Summary of the invention
The present invention provides homogeneous composite fire-proof lagging material for a kind of building heat preservation for solving the technical problem existing in known technology.
The object of this invention is to provide a kind of technique succinct, production efficiency is high, composite inorganic material, and lightweight, fire-protection rating are high, high insulating effect, good mechanical property, for building homogeneous composite fire-proof lagging material of the feature such as applied widely.
The present invention's homogeneous composite fire-proof lagging material for building, adopt the compound pressing technology of heating of tinuous production, with fire retardant, silicon-dioxide, nonflammable polymkeric substance (according to the mass ratio of 3-5: 5-7: 85-90) makes through modification can foamable polymer glue, the setting accelerator that adds reactant total mass 16%-18%, under high speed homogenization reaction conditions, again with structural similitude, and process KH type silane coupling agent carries out the glass microballon of interface processing, silicon ash, laminated clay, the mixed inorganic materials of enhanced fiber (according to the mass ratio of 85-90: 5-8: 8-10: 2-5), mix continuously homogeneous compound, then heat, pressurization, solidify, moulding, again through normal temperature slaking in 24 hours, seasoning in 48 hours, make homogeneous composite inorganic lightweight fireproof insulating material.
The technical scheme that the present invention's homogeneous composite fire-proof lagging material for building is taked is:
A kind of homogeneous composite fire-proof lagging material for building, be characterized in: homogeneous composite fire-proof lagging material, comprise by add fire retardant and aerosil strengthen fire-retardant can foamable polymer glue, the composition such as glass microballon, silicon ash ultra-fine micropowder, nano lamellar clay and multiple fiber.Be add fire retardant, aerosil strengthen fire-retardant can foamable polymer glue, with the glass microballon of processing through silane coupling agent, silicon ash ultra-fine micropowder, nano lamellar clay and fiber, through pre-mixing, compound, the dry slaking of homogeneous, make this homogeneous composite fire-proof lagging material.
The present invention's homogeneous composite fire-proof lagging material for building can also adopt following technical scheme:
Described homogeneous composite fire-proof lagging material, is characterized in that: fire-retardant type need add after the setting accelerator initial set of total mass 16%-18% heating, cure under pressure, drying and moulding after can foamable polymer glue making.
Described for building homogeneous composite fire-proof lagging material, is characterized in that: component one: fire retardant, aerosil, mass ratio that can foamable polymer are 3-5: 5-7: 85-90.Component two: the mass ratio of glass microballon, silicon ash ultrafine powder, laminated clay, fiber is 85-90: 5-8: 8-10: 2-5.
Described for building homogeneous composite fire-proof lagging material, is characterized in that: silicon ash ultra-fine micropowder is light silica ash ultra-fine micropowder.Silicon-dioxide is ultra-fine aerogel type silicon-dioxide.Book clay is that nano level is through expanding the processing book clay of layer and surface silicon alkanisation.
Described for building homogeneous composite fire-proof lagging material, is characterized in that: silane coupling agent is KH550, KH570, KH720 type silane coupling agent, and wherein one or more are used simultaneously.
Described for building homogeneous composite fire-proof lagging material, is characterized in that: the thickness of homogeneous composite fire-proof lagging material is for being 20 millimeters~150 millimeters.
Advantage and positively effect that the present invention has are:
This homogeneous composite fire-proof lagging material, for aspects such as building heat preservation products, owing to having adopted the brand-new technical scheme of the present invention, is compared with prior art products, and the present invention has following evident characteristic:
1, belong to homogeneous composite inorganic, lightweight outer wall fireproof heat-preservation material, fire-protection rating reaches: GB8624-2006 standard: A grade standard.
2, its heat insulation effect reaches, and national standardization Technical Committee is to material of construction, other requirement of adiabatic level.
3, the manufacture of this product application continuous homogenizing complex machining process forms, and has shortened the production cycle, has improved productivity and economic benefit.
4, glass microballon used, silicon ash ultrafine powder powder, aerosil, enhanced fiber, nano lamellar clay etc. have strengthened the physicalies such as fireproof heat insulating of whole material, guarantee that the insulation of this lagging material takes into account security feature.
Embodiment
For further understanding summary of the invention of the present invention, Characteristic, hereby exemplify following examples, and coordinate accompanying drawing to be described in detail as follows:
With reference to accompanying drawing 1.
Embodiment 1
A kind of homogeneous composite fire-proof lagging material for building, comprise that fire-retardant type can foamable polymer glue, glass microballon, aerosil, silicon ash ultra-fine micropowder, nano lamellar clay and fortifying fibre composition, by flame-proof type polyalcohol containing silicone resin, glass microsphere, ultra-fine micropowder mixing makes the mineral rubber that can foam, the solidifying agent that adds total mass 16-18%, with the glass microballon of processing through KH type silane coupling agent mixed interface, silicon ash ultrafine powder, nano lamellar clay, after fortifying fibres etc. mix, homogeneous is compound, dry slaking, obtain thickness for being 20 millimeters~150 millimeters homogeneous composite fire-proof lagging materials for building.
Wherein, nonflammable can foamable polymer, the mass ratio of fire retardant, aerosil is, 85-90: 3-5: 5-7; The mass ratio of glass microballon, silicon ash ultrafine powder, nano lamellar clay, fortifying fibre is 90: 5-7: 3-5: 2-3.
The preparation process of the present embodiment homogeneous composite fire-proof lagging material for building:
Adopt YSL-11 type automatic serial production line, coordinate the complex machining process of homogeneous lagging material, use take nonflammable can foamable polymer, (mass ratio is, 85-90: 3-5: 5-7) for fire retardant, aerosil; Not firing that modification makes under certain temperature condition can foamable polymer glue.Gained glue adds the setting accelerator high speed homogenization reaction of reactant total mass 16%-18%, then the inorganic lightweight material such as the compound glass microballon through KH coupling agent interface processing, silicon ash ultrafine powder, nano lamellar clay, enhanced fiber (pressing the mass ratio of 85-90: 5-7: 3-5: 2-3).At heat through production line pressurization, dryness finalization, make the homogeneous fire-retardant heat-insulation material of homogeneous compound, light fire-proof, after the normal temperature maturing process of 48 hours, carry out specification and cut out, pack again, making thickness is the homogeneous composite fire-proof lagging material between 20 millimeters~150 millimeters.