CN103467067A - 一种抛晶砖 - Google Patents

一种抛晶砖 Download PDF

Info

Publication number
CN103467067A
CN103467067A CN201310355471XA CN201310355471A CN103467067A CN 103467067 A CN103467067 A CN 103467067A CN 201310355471X A CN201310355471X A CN 201310355471XA CN 201310355471 A CN201310355471 A CN 201310355471A CN 103467067 A CN103467067 A CN 103467067A
Authority
CN
China
Prior art keywords
powder
hour
parts
adobe
brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310355471XA
Other languages
English (en)
Inventor
刘大伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUAIBEI WHIRLPOOL BUILDING CERAMIC Co Ltd
Original Assignee
HUAIBEI WHIRLPOOL BUILDING CERAMIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUAIBEI WHIRLPOOL BUILDING CERAMIC Co Ltd filed Critical HUAIBEI WHIRLPOOL BUILDING CERAMIC Co Ltd
Priority to CN201310355471XA priority Critical patent/CN103467067A/zh
Publication of CN103467067A publication Critical patent/CN103467067A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抛晶砖，其是由下述重量份的原料制得:高塑性粘土15-25，高岭石粉15-20，叶腊石粉10-15，瓷石粉20-30，长石粉10-15，石英粉5-10,滑石1-3,改性电石渣颗粒2-4，水适量。

Description

一种抛晶砖
技术领域
本发明涉及制砖领域，确切地说是一种抛晶砖。
背景技术
抛晶砖是一种通过表面打磨成的一种光洁亮砖，它图案清晰逼真，坚硬耐磨，适用于各种装饰，现有的抛釉砖从硬度上是无法比拟的。
发明内容
本发明的目的在于提供一种抗压强度高，硬度好，抗污效果好，亮度超过95%以上，光泽度好的抛晶砖。
上述目的通过以下方案实现：
一种抛晶砖，其特征在于：其是由下述重量份的原料制得:高塑性粘土15-25 ，高岭石粉15-20，叶腊石粉10-15，瓷石粉20-30，长石粉10-15，石英粉5-10,滑石1-3,改性电石渣颗粒2-4，水适量。
所述的一种抛晶砖，其特征在于：
     制备方法为(1)取电石渣破碎，所得粉料于浓度为3-5%的氯化钠中浸泡8-9小时，800-900℃下烧结3-4小时，再以5-10℃每分钟的速率降温到500-550℃保温1-2小时后，取出，冷却，加入相当于粉料总重量1-2%的甲酸钙、1-2%的氧化淀粉、1-2%的硅烷偶联剂kh570，以及适量水，于1800-2000rpm下高速剪切10-15分钟后，取出，烘干，研磨，过100-200目筛，再加入相当于上述粉料总重量1-2%的白乳胶搅拌均匀后加入适量水分，造粒，颗粒粒径在3-5mm，然后将制好的颗粒于200-300℃下烧制20-30分钟后，即得改性电石渣颗粒备用；
（2）按重量份将各原料混匀，三辊研磨机研磨1-2小时，压制成型，得砖坯，将砖坯干燥后进行表面抛坯处理，得到表面具有清晰纹理的砖坯；
（3）再按照常规工艺经施釉、印花装饰、施透明熔块粉，烧成、抛光后，将砖坯入窑烧成并抛光即得。
所述的一种抛晶砖，其特征在于：烧成时间为2-4小时，烧成温度为1100－1300℃。
本发明的有益效果为：本发明的通过添加改性电石渣颗粒，合理配料，使得抗压强度高，硬度好，抗污效果好，亮度超过95%以上，光泽度好，同时耐磨性好,装饰应用范围广,能耗水平低,生产周期短。所得抛光后的抛晶砖中没有肉眼可见的气泡，均一性好。使用电石渣、陶瓷抛光废渣粉等废料，变废为宝。
具体实施方式
一种抛晶砖，其是由下述重量份（kg)的原料制得:高塑性粘土25 ，高岭石粉20，叶腊石粉15，瓷石粉30，长石粉15，石英粉10,滑石3,改性电石渣颗粒4，水适量。
所述的一种抛晶砖，
     制备方法为
     (1)取电石渣破碎，所得粉料于浓度为4%的氯化钠中浸泡9小时，870℃下烧结3小时，再以10℃每分钟的速率降温到500℃保温2小时后，取出，冷却，加入相当于粉料总重量2%的甲酸钙、1%的氧化淀粉、1%的硅烷偶联剂kh570，以及适量水，于1800rpm下高速剪切15分钟后，取出，烘干，研磨，过200目筛，再加入相当于上述粉料总重量1%的白乳胶搅拌均匀后加入适量水分，造粒，颗粒粒径在3-5mm，然后将制好的颗粒于300℃下烧制30分钟后，即得改性电石渣颗粒备用；
（2）按重量份将各原料混匀，三辊研磨机研磨2小时，压制成型，得砖坯，将砖坯干燥后进行表面抛坯处理，得到表面具有清晰纹理的砖坯；
（3）再按照常规工艺经施釉、印花装饰、施透明熔块粉，烧成、抛光后，将砖坯入窑烧成并抛光即得；所述的烧成时间为3小时，烧成温度为1300℃。
本实施例抗压强度为17-20MPA，比重为0.5-0.6，抗折强度为8.3MPA。

Claims (3)

1.一种抛晶砖，其特征在于：其是由下述重量份的原料制得:高塑性粘土15-25 ，高岭石粉15-20，叶腊石粉10-15，瓷石粉20-30，长石粉10-15，石英粉5-10,滑石1-3,改性电石渣颗粒2-4，白土1-2，陶瓷抛光废渣粉1-2，废玻璃粉1-2，水适量。
2.根据权利要求1所述的一种抛晶砖，其特征在于：
     制备方法为：
(1)取电石渣破碎，所得粉料于浓度为3-5%的氯化钠中浸泡8-9小时，800-900℃下烧结3-4小时，再以5-10℃每分钟的速率降温到500-550℃保温1-2小时后，取出，冷却，加入相当于粉料总重量1-2%的甲酸钙、1-2%的氧化淀粉、1-2%的硅烷偶联剂kh570，以及适量水，于1800-2000rpm下高速剪切10-15分钟后，取出，烘干，研磨，过100-200目筛，再加入相当于上述粉料总重量1-2%的白乳胶搅拌均匀后加入适量水分，造粒，颗粒粒径在3-5mm，然后将制好的颗粒于200-300℃下烧制20-30分钟后，即得改性电石渣颗粒备用；
（2）按重量份将各原料混匀，三辊研磨机研磨1-2小时，压制成型，得砖坯，将砖坯干燥后进行表面抛坯处理，得到表面具有清晰纹理的砖坯；
（3）再按照常规工艺经施釉、印花装饰、施透明熔块粉，烧成、抛光后，将砖坯入窑烧成并抛光即得。
3.根据权利要求2所述的一种抛晶砖，其特征在于：烧成时间为2-4小时，烧成温度为1100－1300℃。
CN201310355471XA 2013-08-15 2013-08-15 一种抛晶砖 Pending CN103467067A (zh)