CN103613839A - Toughened basin containing regenerated high-barrier film - Google Patents
Toughened basin containing regenerated high-barrier film Download PDFInfo
- Publication number
- CN103613839A CN103613839A CN201310503784.5A CN201310503784A CN103613839A CN 103613839 A CN103613839 A CN 103613839A CN 201310503784 A CN201310503784 A CN 201310503784A CN 103613839 A CN103613839 A CN 103613839A
- Authority
- CN
- China
- Prior art keywords
- basin
- isolation film
- compound
- toughened
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a toughened basin containing regenerated high-barrier film, and relates to the technical field of chemical engineering. The toughened basin comprises following components by weight: 50-80% of polypropylene, 5-40% of polyethylene, 1-5% of a plasticizer, 5-20% of the regenerated high-barrier film, 0.1-5% of an oil-proofing agent, 0.5-1% of a brightener, 0.5-1% of a stabilizing agent and 1-4% of white carbon black. The toughened basin is simple in component, low in cost and beautiful in appearance. A portion of a regenerated material is used as a raw material, thus increasing the utilization rate of resources. A traditional production technology is changed and a refrigeration process is added, and therefore safety of products is enhanced, electricity and hardness are high and the toughened basin is unbreakable.
Description
Technical field
The present invention relates to chemical technology field, be specifically related to a kind of plastics tempering basin that contains the high-isolation film of regenerating.
Background technology
Plastic furniture is a kind of furniture of new capability.The kind of plastics is a lot, but substantially can be divided into two types: thermosetting resin and thermoplastics.Before a kind of be our common radio receiver, fascia etc.; Then as various household electrical appliances plastic components, a flexible pipe, film or card are vigorous compiles etc.In modern furniture, just this novel material is pressed into chair by model, or is pressed into various films, as the masked material of soft furniture, also have versicolor plastic hose is wound in to a soft chair on steel pipe.Plastics have the feature of easy processing, so that the moulding of this class furniture has more randomness.Random moulding gives expression to planner and has personalized mentality of designing, by the unapproachable moulding of general furniture, embodies a kind of random U.S..Compare with common furniture, plastic furniture feels to be exactly light to people's, and you do not need the strength costing a lot of money, just it can be removed and take easily, even and the inner plastic furniture that has through metal, its support is also generally hollow or diameter is very little.In addition, many plastic furnitures have function that can be folding, so not only saved space, use but also more convenient.Plastic furniture had both been applicable to public place, also can be for general family.In public places, you see maximum is exactly various chairs, and the kind that is applicable to family is countless: basin, dinner table, dining chair, locker, clothes hanger, shoe rack, flower stand.
Traditional plastic furniture formula used is comparatively single, causes product performance not produce targetedly, and the performance of some product is lower, can not meet long service requirements.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of formula simple, the tempering basin that contains the high-isolation film of regenerating of constant product quality.
Technical problem to be solved by this invention realizes by the following technical solutions:
A tempering basin that contains the high-isolation film of regenerating, is comprised of the component of following weight percent,
The optimum weight per-cent of each component is:
Another object of the present invention is to provide a kind of method of preparing the tempering basin that contains the high-isolation film of regenerating, and its step is as follows,
1) by above-mentioned weight ratio, take each component;
2) polypropylene, polyethylene, regeneration high-isolation film are placed in to stirrer, at the temperature of 80-120 ℃, stir 30 minutes, allow it mix;
3) compound mixing is placed in to refrigerating apparatus, at the temperature of-10 ℃ freezing 6 hours;
4) take out the compound after freezing, add successively white carbon black, stablizer, brightening agent, oil-proofing agent and softening agent after metering, be uniformly mixed into compound;
5) compound is placed in to conical double screw extruder hopper, extrusion plastic particle;
6) by plastic grain fusing, introduce in ready-made mould, matched moulds, injection moulding, cooling, moulding;
7) the plastics tempering basin of moulding is carried out to polishing, sterilization.
The invention has the beneficial effects as follows: component of the present invention is simple, cost is low, good looking appearance, can use partial regeneration material as raw material, improve resource utilization, simultaneously owing to having changed traditional production technique, increase freezing this link, improved the security of goods, elasticity and hardness are higher, cannot not fall brokenly.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach object and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
Embodiment 1
A tempering basin that contains the high-isolation film of regenerating, is comprised of the component of following weight percent,
Another object of the present invention is to provide a kind of method of preparing the tempering basin that contains the high-isolation film of regenerating, and its step is as follows,
1) by above-mentioned weight ratio, take each component;
2) polypropylene, polyethylene, regeneration high-isolation film are placed in to stirrer, at the temperature of 80-120 ℃, stir 30 minutes, allow it mix;
3) compound mixing is placed in to refrigerating apparatus, at the temperature of-10 ℃ freezing 6 hours;
4) take out the compound after freezing, add successively white carbon black, stablizer, brightening agent, oil-proofing agent and softening agent after metering, be uniformly mixed into compound;
5) compound is placed in to conical double screw extruder hopper, extrusion plastic particle;
6) by plastic grain fusing, introduce in ready-made mould, matched moulds, injection moulding, cooling, moulding;
7) the plastics tempering basin of moulding is carried out to polishing, sterilization.
Embodiment 2
A tempering basin that contains the high-isolation film of regenerating, is comprised of the component of following weight percent,
Another object of the present invention is to provide a kind of method of preparing the tempering basin that contains the high-isolation film of regenerating, and its step is as follows,
1) by above-mentioned weight ratio, take each component;
2) polypropylene, polyethylene, regeneration high-isolation film are placed in to stirrer, at the temperature of 80-120 ℃, stir 30 minutes, allow it mix;
3) compound mixing is placed in to refrigerating apparatus, at the temperature of-10 ℃ freezing 6 hours;
4) take out the compound after freezing, add successively white carbon black, stablizer, brightening agent, oil-proofing agent and softening agent after metering, be uniformly mixed into compound;
5) compound is placed in to conical double screw extruder hopper, extrusion plastic particle;
6) by plastic grain fusing, introduce in ready-made mould, matched moulds, injection moulding, cooling, moulding;
7) the plastics tempering basin of moulding is carried out to polishing, sterilization.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and specification sheets, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. a tempering basin that contains the high-isolation film of regenerating, is characterized in that: the component by following weight percent forms,
2. a kind of tempering basin that contains the high-isolation film of regenerating according to claim 1, is characterized in that: the component by following weight percent forms,
3. prepare a technique that contains regeneration high-isolation film tempering basin described in claim 1 or 2, it is characterized in that: step is as follows,
1) by above-mentioned weight ratio, take each component;
2) polypropylene, polyethylene, regeneration high-isolation film are placed in to stirrer, at the temperature of 80-120 ℃, stir 30 minutes, allow it mix;
3) compound mixing is placed in to refrigerating apparatus, at the temperature of-10 ℃ freezing 6 hours;
4) take out the compound after freezing, add successively white carbon black, stablizer, brightening agent, oil-proofing agent and softening agent after metering, be uniformly mixed into compound;
5) compound is placed in to conical double screw extruder hopper, extrusion plastic particle;
6) by plastic grain fusing, introduce in ready-made mould, matched moulds, injection moulding, cooling, moulding;
7) the plastics tempering basin of moulding is carried out to polishing, sterilization.