CN103132620B - Integrated closed-cell perlite insulation board - Google Patents
Integrated closed-cell perlite insulation board Download PDFInfo
- Publication number
- CN103132620B CN103132620B CN201310072615.0A CN201310072615A CN103132620B CN 103132620 B CN103132620 B CN 103132620B CN 201310072615 A CN201310072615 A CN 201310072615A CN 103132620 B CN103132620 B CN 103132620B
- Authority
- CN
- China
- Prior art keywords
- parts
- side fascia
- raw material
- perlite
- pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
An integrated closed-cell perlite insulation board is composed of an outer wallboard and a perlite layer according to the mass ratio of 100:1. The insulation board is manufactured by coating fluorocarbon paint on the manufactured outer wallboard, then coating bi-component polyurethane sealant on the outer wallboard, adhering the perlite on the outer wallboard, and pressing the perlite and the outer wallboard together through a pressing machine with 25Mpa pressure. Further, after being fused at the temperature of 80-100 DEG C, the insulation board is conveyed into a microwave drying channel 30 meters long through a conveying belt, and is finished. The integrated closed-cell perlite insulation board has functions of heat insulation and fire proofing and is safer to use, more convenient to mount, low in manufacturing cost and attractive in appearance and can be colorful, and the service life is greatly prolonged to more than 25 years.
Description
Technical field
The present invention relates to building material field, specifically relate to a kind of closed perlite integrated heat-preservation hanging plate.
Background technology
the material such as warming plate many employings EPS plate, ASPS plate of current skin is made, though this kind of material can play insulation effect, but because it is all lipid materials, burning-point is low, can not play fireproofing function, fire spreading can be accelerated when building breaking out of fire, safety factor is not high, and this kind of materials'use life-span is not high, slag-off phenomenon of generally fading after exterior wall arranges 3-5 years, its construction technology relative complex made, cost is high.
Summary of the invention
The object of the invention is to the deficiency overcoming above-mentioned technology, provide one can fireproof warming plate, and long service life, cost of manufacture is cheap.
For achieving the above object, the technical solution used in the present invention is: a kind of closed perlite integrated heat-preservation hanging plate, and it is made up of according to the combination of 100:1 mass ratio side fascia and pearl rock stratum, and described side fascia is made up of the raw material of following weight portion: pvc 200 ~ 300 parts, calcium powder 700 ~ 800 parts, stearic acid 5 ~ 8 parts, dibutyl ester 3 ~ 7 parts, CPE30 ~ 40 part, 3 ~ 7 parts, pe wax, pvc stabilizing agent 33 ~ 37 parts, AC blowing agent 9 ~ 11 parts, PVC foam conditioning agent 20 ~ 30 parts; Described pearl rock stratum is made up of the raw material of following weight portion: bead 120 ~ 180 parts, hydrophober 2.1 ~ 2.6 parts, water glass 90 ~ 110 parts, silicon phosphate 6 ~ 10 parts, calcium bicarbonate 22 ~ 26 parts, 95 ~ 105 parts, water, polypropylene 0.4 ~ 0.6 part, hydroxypropyl methylcellulose 1.2 ~ 1.8 parts.
The manufacture craft of described side fascia above-mentioned side fascia raw material components is taken raw material mix, and the temperature that controls environment makes the softening mixing of raw material at 185 ~ 220 degrees Celsius, to be expressed in condensation mould by raw material to carry out cooling forming and get final product by extruding machine.
Described a kind of closed perlite integrated heat-preservation hanging plate manufacture craft is: on the side fascia made, coat F-C paint, and then on side fascia, coat dual-component polyurethane fluid sealant, perlite is bonded on side fascia, and perlite and side fascia to be forced together composition warming plate by press 25Mpa pressure, and fuse through 80-100 degree celsius temperature, then the microwave drying passage that warming plate is delivered into 30 meters long by conveyer belt is dried, to obtain final product.
The raw material components of the better weight portion of side fascia of the present invention is: pvc 250 parts, calcium powder 750 parts, stearic acid 7 parts, dibutyl ester 5 parts, CPE35 part, 5 parts, pe wax, pvc stabilizing agent 35 parts, AC blowing agent 10 parts, PVC foam conditioning agent 25 parts;
The raw material components of the better weight portion of pearl rock stratum of the present invention is: bead 150 parts, hydrophober 2.4 parts, water glass 100 parts, silicon phosphate 8 parts, calcium bicarbonate 24 parts, 100 parts, water, polypropylene 0.5 part, hydroxypropyl methylcellulose 1.5 parts.
Beneficial effect of the present invention is: while insulation, also have fire-proof function, use safer, and greatly increase application life, can reach more than 25 years, easier for installation, and cost of manufacture is low, good looking appearance, can make shades of colour.
Detailed description of the invention
Below in conjunction with embodiment, the present invention will be further described.
Embodiment 1
A kind of closed perlite integrated heat-preservation hanging plate, it is made up of according to the combination of 100:1 mass ratio side fascia and pearl rock stratum, described side fascia is made up of the raw material of following weight portion: pvc 200 parts, calcium powder 700 parts, stearic acid 5 parts, dibutyl ester 3 parts, CPE30 part, 3 parts, pe wax, pvc stabilizing agent 33 parts, AC blowing agent 9 parts, PVC foam conditioning agent 20 parts; Described pearl rock stratum is made up of the raw material of following weight portion: bead 120 parts, hydrophober 2.1 parts, water glass 90 parts, silicon phosphate 6 parts, calcium bicarbonate 22 parts, 95 parts, water, polypropylene 0.4 part, hydroxypropyl methylcellulose 1.2 parts.
