CN103508723B - A kind of preparation method of high temperature five color painting in the glaze hair ceramic double-layer vacuum cup - Google Patents
A kind of preparation method of high temperature five color painting in the glaze hair ceramic double-layer vacuum cup Download PDFInfo
- Publication number
- CN103508723B CN103508723B CN201210220265.3A CN201210220265A CN103508723B CN 103508723 B CN103508723 B CN 103508723B CN 201210220265 A CN201210220265 A CN 201210220265A CN 103508723 B CN103508723 B CN 103508723B
- Authority
- CN
- China
- Prior art keywords
- glaze
- time
- carry out
- layer vacuum
- cup
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A preparation method for high temperature five color painting in the glaze hair ceramic double-layer vacuum cup, the method comprises the following steps: step one, blank forming: adopt selected raw material, carries out the batching of pug by certain percentage by weight; Above-mentioned batching is carried out mud processed processing, then carry out solidifying molded inner bag and outer cup respectively; After depanning, inner bag and outer cup are carried out seamless interfacing by interface mud, through refine base, become mao ceramic double-layer vacuum cup semi-finished product; Step 2, to fire through four times, after cooling, sorting detects, finished product, the hair ceramic double-layer vacuum cup tool that this method is fired, cup body adopts double-decker can play the effect of insulation and cold insulation, without the need to adding any insulation material, be adopt hard fire colour under glaze to carry out colored drawing to fire and form outside cup body, color be vivid, graceful, never shank color.<!--1-->
Description
Technical field
The present invention relates to a kind of preparation method of high temperature five color painting in the glaze hair ceramic double-layer vacuum cup.
Background technology
Traditional thermos cup is mostly that glass or metal are made, adopt the double-decker form of inner bag and outer cup, like this when splendid attire hot water, owing to there is certain interval between inner bag and outer cup, so just play the object of heat-insulation and heat-preservation, the cup feature of this glass or metal material manufactures simply, cost is low, but along with the living standard of people improves gradually, more and more focus on life grade and quality of life, also thermos cup is had higher requirement, there is the thermos cup of hair ceramic products in the market, the another in addition modification such as marble paper on hair porcelain surface, greatly enrich decorative effect, but the thermos cup surface pattern of the hair ceramic products produced at present is old, easily fade, make troubles to user.
Summary of the invention
The present invention again with overcome the deficiencies in the prior art, a kind of preparation method of high temperature five color painting in the glaze hair ceramic double-layer vacuum cup is provided.
The present invention is achieved in that a kind of preparation method of high temperature five color painting in the glaze hair ceramic double-layer vacuum cup, and the method comprises the following steps:
Step one, blank forming: adopt selected raw material, carry out the batching of pug as following weight percent, china clay 10% ~ 15%, kaolin 70% ~ 95%, water 5%; Above-mentioned batching is carried out mud processed processing, then carry out solidifying molded inner bag and outer cup respectively; After depanning, inner bag and outer cup are carried out seamless interfacing by interface mud, through accurate repaired biscuit, become mao ceramic double-layer vacuum cup semi-finished product;
Step 2, glaze firing: dried by the hair ceramic double-layer vacuum cup semi-finished product prepared in step one, wash water, remove surface impurity, carry out first time and fire, and firing temperature is 820 DEG C ~ 830 DEG C for the first time, and the firing time is 4 ~ 6 hours; After cooling, carry out executing inside and outside glaze, carry out second time and fire, second time firing temperature is 840 DEG C ~ 850 DEG C, and the firing time is 4 ~ 6 hours; After cooling, carry out hand painting, then carry out Fen glaze, carry out button mud cake high temperature button after getting mouthful glaze and burn, firing temperature is 1390 DEG C ~ 1400 DEG C for the third time, and the firing time is 16 ~ 18 hours; After cooling, rim of a cup carries out wiping husky polishing, and phase mouth glaze carries out the 4th time and fires, and the 4th time firing temperature is 1350 DEG C ~ 1360 DEG C, and the firing time is 12 hours; After cooling, sorting detect, finished product.
Described phase mouth glaze operation is the half-finished rim of a cup abrasive machine of hair ceramic double-layer vacuum cup fired of third time is carried out polishing wipe sand, moves on rotating disk and carry out glazing with the high-temperature glaze that Fen water-color paintbrush glues 60 ° after polishing.
