utilization.But some mud is because composition is too complicated, or in post-processed, sludge components structure is destroyed, and cause its become cannot be curing mud.For this mud, because it is in fluid state, cannot be existed easily with water body flow by appropriate disposal, make contaminated area extension; After muck surface is dry, dust can fly away into the medium harm of atmosphere, therefore need can make its method settling out in the short period of time, sludge solidifying agent is exactly one of product that object produces thus.
And sludge solidifying agent effect is in the market not satisfactory, solidification intensity is low, and can not be directly used in the mud that water content is higher, conventionally also need mud to do the processing that reduces water content, and complex procedures, cost is higher.
Summary of the invention
Technical purpose of the present invention is for the problem existing in reality, the sludge curing agent that a kind of cost is low, solidification effect is good is provided, can be directly used in solidifying of high-moisture mud, as the mud or the mud that produce from sewage work, industrial production, the mud producing from river course, lake etc., and be equally applicable to solidifying of grout.
For realizing above-mentioned technical purpose, technical scheme provided by the invention is:
A sludge curing agent, is characterized in that, comprises the component of following weight proportion:
The fluorite of 18~20 parts, the soda ash of 20~23 parts, the quartz sand of 7~9 parts, the gypsum of 40~50 parts, the unslaked lime of 10~12 parts, the Wingdale of 6~8 parts.
As preferably, described gypsum can adopt fluorgypsum.Fluorgypsum, mainly from using industrial solid waste, originates from the factories such as inorganic fluoride, organic fluoride factory and other hydrofluoric acid, and output is considerable, for belonging to the strong harmful solid waste of corrodibility, plant, animal and human is had to great side effect.Therefore use in a large number in the present invention, realize waste recycling, energy-conserving and environment-protective.
Further, by after contained component combined grinding, it is 300~600m that solidifying agent body is specific surface area
2/ kg's is Powdered, when mud is done to solidification treatment, easy to use, and solidification effect is good.
The present invention provides a kind of manufacture method of sludge curing agent simultaneously, can be used as the production of above-mentioned sludge curing agent, it is characterized in that, comprises the following steps:
(1) Fluorspar Powder of 18~20 mass parts is broken to the particle of particle diameter below 10mm;
(2) fluorite after pulverizing is mixed with the soda ash of 20~23 mass parts, the quartz sand of 7~9 mass parts, then by mixture grinding to particle diameter below 1mm;
(3) mixed powder after grinding is sent into calcining compartment calcining;
(4) fluorite, soda ash and quartz sand powder after the Wingdale of the unslaked lime of the gypsum of 40~50 mass parts, 10~12 mass parts, 6~8 mass parts and calcining are milled to predetermined pulverulence, mix.
Further, the calcining temperature of step (3) is controlled at 800~900 ℃.
Further, in step (4), by each component mixture grinding of solidifying agent to specific surface area 300~600m
2after/kg, can pack.
Beneficial effect of the present invention:
1) solidifying agent of the present invention is applied in the slurried materiales such as mud or cement, can realize fast solidifying, hard soon.When sclerosis, can also produce certain volumetric expansion, be conducive to improve the structure density of building product, strengthen grogs cohesiveness, therefore there is early strong, high-strength feature;
2) solidifying agent of the present invention passes through chemical reaction, from mud, absorb a large amount of free water contents and change into hydrated product crystal water, therefore under high water-solid ratio, can avoid the sedimentation phenomenon of particle before condensing, can directly solidify water content up to mud or the mud of 100%-300%, the intensity after solidifying and the volume of solidifying agent are proportional;
3) use solidifying agent of the present invention, it is little that hydration reaction is affected by organic matter, can cohere organic soil, to also having good solidification effect containing organic high cement slurry and mud;
4) solidifying agent of the present invention is powdered material, curing easy to use, at the construction field (site) solidifying agent is added in mud or mud and stirs and can realize fast setting in predetermined ratio;
5) curing mud or the mud of solidifying agent of the present invention both can harden in air, also can in water, harden, the mud or the sludge solidification body chemical resistance of concrete that reach some strength are good, even the dry wet immersion effect of seawater, cured body can not ftracture yet, and intensity does not decline yet.
Embodiment
In order to illustrate technical scheme of the present invention and technique effect, below in conjunction with specific embodiment, the present invention is described further.
Sludge curing agent of the present invention, mainly comprises the component of following weight proportion:
18~20 parts, fluorite (fluorite);
20~23 parts of soda ash (sodium carbonate);
7~9 parts of quartz sands;
40~50 parts, gypsum;
10~12 parts of unslaked limes;
6~8 parts, Wingdale.
embodiment 1:
A sludge curing agent, consists of the component of following weight part proportioning: 18 parts of fluorites, 23 parts of soda ash, 9 parts of quartz sands, 40 parts of fluorgypsums, 12 parts of unslaked limes, 8 parts of Wingdales.
In manufacturing processed, first, Fluorspar Powder is broken to the particle of particle diameter below 10mm.Fluorite after pulverizing is mixed with soda ash, quartz sand, then by mixture grinding to particle diameter below 1mm, afterwards the mixed powder after grinding is sent into the calcining compartment of 800 ℃~900 ℃ and is calcined.
