CN103612435A - Metal ink material and preparation method thereof - Google Patents
Metal ink material and preparation method thereof Download PDFInfo
- Publication number
- CN103612435A CN103612435A CN201310617028.5A CN201310617028A CN103612435A CN 103612435 A CN103612435 A CN 103612435A CN 201310617028 A CN201310617028 A CN 201310617028A CN 103612435 A CN103612435 A CN 103612435A
- Authority
- CN
- China
- Prior art keywords
- ink
- metal
- coating
- metal base
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a metal ink material which comprises a metal base material and an ink coating uniformly coated on the foil surface of the metal base material, wherein the thickness of the metal base material is not less than 0.007mm, the thickness of the ink coating is 0.005-0.025mm, the ink in the ink coating is offset high-gloss resin ink or offset rotary ink, and the metal base material is a metal coiled material or a metal alloy coiled material. The invention also discloses a preparation method of the metal ink material, which comprises the steps of ink mixing, coating and drying. The metal ink material disclosed by the invention is simple in structure and convenient and quick to process and is not restricted by the specification of the metal base material; the ink is coated on the metal base material in a spreading manner to obtain products with different specifications and different properties; the product has high surface smoothness and gloss.
Description
Technical field
The present invention relates to a kind of metal ink material, be specially a kind of metal ink material and preparation method thereof.
Background technology
As everyone knows, ink is that the mode spraying by printing depends on metallic substrate surface in industrial major part at present, although above-mentioned processing mode efficiency is high, its shower nozzle adopting is small and dense, and shower nozzle is easy to blocking, causes product quality not pass a test; Printing spray nozzle mode is subject to metal base size restrictions simultaneously, can not produce larger longer coiled material.
Summary of the invention
Technical problem solved by the invention is to provide a kind of metal ink material and preparation method thereof, to solve the problem proposing in above-mentioned background technology.
Technical problem solved by the invention realizes by the following technical solutions:
A metal ink material, comprises metal base and the ink coating of even blade coating on metal base paper tinsel face, and the thickness of described metal base is not less than 0.007mm, and the thickness of described ink coating is 0.005～0.025mm.
A kind of optimization as above technical scheme; Ink in described ink coating is offset printing light resin ink or offset rotary ink.
A kind of optimization as above technical scheme; Described metal base is metal coiled material or metal alloy coiled material.
The preparation method who prepares metal ink material described in above-mentioned arbitrary technical scheme, comprises the following steps:
(1) allotment ink; In the gluey fluid of 60～85wt% ink, add 20～30wt% diluent, 5～15wt% auxiliary agent, after stirring, form the gluey fluid of ink for the treatment of blade coating;
(2) coating; The gluey fluid of the ink for the treatment of blade coating in step (1) is added in coating machine, utilize coating machine to scrape the gluey fluid of inking at metal base paper tinsel face, the high temperature oven that utilizes coating machine is dried the gluey fluid of ink, it is attached to and on metal base, forms ink coating;
(3) dry: will in step (2), with the metal base of ink coating, be placed in constant-temperature house 3～7 days, treat that it dries the overcuring phase, obtain metal ink material.
A kind of optimization as above technical scheme; Auxiliary agent in step (1) is the one or more combination in curing agent, delustering agent, drying retardant, antifriction liniment, drier.
A kind of optimization as above technical scheme; Temperature in step (3) in constant-temperature house is 30～80 ℃.
The present invention compared with prior art, has the following advantages:
The present invention is simple in structure, easy to process quick, is not subject to the specification limits of metal base, utilizes the mode of coating on metal base, to scrape inking, makes the product of different size, different performance; Product surface smoothness and glossiness are high.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
The specific embodiment
In order to make of the present inventionly to realize technological means, creation characteristic, reach object and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
As shown in Figure 1, a kind of metal ink material, comprises metal base 2 and the ink coating 1 of even blade coating on metal base 2 paper tinsel faces, and the thickness of described metal base 2 is not less than 0.007mm, and the thickness of described ink coating 1 is 0.005～0.025mm.