The invention has the beneficial effects as follows:
1, the hair ceramic double-layer vacuum cup tool fired of this method, cup body adopts double-decker can play the effect of insulation and cold insulation, without the need to adding any insulation material;
2, be adopt hard fire colour under glaze to enter to draw multi-coloured porcelain system to form outside cup body, color be vivid, graceful, never shank color;
3, underglaze colour technique bold innovation on traditional basis, product exquisiteness is attractive in appearance, unleaded, without every, radiationless environmental protection.
Detailed description of the invention
In order to make object of the present invention, technical scheme and advantage clearly understand, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
A preparation method for high temperature five color painting in the glaze hair ceramic double-layer vacuum cup, the method comprises the following steps:
Step one, blank forming: adopt selected raw material, carry out the batching of pug as following weight percent, china clay 10% ~ 15%, kaolin 70% ~ 95%, water 5%; Above-mentioned batching is carried out mud processed processing, then carry out solidifying molded inner bag and outer cup respectively; After depanning, inner bag and outer cup are carried out seamless interfacing by interface mud, through accurate repaired biscuit, become mao ceramic double-layer vacuum cup semi-finished product;
Step 2, glaze firing: dried by the hair ceramic double-layer vacuum cup semi-finished product prepared in step one, wash water, remove surface impurity, carry out first time and fire, and firing temperature is 820 DEG C ~ 830 DEG C for the first time, and the firing time is 4 ~ 6 hours; After cooling, carry out executing inside and outside glaze, carry out second time and fire, second time firing temperature is 840 DEG C ~ 850 DEG C, and the firing time is 4 ~ 6 hours; After cooling, carry out hand painting, then carry out Fen glaze, carry out button mud cake high temperature button after getting mouthful glaze and burn, firing temperature is 1390 DEG C ~ 1400 DEG C for the third time, and the firing time is 16 ~ 18 hours; After cooling, rim of a cup carries out wiping husky polishing, and phase mouth glaze carries out the 4th time and fires, and the 4th time firing temperature is 1350 DEG C ~ 1360 DEG C, and the firing time is 12 hours; After cooling, sorting detect, finished product.
Described phase mouth glaze operation is the half-finished rim of a cup abrasive machine of hair ceramic double-layer vacuum cup fired of third time is carried out polishing wipe sand, moves on rotating disk and carry out glazing with the high-temperature glaze that Fen water-color paintbrush glues 60 ° after polishing.
These are only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. a preparation method for high temperature five color painting in the glaze hair ceramic double-layer vacuum cup, is characterized in that: the method comprises the following steps:
Step one, blank forming: adopt selected raw material, carry out the batching of pug as following weight percent, china clay 10% ~ 15%, kaolin 70% ~ 95%, water 5%; Above-mentioned batching is carried out mud processed processing, then carry out solidifying molded inner bag and outer cup respectively; After depanning, inner bag and outer cup are carried out seamless interfacing by interface mud, through accurate repaired biscuit, become mao ceramic double-layer vacuum cup semi-finished product;
Step 2, glaze firing: dried by the hair ceramic double-layer vacuum cup semi-finished product prepared in step one, wash water, remove surface impurity, carry out first time and fire, and firing temperature is 820 DEG C ~ 830 DEG C for the first time, and the firing time is 4 ~ 6 hours; After cooling, carry out executing inside and outside glaze, carry out second time and fire, second time firing temperature is 840 DEG C ~ 850 DEG C, and the firing time is 4 ~ 6 hours; After cooling, carry out hand painting, then carry out Fen glaze, carry out button mud cake high temperature button after getting mouthful glaze and burn, firing temperature is 1390 DEG C ~ 1400 DEG C for the third time, and the firing time is 16 ~ 18 hours; After cooling, rim of a cup carries out wiping husky polishing, and phase mouth glaze carries out the 4th time and fires, and the 4th time firing temperature is 1350 DEG C ~ 1360 DEG C, and the firing time is 12 hours; After cooling, sorting detect, finished product.
2. the preparation method of a kind of high temperature five color painting in the glaze hair ceramic double-layer vacuum cup according to claim 1, it is characterized in that: described phase mouth glaze operation is the half-finished rim of a cup abrasive machine of hair ceramic double-layer vacuum cup fired of third time is carried out polishing wipe sand, move to after polishing on rotating disk and carry out glazing with the high-temperature glaze that Fen water-color paintbrush glues 60 °.