Finally, after the mixed powder after calcining is mixed with fluorgypsum, unslaked lime and Wingdale etc., further grinding, grinding is to specific surface area 300~600m
2/ kg, can pack deposit standby.
embodiment 2:
A sludge curing agent, consists of the component of following weight part proportioning: 18~19 parts of fluorites, 21~22 parts of soda ash, 8 parts of quartz sands, 45 parts of fluorgypsums, 10~11 parts of unslaked limes, 6~7 parts of Wingdales.Described fluorgypsum is to fluoridize the by product that saltworks utilizes fluorite and vitriol oil preparing hydrogen fluoric acid.
In manufacturing processed, first, Fluorspar Powder is broken to the particle of particle diameter below 10mm.Fluorite after pulverizing is mixed with soda ash, quartz sand, then by mixture grinding to particle diameter below 1mm, afterwards the mixed powder after grinding is sent into the calcining compartment of 800 ℃~900 ℃ and is calcined.
Finally, after the mixed powder after calcining is mixed with fluorgypsum, unslaked lime and Wingdale etc., carry out grinding, grinding is to specific surface area 300~600m
2/ kg, can pack deposit standby.
embodiment 3:
A sludge curing agent, consists of the component of following weight part proportioning: 19 parts of fluorites, 21.5 parts of soda ash, 8 parts of quartz sands, 42~48 parts of fluorgypsums, 11 parts of unslaked limes, 7 parts of Wingdales.Described fluorgypsum comes from the by product that fluoride salt is produced.
In manufacturing processed, first, Fluorspar Powder is broken to the particle of particle diameter below 10mm.Fluorite after pulverizing is mixed with soda ash, quartz sand, then by mixture grinding to particle diameter below 1mm, afterwards the mixed powder after grinding is sent into the calcining compartment of 850 ℃ and is calcined.
Finally, after the mixed powder after calcining is mixed with fluorgypsum, unslaked lime and Wingdale etc., carry out grinding, grinding is to specific surface area 400~500m
2/ kg, can pack deposit standby.
By above-mentioned embodiment, after solidifying agent is made.During use, by treating that mud such as curing mud, mud or cement etc. first sieve, remove impurity, pulverize the clod of bonding, according to the water content of mud, in mud, mix appropriate solidifying agent powder.General water content is the proportion of 100%~300%(moisture content and dry earth) mud, according to inner blending method, mix 15%~35%(solidifying agent and gross weight ratio) solidifying agent powder, at normal temperatures, solidify after 2 hours, can there is certain intensity, general volume is more, and solidification intensity is larger.And common sludge solidifying agent generally can only become the sludge solidification of such high-moisture curdled appearance, do not there is actual strength, cannot meet the demand of building product.
Because different solidifying agent proportionings are different, its solidification effect is difference slightly.Before to a large amount of slurry curings, the mud that can take a morsel mixes the solidifying agent of different ratios, does contrast test experiment, according to target solidification intensity, chooses the optimum ratio that mixes.
More than show and described ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand, the present invention is not restricted to the described embodiments, that in above-described embodiment and specification sheets, describes just illustrates principle of the present invention, and without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications.The claimed scope of the present invention is defined by appending claims, specification sheets and equivalent thereof.
Claims (9)
1. a sludge curing agent, is characterized in that, comprises the component of following weight proportion:
The fluorite of 18~20 parts, the soda ash of 20~23 parts, the quartz sand of 7~9 parts, the gypsum of 40~50 parts, the unslaked lime of 10~12 parts, the Wingdale of 6~8 parts.
2. according to a kind of sludge curing agent described in power 1, it is characterized in that:
Described gypsum is fluorgypsum.
3. according to a kind of sludge curing agent described in power 2, it is characterized in that:
Described fluorgypsum is the industrial waste gypsum producing in fluorochemical production process.
4. according to a kind of sludge curing agent described in power 1,2 or 3, it is characterized in that:
By after contained component combined grinding, it is 300~600m that solidifying agent body is specific surface area
2/ kg's is Powdered.
5. a sludge curing agent manufacture method, is characterized in that, comprises the following steps:
(1) Fluorspar Powder of 18~20 mass parts is broken to the particle of particle diameter below 10mm;
(2) fluorite after pulverizing is mixed with the soda ash of 20~23 mass parts, the quartz sand of 7~9 mass parts, then by mixture grinding to particle diameter below 1mm;
(3) mixed powder after grinding is sent into calcining compartment calcining;
(4) fluorite, soda ash and quartz sand powder after the Wingdale of the unslaked lime of the gypsum of 40~50 mass parts, 10~12 mass parts, 6~8 mass parts and calcining are milled to predetermined state Powdered, mix.
6. according to a kind of sludge curing agent manufacture method described in power 5, it is characterized in that:
The calcining temperature of step (3) is 800~900 ℃.
7. according to a kind of sludge curing agent manufacture method described in power 5 or 6, it is characterized in that:
In step (4), by each component mixture grinding of solidifying agent to specific surface area 300~600m
2/ kg.
8. according to a kind of sludge curing agent manufacture method described in power 5 or 6, it is characterized in that:
Described gypsum is fluorgypsum.
9. according to a kind of sludge curing agent manufacture method described in power 8, it is characterized in that:
The industrial waste gypsum that described fluorgypsum produces from fluorochemical production process.