CN103571126A - 洗衣机排水管用低温吹塑tpe材料 - Google Patents
洗衣机排水管用低温吹塑tpe材料 Download PDFInfo
- Publication number
- CN103571126A CN103571126A CN201210278687.6A CN201210278687A CN103571126A CN 103571126 A CN103571126 A CN 103571126A CN 201210278687 A CN201210278687 A CN 201210278687A CN 103571126 A CN103571126 A CN 103571126A
- Authority
- CN
- China
- Prior art keywords
- district
- washing machine
- low
- molding
- white oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于聚合物改性材料生产加工技术领域,具体涉及一种用于挤出成型的洗衣机排水管用低温吹塑TPE材料。其特征是由以下组分按重量份组成:SEBS100-200、白油50-100、聚乙烯100-140、稳定剂0.2-0.4;其中,所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物;所述白油为石腊油或环烷油或二者的混合物。因而具有可低温挤出吹塑成型,回弹性好,强度高,环保,可重复利用的优点。
Description
技术领域:本发明属于聚合物改性材料生产加工技术领域,具体涉及一种用于挤出成型的洗衣机排水管用低温吹塑TPE材料。
背景技术:目前,洗衣机排水管大都采用挤出吹塑成型工艺生产,一般采用的材质有PVC、EVA等。但是PVC材料因为环保方面的问题已经逐步被淘汰,现在市场上大多数都是EVA吹塑的产品,但EVA产品弹性差,气味大,使其应用受到限制。
发明内容:本发明的目的是提供一种可低温挤出吹塑成型,回弹性好,强度高,环保,可重复利用的洗衣机排水管用低温吹塑TPE材料。
本发明的技术方案是:一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS100-200、白油50-100、聚乙烯100-140、稳定剂0.2-0.4;其中,所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物;所述白油为石腊油或环烷油或二者的混合物。
其加工方法为:在50-80℃的条件下,先将白油和SEBS在搅拌机内慢速混合20-30分钟后,再与其他的原料助剂一起混合10-20分钟,然后加入双螺杆挤出机中,经熔融挤出、冷却、造粒、包装成品即可。其中双螺杆挤出机的螺筒内温度为:一区170-180℃,二区180-190℃,三区180-190℃,四区180-190℃,五区180-190℃,六区180-190℃,七区180-190℃,八区180-190℃,机头180-190℃,双螺杆挤出机转速为100-400转/分。
本发明最佳的技术方案是:一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS150、白油75、聚乙烯120、稳定剂0.3;其中,所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物;所述白油为石腊油或环烷油或二者的混合物。
其加工方法为:在50℃-80℃的条件下,先将白油和SEBS在搅拌机内慢速混合20-30分钟后,再与其他的原料助剂一起混合10-20分钟,然后加入双螺杆挤出机中,经熔融挤出、冷却、造粒、包装成品即可。其中双螺杆挤出机的螺筒内温度为:一区170-180℃,二区180-190℃,三区180-190℃,四区180-190℃,五区180-190℃,六区180-190℃,七区180-190℃,八区180-190℃,机头180-190℃,双螺杆挤出机转速为100-400转/分。
本发明的有益效果:在材料SEBS中,加入了白油和聚乙烯,使之形成了互穿网络结构的新材料,改善了材料的熔体性能,提高了材料的熔体强度,使其可低温挤出吹塑成型,改性后的材料同时具有回弹性好,强度高,环保,可重复利用的优点。
具体实施方式:以下结合具体实施例来进一步说明本发明的技术方案。
实施例1:一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS100、白油100、聚乙烯140、稳定剂0.2;其中,所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物;所述白油为石腊油或环烷油或二者的混合物。
其加工方法为:在50℃-80℃的条件下,先将白油和SEBS在搅拌机内慢速混合20-30分钟后,再与其他的原料助剂一起混合10-20分钟,然后加入双螺杆挤出机中,经熔融挤出、冷却、造粒、包装成品即可。其中双螺杆挤出机的螺筒内温度为:一区170-180℃,二区180-190℃,三区180-190℃,四区180-190℃,五区180-190℃,六区180-190℃,七区180-190℃,八区180-190℃,机头180-190℃,双螺杆挤出机转速为100-400转/分。
实施例2:一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS200、白油50、聚乙烯100、稳定剂0.4;其中,所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物;所述白油为石腊油或环烷油或二者的混合物。
其加工方法为:在50℃-80℃的条件下,先将白油和SEBS在搅拌机内慢速混合20-30分钟后,再与其他的原料助剂一起混合10-20分钟,然后加入双螺杆挤出机中,经熔融挤出、冷却、造粒、包装成品即可。其中双螺杆挤出机的螺筒内温度为:一区170-180℃,二区180-190℃,三区180-190℃,四区180-190℃,五区180-190℃,六区180-190℃,七区180-190℃,八区180-190℃,机头180-190℃,双螺杆挤出机转速为100-400转/分。
实施例3:一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS150、白油75、聚乙烯120、稳定剂0.3;其中,所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物;所述白油为石腊油或环烷油或二者的混合物。
其加工方法为:在50℃-80℃的条件下,先将白油和SEBS在搅拌机内慢速混合20-30分钟后,再与其他的原料助剂一起混合10-20分钟,然后加入双螺杆挤出机中,经熔融挤出、冷却、造粒、包装成品即可。其中双螺杆挤出机的螺筒内温度为:一区170-180℃,二区180-190℃,三区180-190℃,四区180-190℃,五区180-190℃,六区180-190℃,七区180-190℃,八区180-190℃,机头180-190℃,双螺杆挤出机转速为100-400转/分。
Claims (4)
1.一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS100-200、白油50-100、聚乙烯100-140、稳定剂0.2-0.4。
2.按权利要求1所述的一种洗衣机排水管用低温吹塑TPE材料,其特征是由以下组分按重量份组成:SEBS150、白油75、聚乙烯120、稳定剂0.3。
3.按权利要求1或2所述的一种洗衣机排水管用低温吹塑TPE材料,其特征是:所述的稳定剂是主抗氧剂1010和辅助抗氧剂168 1∶1的混合物。
4.按权利要求1或2所述的一种洗衣机排水管用低温吹塑TPE材料,其特征是:所述白油为石腊油或环烷油或二者的混合物。