CN103588584A - 一种用于生产粒状硫酸铵的粘合剂 - Google Patents
一种用于生产粒状硫酸铵的粘合剂 Download PDFInfo
- Publication number
- CN103588584A CN103588584A CN201310614637.5A CN201310614637A CN103588584A CN 103588584 A CN103588584 A CN 103588584A CN 201310614637 A CN201310614637 A CN 201310614637A CN 103588584 A CN103588584 A CN 103588584A
- Authority
- CN
- China
- Prior art keywords
- ammonium sulfate
- tackiness agent
- granular ammonium
- calcium carbonate
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于生产粒状硫酸铵的粘合剂,粘合剂的主要成分是:硫酸铝、碳酸钙、磷酸一铵;粘合剂的各成分的质量百分数:碳酸钙10%~15%,硫酸铝70%~75%,磷酸一铵5%~10%;上述粘合剂在用于生产粒状硫酸铵;本发明提供的方法有以下优点:(1)使用新型粘合剂生产出来的粒状硫酸铵产品,在保证产品内外观质量的前提下,氮含量确保在19.5%以上,吨产品成本下降100元,经济效益显著;(2)本发明生产方法采用的装置及流程均为现有成熟的流程,改动较小,降低了投资的风险。<sup/>
Description
技术领域
本发明涉及粘合剂领域,具体涉及一种用于生产粒状硫酸铵的粘合剂。
背景技术
硫酸铵是广泛用于化工、染织、医药、皮革等行业的工业原料。晶体硫酸铵作为肥料在使用过程中存在许多缺点:易结块、流动性差,难以实现机械化施肥,在施用过程中易形成粉尘而流失。 粒状硫酸铵物理性能好,装卸时不起尘,长期存放不易结块、流动性好,施肥时易撒布,并可实现飞机播肥、减少损失,同时还可起到缓释作用,提高肥料的利用率,越来越受到市场尤其是国外市场的欢迎。
瓮福(集团)有限责任公司下属瓮福磷肥厂与2009年研发出了粒状硫酸铵造粒新工艺,填补了国内相关技术的一项空白。长期以来瓮福集团生产的粒状硫酸铵产品含氮量≧19.5,吨产品粘合剂成本约为150元,经过瓮福磷肥厂相关技术、生产人员的努力,开发出一种新型粘合剂,在保证粒状硫酸铵产品内外观质量的前提下,吨产品粘合剂成本下降到50元,每吨产品节约100元,创造了良好的经济效益。
发明内容
本发明的目的是基于市场需求提供一种新型粒状硫酸铵生产使用粘合剂。在保证产品内外观质量的同时使得粒状硫酸铵产品吨成本下降100元/吨。
本发明一种用于生产粒状硫酸铵的粘合剂,其粘合剂的主要成分是:硫酸铝、碳酸钙、磷酸一铵;粘合剂的各成分的质量百分数:碳酸钙10%~15%,硫酸铝70%~75%,磷酸一铵 5%~10%。
上述粘合剂在用于生产粒状硫酸铵产品时,硫酸铵料浆与粘合剂的有效配比为见下表
粒状硫酸铵制浆配比表:
序号 | 名称 | 规格 | 折纯量 (kg) |
1 | 粘合剂 | 混合物 | 50 |
2 | 硫酸铵料浆 | 20.7-0-22.3 | 1000 |
合计 | 1050 |
该粘合剂有效的利用物料的粘度和反应热来提高产品的成球率,正常生产时不需要使用蒸汽或水来帮助造粒,降低了烘干强度,可以降低成本、提高产量、减低煤耗,同时可根据市场的需要解决有效养分均匀配料问题。
上述粘合剂在使用时,上游装置生产的硫酸铵料浆与粘合剂按一定比例混合,送入造粒/干燥机喷浆造粒,半成品经破碎、筛分、洗涤后得到合格的2mm-4mm产品颗粒,根据需要添加着色剂、包裹剂得到粒状硫酸铵产品。
上述方法中,所述制取粒状硫酸铵产品使用的原料为磷石膏制硫酸铵生产的硫酸铵溶液,密度:1.24 g/ml -1.26g/ml,含水率:50%~58% N含量:20.5%-21.0%;新型粘合剂中硫酸铝为通常工业硫酸铝,磷酸一铵为通常肥料级磷酸一铵,碳酸钙为上游装置副产品(碳酸钙含量:60%;水分含量:15%-20%)。