In the present invention, the ink in described ink coating 1 is offset printing light resin ink or offset rotary ink.Described metal base 2 is metal coiled material or metal alloy coiled material.
The preparation method of above-mentioned metal ink material, comprises the following steps:
(1) allotment ink; In the gluey fluid of 60wt% ink, add 20wt% diluent, 5wt% auxiliary agent, after stirring, form the gluey fluid of ink for the treatment of blade coating;
(2) coating; The gluey fluid of the ink for the treatment of blade coating in step (1) is added in coating machine, utilize coating machine to scrape the gluey fluid of inking at metal base paper tinsel face, the high temperature oven that utilizes coating machine is dried the gluey fluid of ink, it is attached to and on metal base, forms ink coating;
(3) dry: will in step (2), with the metal base of ink coating, be placed in constant-temperature house 3～7 days, treat that it dries the overcuring phase, obtain metal ink material.
Embodiment 2
The preparation method of above-mentioned metal ink material, comprises the following steps:
(1) allotment ink; In the gluey fluid of 85wt% ink, add 30wt% diluent, 15wt% auxiliary agent, after stirring, form the gluey fluid of ink for the treatment of blade coating;
(2) coating; The gluey fluid of the ink for the treatment of blade coating in step (1) is added in coating machine, utilize coating machine to scrape the gluey fluid of inking at metal base paper tinsel face, the high temperature oven that utilizes coating machine is dried the gluey fluid of ink, it is attached to and on metal base, forms ink coating;
(3) dry: will in step (2), with the metal base of ink coating, be placed in constant-temperature house 3～7 days, treat that it dries the overcuring phase, obtain metal ink material.
Embodiment 3
The preparation method of above-mentioned metal ink material, comprises the following steps:
(1) allotment ink; In the gluey fluid of 73wt% ink, add 25wt% diluent, 10wt% auxiliary agent, after stirring, form the gluey fluid of ink for the treatment of blade coating;
(2) coating; The gluey fluid of the ink for the treatment of blade coating in step (1) is added in coating machine, utilize coating machine to scrape the gluey fluid of inking at metal base paper tinsel face, the high temperature oven that utilizes coating machine is dried the gluey fluid of ink, it is attached to and on metal base, forms ink coating;
(3) dry: will in step (2), with the metal base of ink coating, be placed in constant-temperature house 3～7 days, treat that it dries the overcuring phase, obtain metal ink material.
More than show and described basic principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and description, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (6)
1. a metal ink material, is characterized in that: comprise metal base and the ink coating of even blade coating on metal base paper tinsel face, the thickness of described metal base is not less than 0.007mm, and the thickness of described ink coating is 0.005～0.025mm.
2. metal ink material according to claim 1, is characterized in that: the ink in described ink coating is offset printing light resin ink or offset rotary ink.
3. metal ink material according to claim 1, is characterized in that: described metal base is metal coiled material or metal alloy coiled material.
4. the preparation method of metal ink material as described in claim as arbitrary in claims 1 to 3, is characterized in that: comprise the following steps:
(1) allotment ink; In the gluey fluid of 60～85wt% ink, add 20～30wt% diluent, 5～15wt% auxiliary agent, after stirring, form the gluey fluid of ink for the treatment of blade coating;
(2) coating; The gluey fluid of the ink for the treatment of blade coating in step (1) is added in coating machine, utilize coating machine to scrape the gluey fluid of inking at metal base paper tinsel face, the high temperature oven that utilizes coating machine is dried the gluey fluid of ink, it is attached to and on metal base, forms ink coating;
(3) dry: will in step (2), with the metal base of ink coating, be placed in constant-temperature house 3～7 days, treat that it dries the overcuring phase, obtain metal ink material.
5. preparation method according to claim 4, is characterized in that: the auxiliary agent in step (1) is the one or more combination in curing agent, delustering agent, drying retardant, antifriction liniment, drier.
6. preparation method according to claim 4, is characterized in that: the temperature in step (3) in constant-temperature house is 30～80 ℃.