CN103525345B - Flock Adhesive stick - Google Patents
Flock Adhesive stick Download PDFInfo
- Publication number
- CN103525345B CN103525345B CN201310469062.2A CN201310469062A CN103525345B CN 103525345 B CN103525345 B CN 103525345B CN 201310469062 A CN201310469062 A CN 201310469062A CN 103525345 B CN103525345 B CN 103525345B
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive stick
- flock adhesive
- diluted
- dissolved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-methacrylic 6-10 part, E-S1 epoxy number fat 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product; Have raw material to be easy to get, cost is low, and environmental protection is easy to use, effective advantage.
Description
Technical field
The invention belongs to a kind of tackiness agent.
Background technology
Tackiness agent (Bondingagent) is one of most important subsidiary material, applies very extensive in package handling.Tackiness agent is the sticking material of tool, the material that two kinds are separated can be linked together by its viscosity.The kind of tackiness agent is a lot.1. natural glue it be taken from the material of occurring in nature.Comprise the biological adhesives such as starch, protein, dextrin, gelatin, shellac, hide glue, rosin; Also the mineral binders such as pitch are comprised.2. artificial tackiness agent this be use made material, comprise the inorganic adhesives such as water glass, and the organic binder bond such as synthetic resins, synthetic rubber.Glued joint (bonding, bonding, cementing, gluing) and refer to the technology that homogeneity or heterogeneous body surface stick with glue agent and link together to there is stress distribution continuous, lightweight, or sealing, the features such as most technological temperature is low.Glued joint the connection being specially adapted to unlike material, different thickness, ultra-thin specification and complex component.Glued joint RECENT DEVELOPMENTS the fastest, application industry is extremely wide, and has great effect to high-and-new science and technology progress and people's daily life improvement.Therefore, study, all kinds of tackiness agent of development and production is very important.
Retrieve through Chinese publication, do not find the scheme identical with present patent application.
Summary of the invention:
The object of the invention is to; A kind of Flock Adhesive stick is proposed.
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-methacrylic 6-10 part, E-S1 epoxy number fat 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.
Flock Adhesive stick of the present invention, the flocking that can adapt to various occasion uses, and bond strength reaches more than the twice of prior art.
The present invention compared with prior art its beneficial effect is: have raw material and be easy to get, cost is low, and environmental protection is easy to use, effective advantage.
Embodiment:
Below in conjunction with embodiment, the invention will be further described, but embodiments of the present invention are not limited thereto.
Flock Adhesive stick of the present invention, raw materials usedly buys acquisition.
Embodiment 1
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-methacrylic 6-10 part, E-S1 epoxy number fat 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 2
Flock Adhesive stick of the present invention, is characterized in that: by weight, by methyl acrylate 25 parts, Propylene glycol monoacrylate 6 parts, ethyl propenoate 260 parts, 9 parts, vinylformic acid, N-methacrylic 6 parts, 90 parts, E-S1 epoxy number fat, benzoyl peroxide 1 part, N, N-dimethyl benzylamine 1 part, vinyl acetate 50 parts composition, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 3
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by methyl acrylate 50 parts, Propylene glycol monoacrylate 10 parts, ethyl propenoate 300 parts, 15 parts, vinylformic acid, N-methacrylic 10 parts, 120 parts, E-S1 epoxy number fat, benzoyl peroxide 5 parts, N, N-dimethyl benzylamine 3 parts, vinyl acetate 80 parts composition, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 4
Flock Adhesive stick of the present invention, is characterized in that: by weight, by methyl acrylate 25 parts, Propylene glycol monoacrylate 10 parts, ethyl propenoate 260 parts, 15 parts, vinylformic acid, N-methacrylic 6 parts, 120 parts, E-S1 epoxy number fat, benzoyl peroxide 1 part, N, N-dimethyl benzylamine 3 parts, vinyl acetate 50 parts composition, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 5
Flock Adhesive stick of the present invention, is characterized in that: by weight, by methyl acrylate 50 parts, Propylene glycol monoacrylate 6 parts, ethyl propenoate 300 parts, 9 parts, vinylformic acid, N-methacrylic 10 parts, 90 parts, E-S1 epoxy number fat, benzoyl peroxide 5 parts, N, N-dimethyl benzylamine 1 part, vinyl acetate 80 parts composition, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.
Flock Adhesive stick of the present invention, product specification, quality: solid content more than 80%, its 1% solution pH value is 7.0-7.5; Viscosity 100-120 centipoise.
Claims (1)
1. a Flock Adhesive stick, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-Methacrylamide 6-10 part, E-51 epoxy resin 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials ethanol is dissolved at 70-75 DEG C, be diluted to 15% ethanolic soln, added by whole material, at room temperature stirring reaction 12-22 hour, obtains product.