本发明提供的方法有以下优点:
(1)使用新型粘合剂生产出来的粒状硫酸铵产品,在保证产品内外观质量的前提下,氮含量确保在19.5%以上,吨产品成本下降100元,经济效益显著;
(2)本专利生产方法采用的装置及流程均为现有成熟的流程,改动较小,降低了投资的风险。
具体实施方式
实施在一个带搅拌器的混配槽中,同时加入硫酸铵料浆及粘合剂,硫酸铵料浆的密度1.24 g/ml-1.26g/ml,进入混配槽的硫酸铵料浆及粘合剂进行精确配比计量。初步混合后的料浆泵送至料浆循环***进一步混合,适当加温将料浆温度升至85℃-100℃。制备好的料浆送入造粒/干燥机喷浆造粒并干燥,干燥的热源采用燃煤沸腾炉产生的约550℃-600℃的高温烟道气。高温气体对喷浆料浆并流干燥,干燥后得到的半成品通过斗提机送到半成品筛进行筛分,经筛分后,2mm-4mm颗粒进入冷却筒冷却和包裹得到产品,>4mm颗粒经破碎机破碎后与筛分出来的的1mm-2mm颗粒作为返料返回造粒/干燥机。干燥后的尾气通过尾气风机经旋风降尘送入文丘里洗涤器洗涤除尘,除尘达标的气体通过排气筒排空。
瓮福(集团)有限责任公司瓮福磷肥厂使用本发明方法,利用一套200kt/a粒状一铵装置将磷石膏制硫酸铵生产的硫酸铵料浆与磷铵料浆经配比、造粒干燥、破碎、筛分、洗涤、着色包裹后生产出粒状硫酸铵,目前已形成100kt/a的粒状硫酸铵产品生产能力。
【相关数据】
1.粒状硫酸铵制浆配比表:
序号 | 名称 | 规格 | 折纯量 (kg) |
1 | 粘合剂 | 混合物 | 50 |
2 | 硫酸铵料浆 | 20.7-0-22.3 | 1000 |
合计 | 1050 |
2.使用粘合剂后的产品数据
2013年6月21日-28日生产的粒状硫酸铵产品情况:
平均含氮量(数学加权平均值):20.53%
生产日期 | 班次 | 数量 | 总氮 |
2013-6-28 | 白 | 233.5 | 19.86 |
2013-6-28 | 夜 | 183 | 21.18 |
2013-6-27 | 白 | 177 | 20.03 |
2013-6-27 | 夜 | 208.5 | 19.82 |
2013-6-26 | 白 | 186 | 19.59 |
2013-6-26 | 夜 | 179 | 19.54 |
2013-6-25 | 白 | 194 | 19.57 |
2013-6-25 | 夜 | 116 | 19.48 |
2013-6-24 | 白 | 181 | 20.22 |
2013-6-24 | 夜 | 191.5 | 20.04 |
2013-6-23 | 白 | 156 | 19.5 |
2013-6-23 | 夜 | 180 | 19.88 |
2013-6-22 | 白 | 196 | 19.72 |
2013-6-22 | 夜 | 158 | 19.97 |
2013-6-21 | 白 | 169.5 | 19.67 |
2013-6-21 | 夜 | 176 | 19.76 |
总产量 | 2885 | ||
平均含氮量 | 19.86 |
Claims (2)
1. 一种用于生产粒状硫酸铵的粘合剂,其特征是粘合剂的主要成分是:硫酸铝、碳酸钙、磷酸一铵;粘合剂的各成分的质量百分数:碳酸钙10%~15%,硫酸铝70%~75%,磷酸一铵 5%~10%;上述粘合剂在用于生产粒状硫酸铵产品时,硫酸铵料浆与粘合剂的有效配比见下 :
粒状硫酸铵制浆配比:
上述粘合剂在使用时,上游装置生产的硫酸铵料浆与粘合剂按一定比例混合,送入造粒/干燥机喷浆造粒,半成品经破碎、筛分、洗涤后得到合格的2mm-4mm产品颗粒,根据需要添加着色剂、包裹剂得到粒状硫酸铵产品。
2.根据权利要求1所述一种用于生产粒状硫酸铵的粘合剂,其特征是制取粒状硫酸铵产品使用的原料为磷石膏制硫酸铵生产的硫酸铵溶液,密度:1.24 g/ml -1.26g/ml,含水率:50%~58% N含量:20.5%-21.0%;粘合剂中硫酸铝为通常工业硫酸铝,磷酸一铵为通常肥料级磷酸一铵,碳酸钙为上游装置副产品其中碳酸钙含量:60%;水分含量:15%-20%。