CN103553714A - Glaze material with cracking block effect - Google Patents
Glaze material with cracking block effect Download PDFInfo
- Publication number
- CN103553714A CN103553714A CN201310463989.5A CN201310463989A CN103553714A CN 103553714 A CN103553714 A CN 103553714A CN 201310463989 A CN201310463989 A CN 201310463989A CN 103553714 A CN103553714 A CN 103553714A
- Authority
- CN
- China
- Prior art keywords
- glaze
- block effect
- coat enamel
- weight
- cracking block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a glaze material with a cracking block effect, the glaze material with the cracking block effect includes a base glaze, a middle glaze and a surface glaze, and the glaze material with the cracking block effect is characterized in that: the base glaze comprises, by weight, 27.78% of potassium feldspar, 27.78% of quartz, 23.15% of kaolin, 13.88% of calcium carbonate and 7.41% of iron (III) oxide; the middle glaze comprises the following raw materials: by weight, 26.70% of the potassium feldspar, 26.70% of the quartz, 22.22% of the kaolin, 13.34% of the calcium carbonate, 2.23% of the iron (III) oxide and 8.81% of zirconium silicate; the surface glaze comprises the following raw materials: by weight, 28.20% of the potassium feldspar, 28.20% of the quartz, 23.22% of the kaolin, 13.9% of the calcium carbonate, 6.48% of a high temperature oxidation pigment, and a paint with an adding amount of no greater than 7% of the total weight of the raw materials of the surface glaze. A ceramic product made by the glaze formula provided by the invention shows the cracking block effect on the glaze surface, and the cracking block effect is natural and vivid, and is rough and bold in cracks.
Description
Technical field
The present invention relates to a kind of glaze with cleavage block effect, belong to ceramic glaze technical field.
Background technology
Under modern civilization tide promotes, people are to the expectation of the aesthstic level of ceramic and pursue increasingly strong, and the ceramic of different decorative patterns makes ceramic effect field more colourful.At present, the ceramic with crazing effect on sale on the market, crackle is generally very thin, does not also have the ceramic of bulk cleavage block effect.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of glaze, for the preparation of the ceramic of bulk cleavage block effect.
In order to address the above problem, the invention provides a kind of glaze with cleavage block effect, comprise ground-coat enamel, middle glaze and cover-coat enamel, it is characterized in that, described ground-coat enamel comprises following raw material by weight percentage:
Described middle glaze comprises following raw material by weight percentage:
Described cover-coat enamel comprises following raw material by weight percentage
And pigment, the addition of pigment is to be no more than 7% of above-mentioned cover-coat enamel raw material gross weight.
The ceramic that adopts the formula of glaze provided by the invention to make, glaze surface can present a kind of effect of cleavage block, naturally true to nature, and crackle is rough bold and generous, crack width 1.5-2.5mm, the about 1.5--2.0/ square centimeter of cleavage block.
Embodiment
For the present invention is become apparent, hereby with preferred embodiment, be described in detail below.
Embodiment 1
One, glaze formula
1, ground-coat enamel comprises following raw material: (ground-coat enamel: this prepares 100KG)
Table 1
Name of material | Supply producer | Stock number | Formulation weight (kg) | Remarks |
Potassium felspar sand | COLOROBBIA | 1106 | 27.78 | ? |
Quartzy | COLOROBBIA | 3003 | 27.78 | ? |
Kaolin | COLOROBBIA | TK-35 | 23.15 | ? |
Calcium carbonate | COLOROBBIA | ? | 13.88 | ? |
Ferric oxide | COLOROBBIA | ? | 7.41 | Tinting material |
2, middle glaze comprises following raw material: (middle glaze: this prepares 1OOKG)
Table 2
Name of material | Supply producer | Stock number | Formulation weight (kg) | Remarks |
Potassium felspar sand | COLOROBBIA | 1106 | 26.70 | ? |
Quartzy | COLOROBBIA | 3003 | 26.70 | ? |
Kaolin | COLOROBBIA | TK-35 | 22.22 | ? |
Calcium carbonate | COLOROBBIA | ? | 13.34 | ? |
Titanium oxide | COLOROBBIA | ? | 2.23 | Tinting material |
Sunset acid zirconium | ? | ? | 8.81 | Tinting material |
3, cover-coat enamel comprises following raw material: (middle glaze: this prepares 100KG)
Table 3
Two, prepare ceramic
Step 1): the raw material of ground-coat enamel is mixed in proportion and is ground to 250 orders;
Step 2): ceramic body is immersed in to glazing in ground-coat enamel, and the thickness of ground-coat enamel is 0.8~1mm;
Step 3): the raw material of middle glaze is mixed in proportion and is ground to 250 orders;
Step 4): to step 2 glaze in the ceramic body spraying) obtaining, the thickness of middle glaze is no more than 0.5mm;
Step 5): the raw material of cover-coat enamel is mixed in proportion and is ground to 250 orders:
Step 6): to step 4 the ceramic body spraying cover-coat enamel) obtaining, the thickness of cover-coat enamel is no more than 0.5mm;
Step 7): by step 6 work in-process that) obtain are fired 12 hours under 1250 °, obtain having the ceramic of cleavage block effect.
This glaze divides 3 glazings, draws the crackle effect glaze of iron oxide red background color, brown crackle, yellow cover-coat enamel, and crack width is at 1.5-3mm, and the yellow piece area of cover-coat enamel 1.5-2.5 square centimeter is irregular.
Claims (1)
1. a glaze with cleavage block effect, comprises ground-coat enamel, middle glaze and cover-coat enamel, it is characterized in that, described ground-coat enamel comprises following raw material by weight percentage:
Described middle glaze comprises following raw material by weight percentage:
Described cover-coat enamel comprises following raw material by weight percentage:
And pigment, the addition of pigment is to be no more than 7% of above-mentioned cover-coat enamel raw material gross weight.