CN103601962B - A kind of family life plastics kitchen cabinet - Google Patents
A kind of family life plastics kitchen cabinet Download PDFInfo
- Publication number
- CN103601962B CN103601962B CN201310502858.3A CN201310502858A CN103601962B CN 103601962 B CN103601962 B CN 103601962B CN 201310502858 A CN201310502858 A CN 201310502858A CN 103601962 B CN103601962 B CN 103601962B
- Authority
- CN
- China
- Prior art keywords
- compound
- kitchen cabinet
- component
- family life
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of family life plastics kitchen cabinet, relate to chemical technology field, be made up of the component of following weight percent, polypropylene 20-70%, polypropylene random copolymer 5-30%, glass fibre 5-20%, polyethylene 10-60%, slipproofing agent 0.1-5%, talcum powder 0.5-5%, stablizer 0.5-1%, colour batch 0.5-1%.Instant component is simple, and cost is low, and the kitchen cabinet hardness of preparation is good, outward appearance is beautiful, and planeness is good, simultaneously owing to changing traditional production technique, increase this link freezing, improve the security of goods, at a higher temperature still there is good stability.
Description
Technical field
The present invention relates to chemical technology field, be specifically related to a kind of family life plastics kitchen cabinet.
Background technology
Plastic furniture is a kind of furniture of new capability.The kind of plastics is a lot, but substantially can be divided into two types: thermosetting resin and thermoplastics.Front a kind of be our common radio receiver, fascia etc.; Then a kind of as various household electrical appliances plastic components, flexible pipe, film or the vigorous volume of card etc.In modern furniture, just this novel material is pressed into chair by model, or is pressed into various film, as the masked material of soft furniture, also have and the plastic hose of shades of colour is wound on steel pipe a soft chair.Plastics have the feature of easily processing, so make the moulding of this kind of furniture have more randomness.Random moulding gives expression to planner and has personalized mentality of designing, embodies a kind of U.S. arbitrarily by the unapproachable moulding of general furniture.Compared with common furniture, plastic furniture feels to be exactly light to people, and you do not need the strength costed a lot of money, and just it can be removed easily and take, even and inside have the plastic furniture of through metal, its support is also generally hollow or diameter is very little.In addition, many plastic furnitures have the function that can fold, so not only saved space, to use but also more convenient.Plastic furniture was both applicable to public place, also may be used for general family.In public places, you see that maximum is exactly various chairs, and the kind being applicable to family is then countless: dinner table, dining chair, locker, clothes hanger, shoe rack, flower stand.
Traditional plastic furniture formula used is comparatively single, and cause product performance not produce targetedly, the performance of some product is lower, can not meet long service requirements.
Summary of the invention
It is simple that technical problem to be solved by this invention is to provide a kind of formula, the family life plastics kitchen cabinet of constant product quality.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of family life plastics kitchen cabinet, is made up of the component of following weight percent,
The optimum weight per-cent of each component is:
Another object of the present invention is to provide a kind of method preparing family life plastics kitchen cabinet, and its step is as follows,
1) each component is taken by above-mentioned weight ratio;
2) polypropylene, polypropylene random copolymer, glass fibre are placed in stirrer, stir 30 minutes at the temperature of 80-120 DEG C, allow it mix;
3) compound mixed is placed in refrigerating apparatus, at the temperature of-10 DEG C freezing 6 hours;
4) take out freezing after compound, add the polyethylene after metering, slipproofing agent, talcum powder, stablizer and colour batch successively, be uniformly mixed into compound;
5) compound is placed in conical double screw extruder hopper, extrusion plastic particle;
6) plastic grain is melted, introduce in ready-made mould, matched moulds, injection moulding, cooling, shaping.
The invention has the beneficial effects as follows: instant component is simple, cost is low, the kitchen cabinet hardness of preparation is good, outward appearance is beautiful, planeness is good, simultaneously owing to changing traditional production technique, increases this link freezing, improve the security of goods, at a higher temperature still there is good stability.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of family life plastics kitchen cabinet, is made up of the component of following weight percent,
Another object of the present invention is to provide a kind of method preparing family life plastics kitchen cabinet, and its step is as follows,
1) each component is taken by above-mentioned weight ratio;
2) polypropylene, polypropylene random copolymer, glass fibre are placed in stirrer, stir 30 minutes at the temperature of 80-120 DEG C, allow it mix;
3) compound mixed is placed in refrigerating apparatus, at the temperature of-10 DEG C freezing 6 hours;
4) take out freezing after compound, add the polyethylene after metering, slipproofing agent, talcum powder, stablizer and colour batch successively, be uniformly mixed into compound;
5) compound is placed in conical double screw extruder hopper, extrusion plastic particle;
6) plastic grain is melted, introduce in ready-made mould, matched moulds, injection moulding, cooling, shaping.
Embodiment 2
A kind of family life plastics kitchen cabinet, is made up of the component of following weight percent,
Another object of the present invention is to provide a kind of method preparing family life plastics kitchen cabinet, and its step is as follows,
1) each component is taken by above-mentioned weight ratio;
2) polypropylene, polypropylene random copolymer, glass fibre are placed in stirrer, stir 30 minutes at the temperature of 80-120 DEG C, allow it mix;
3) compound mixed is placed in refrigerating apparatus, at the temperature of-10 DEG C freezing 6 hours;
4) take out freezing after compound, add the polyethylene after metering, slipproofing agent, talcum powder, stablizer and colour batch successively, be uniformly mixed into compound;
5) compound is placed in conical double screw extruder hopper, extrusion plastic particle;
6) plastic grain is melted, introduce in ready-made mould, matched moulds, injection moulding, cooling, shaping.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. a family life plastics kitchen cabinet, is characterized in that: be made up of the component of following weight percent:
Preparation method is as follows:
1) each component is taken by above-mentioned weight ratio;
2) polypropylene, polypropylene random copolymer, glass fibre are placed in stirrer, stir 30 minutes at the temperature of 80-120 DEG C, allow it mix;
3) compound mixed is placed in refrigerating apparatus, at the temperature of-10 DEG C freezing 6 hours;
4) take out freezing after compound, add the polyethylene after metering, slipproofing agent, talcum powder, stablizer and colour batch successively, be uniformly mixed into compound;
5) compound is placed in conical double screw extruder hopper, extrusion plastic particle;
6) plastic grain is melted, introduce in ready-made mould, matched moulds, injection moulding, cooling, shaping.