The manufacture craft of described side fascia above-mentioned side fascia raw material components is taken raw material mix, and the temperature that controls environment makes the softening mixing of raw material at 185 ~ 220 degrees Celsius, to be expressed in condensation mould by raw material to carry out cooling forming and get final product by extruding machine.
Described a kind of closed perlite integrated heat-preservation hanging plate manufacture craft is: on the side fascia made, coat F-C paint, and then on side fascia, coat dual-component polyurethane fluid sealant, perlite is bonded on side fascia, and perlite and side fascia to be forced together composition warming plate by press 25Mpa pressure, and fuse through 80-100 degree celsius temperature, then the microwave drying passage that warming plate is delivered into 30 meters long by conveyer belt is dried, to obtain final product.
Embodiment 2
A kind of closed perlite integrated heat-preservation hanging plate, it is made up of according to the combination of 100:1 mass ratio side fascia and pearl rock stratum, described side fascia is made up of the raw material of following weight portion: pvc 300 parts, calcium powder 800 parts, stearic acid 8 parts, dibutyl ester 7 parts, CPE40 part, 7 parts, pe wax, pvc stabilizing agent 37 parts, AC blowing agent 11 parts, PVC foam conditioning agent 30 parts; Described pearl rock stratum is made up of the raw material of following weight portion: bead 180 parts, hydrophober 2.6 parts, water glass 110 parts, silicon phosphate 10 parts, calcium bicarbonate 26 parts, 105 parts, water, polypropylene 0.6 part, hydroxypropyl methylcellulose 1.8 parts.
Manufacture craft is with embodiment 1.
Embodiment 3
A kind of closed perlite integrated heat-preservation hanging plate, it is made up of according to the combination of 100:1 mass ratio side fascia and pearl rock stratum, described side fascia is made up of the raw material of following weight portion: pvc 250 parts, calcium powder 750 parts, stearic acid 7 parts, dibutyl ester 5 parts, CPE35 part, 5 parts, pe wax, pvc stabilizing agent 35 parts, AC blowing agent 10 parts, PVC foam conditioning agent 25 parts; Described pearl rock stratum is made up of the raw material of following weight portion: bead 150 parts, hydrophober 2.4 parts, water glass 100 parts, silicon phosphate 8 parts, calcium bicarbonate 24 parts, 100 parts, water, polypropylene 0.5 part, hydroxypropyl methylcellulose 1.5 parts.
Claims (4)
1. a closed perlite integrated heat-preservation hanging plate, it is characterized in that: it is made up of according to the combination of 100:1 mass ratio side fascia and pearl rock stratum, described side fascia is made up of the raw material of following weight portion: pvc 200 ~ 300 parts, calcium powder 700 ~ 800 parts, stearic acid 5 ~ 8 parts, dibutyl ester 3 ~ 7 parts, CPE30 ~ 40 part, 3 ~ 7 parts, pe wax, pvc stabilizing agent 33 ~ 37 parts, AC blowing agent 9 ~ 11 parts, PVC foam conditioning agent 20 ~ 30 parts; Described pearl rock stratum is made up of the raw material of following weight portion: bead 120 ~ 180 parts, hydrophober 2.1 ~ 2.6 parts, water glass 90 ~ 110 parts, silicon phosphate 6 ~ 10 parts, calcium bicarbonate 22 ~ 26 parts, 95 ~ 105 parts, water, polypropylene 0.4 ~ 0.6 part, hydroxypropyl methylcellulose 1.2 ~ 1.8 parts; The manufacture craft of described side fascia above-mentioned side fascia raw material components is taken raw material mix, and the temperature that controls environment makes the softening mixing of raw material at 185 ~ 220 degrees Celsius, to be expressed in condensation mould by raw material to carry out cooling forming and get final product by extruding machine.
2. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: described a kind of closed perlite integrated heat-preservation hanging plate manufacture craft is: on the side fascia made, coat F-C paint, and then on side fascia, coat dual-component polyurethane fluid sealant, perlite is bonded on side fascia, and perlite and side fascia to be forced together composition warming plate by press 25Mpa pressure, and fuse through 80-100 degree celsius temperature, then the microwave drying passage that warming plate is delivered into 30 meters long by conveyer belt is dried, to obtain final product.
3. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: the raw material components of described side fascia is: pvc 250 parts, calcium powder 750 parts, stearic acid 7 parts, dibutyl ester 5 parts, CPE35 part, 5 parts, pe wax, pvc stabilizing agent 35 parts, AC blowing agent 10 parts, PVC foam conditioning agent 25 parts.
4. a kind of closed perlite integrated heat-preservation hanging plate according to claim 1, it is characterized in that: the raw material components of described pearl rock stratum is: bead 150 parts, hydrophober 2.4 parts, water glass 100 parts, silicon phosphate 8 parts, calcium bicarbonate 24 parts, 100 parts, water, polypropylene 0.5 part, hydroxypropyl methylcellulose 1.5 parts.