CN105690890A - Elastic three-layer waterproof and breathable composite fabric and production technology thereof - Google Patents
Elastic three-layer waterproof and breathable composite fabric and production technology thereof Download PDFInfo
- Publication number
- CN105690890A CN105690890A CN201410684486.5A CN201410684486A CN105690890A CN 105690890 A CN105690890 A CN 105690890A CN 201410684486 A CN201410684486 A CN 201410684486A CN 105690890 A CN105690890 A CN 105690890A
- Authority
- CN
- China
- Prior art keywords
- fabric
- layer
- elastic
- composite fabric
- intermediate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an elastic three-layer waterproof and breathable composite fabric. The surface layer of the composite fabric is a woven or knitted elastic fabric, the middle layer of the composite fabric is an elastic film, the base layer of the composite fabric is a napped knitted fabric, and the composite fabric is formed through bonding the surface layer and the middle layer and bonding the middle layer and the base layer. The elastic three-layer waterproof and breathable composite fabric combines the characteristics of fabrics of the surface layer, the middle layer and the bottom layer, has certain weather protection ability and good warming ability, and is suitable for producing clothes for activities with large body movement due to good elasticity and ductility.
Description
Technical field
The present invention relates to textile and textile technology, be specifically related to a kind of elastic force three layers waterproof moisture-permeable composite fabric and production technology thereof。
Background technology
Traditional waterproof moisture-permeable composite fabric feel is partially hard, elastic low and poor ductility, is not suitable for making sportswear；And sense of touch is ice-cold, thermal property is limited, it is necessary to adds heat insulating material formed at nexine, could play thermal effect well。Current people are more and more higher for the requirement of the functions such as fabric flexibility, elasticity and Waterproof Breathable, therefore, it is necessary to waterproof moisture-permeable composite fabric of the prior art carries out the improvement of structure and production technology。
Summary of the invention
It is an object of the invention to overcome the defect existed in prior art, it is provided that the elastic force three layers waterproof moisture-permeable composite fabric that a kind of flexibility, elasticity and waterproofing and moisture-penetration performances are excellent。
For realizing above-mentioned technique effect, the technical scheme is that a kind of elastic force three layers waterproof moisture-permeable composite fabric, it is characterized in that, the surface layer of described composite material is woven or knitting elastic fabric, intermediate layer is elastic film, bottom is brushed goods, and described composite material surface layer is bonded with intermediate layer, intermediate layer and bottom。
Wherein, described surface layer is polyester fibre/spandex spandex fabric fabric, and intermediate layer is PU high transparency film, and bottom is terylene polar fleece。
Wherein, the binding agent between described composite material surface layer and intermediate layer and intermediate layer and bottom is moisture cure urethanes。
The present invention also aims to provide the production technology of a kind of elastic force three layers waterproof moisture-permeable composite fabric, it is characterised in that comprise the following steps:
S1: elastic film is unwind, PUR coating, lamination composite cover fabric；
S2: by curling for S1 gained two-layer composite material-feeding, maturation of banking up；
S3: two-layer compound fabric unwinds, pellicular front PUR coating, lamination composite bottom layer fabric；
S4: by curling for S3 gained two-layer composite material-feeding, maturation of banking up。
The production technology of elastic force three layers waterproof moisture-permeable composite fabric according to claim 4, it is characterised in that the ambient humidity of maturation of banking up in described S2 and S4 is 80～90%, temperature is 30～34 DEG C。
Advantages of the present invention and having the beneficial effects that:
This elastic force three layers waterproof moisture-permeable composite fabric combines the feature of surface layer, intermediate layer and ply stratum; both there is certain climate protection ability; also there is good warming ability, simultaneously because of good springiness, have extension ability, be suitable for making the activity clothing that limb motion is relatively larger。
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described。Following example are only for clearly illustrating technical scheme, and can not limit the scope of the invention with this。
Embodiment 1
The elastic force three layers waterproof moisture-permeable composite fabric of embodiment 1, it is characterized in that, the surface layer of described composite material is woven or knitting elastic fabric, and intermediate layer is elastic film, bottom is brushed goods, and described composite material surface layer is bonded with intermediate layer, intermediate layer and bottom。
Wherein, described surface layer is polyester fibre/spandex spandex fabric fabric, and intermediate layer is PU high transparency film, and bottom is terylene polar fleece。
Wherein, the binding agent between described composite material surface layer and intermediate layer and intermediate layer and bottom is moisture cure urethanes。
The production technology of elastic force three layers waterproof moisture-permeable composite fabric comprises the following steps:
S1: elastic film is unwind, PUR coating, lamination composite cover fabric；
S2: by curling for S1 gained two-layer composite material-feeding, maturation of banking up；
S3: two-layer compound fabric unwinds, pellicular front PUR coating, lamination composite bottom layer fabric；
S4: by curling for S3 gained two-layer composite material-feeding, maturation of banking up。
The production technology of elastic force three layers waterproof moisture-permeable composite fabric according to claim 4, it is characterised in that the ambient humidity of maturation of banking up in described S2 and S4 is 85%, temperature is 32 DEG C。
Embodiment 2
Embodiment 2 is in that from the different of embodiment 1: the ambient humidity of maturation of banking up in S2 and S4 is 80%, and temperature is 30 DEG C。
Embodiment 3
Embodiment 3 is in that from the different of embodiment 1: the ambient humidity of maturation of banking up in S2 and S4 is 90%, and temperature is 34 DEG C。
Ensureing the temperature of maturation, humidity and time, such guarantee binding agent fully reacts, and gives the good intensity of product and washing fastness。
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention。
Claims (5)
1. an elastic force three layers waterproof moisture-permeable composite fabric, it is characterized in that, the surface layer of described composite material is woven or knitting elastic fabric, and intermediate layer is elastic film, bottom is brushed goods, and described composite material surface layer is bonded with intermediate layer, intermediate layer and bottom。
2. elastic force three layers waterproof moisture-permeable composite fabric according to claim 1, it is characterised in that described surface layer is polyester fibre/spandex spandex fabric fabric, intermediate layer is PU high transparency film, and bottom is terylene polar fleece。
3. elastic force three layers waterproof moisture-permeable composite fabric according to claim 1, it is characterised in that the binding agent between described composite material surface layer and intermediate layer and intermediate layer and bottom is moisture cure urethanes。
4. the production technology of an elastic force three layers waterproof moisture-permeable composite fabric, it is characterised in that comprise the following steps:
S1: elastic film is unwind, PUR coating, lamination composite cover fabric；
S2: by curling for S1 gained two-layer composite material-feeding, maturation of banking up；
S3: two-layer compound fabric unwinds, pellicular front PUR coating, lamination composite bottom layer fabric；
S4: by curling for S3 gained two-layer composite material-feeding, maturation of banking up。
5. the production technology of elastic force three layers waterproof moisture-permeable composite fabric according to claim 4, it is characterised in that the ambient humidity of maturation of banking up in described S2 and S4 is 80～90%, and temperature is 30～34 DEG C。