CN103450391A - 耐水性无皂丙烯酸乳液 - Google Patents
耐水性无皂丙烯酸乳液 Download PDFInfo
- Publication number
- CN103450391A CN103450391A CN2013103676609A CN201310367660A CN103450391A CN 103450391 A CN103450391 A CN 103450391A CN 2013103676609 A CN2013103676609 A CN 2013103676609A CN 201310367660 A CN201310367660 A CN 201310367660A CN 103450391 A CN103450391 A CN 103450391A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic emulsion
- water
- acrylamide
- soap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
耐水性无皂丙烯酸乳液,包括按照质量份数计的如下原料:丙烯酸丁酯5-25份、丙烯酸0.1-1.5份、甲基丙烯酸甲酯12-28份、N-羟甲基丙烯酰胺5-10份、乙酰丙酮钙0.2-0.8份、2-丙烯酰胺基-2-甲基丙磺酸0.5-1份、过硫酸铵0.1-0.5份、有机硅憎水粉末SHP50 0.2-0.5份、水40-50份。本发明具有良好的耐水性,其干膜耐水性较好,40天后无变化,耐湿洗性大于3000次。
Description
技术领域
本发明属于丙烯酸乳液领域,具体涉及一种耐水性无皂丙烯酸乳液。
背景技术
传统的丙烯酸乳液存在耐水性不佳的缺点,而在丙烯酸乳液的聚合过程中又会添加一定量的乳化剂,当该丙烯酸乳液被用来涂装时,残留其中的乳化剂又会进一步影响涂膜的性能导致涂膜的耐水性、附着力不佳,光泽不理想等。
虽然现有丙烯酸乳液的性能已得到改善,但仍不能满足人们的使用需求。综上所述,如何克服现有技术的不足已成为现有丙烯酸乳液领域亟待解决的问题。
发明内容
本发明的目的是克服现有技术的不足而提出一种耐水性无皂丙烯酸乳液,本发明的耐水性无皂丙烯酸乳液,具有良好的耐水性和附着力,涂膜的光泽度较佳。
本发明的技术方案如下:
耐水性无皂丙烯酸乳液,包括按照质量份数计的如下原料:丙烯酸丁酯5-25份、丙烯酸0.1-1.5份、甲基丙烯酸甲酯12-28份、N-羟甲基丙烯酰胺5-10份、乙酰丙酮钙0.2-0.8份、2-丙烯酰胺基-2-甲基丙磺酸0.5-1份、过硫酸铵0.1-0.5份、有机硅憎水粉末SHP50 0.2-0.5份、水40-50份。
所述的耐水性无皂丙烯酸乳液,包括按照质量份数计的如下原料:丙烯酸丁酯20.8份、丙烯酸1.2份、甲基丙烯酸甲酯20份、N-羟甲基丙烯酰胺8份、乙酰丙酮钙0.6份、2-丙烯酰胺基-2-甲基丙磺酸0.7份、过硫酸铵0.3份、有机硅憎水粉末SHP50 0.4份、水45份。
本发明制备方法:按照质量配比,将水加入反应瓶中,搅拌升温至60℃,加入丙烯酸丁酯、丙烯酸、甲基丙烯酸甲酯、N-羟甲基丙烯酰胺、乙酰丙酮钙、2-丙烯酰胺基-2-甲基丙磺酸、有机硅憎水粉末SHP50,搅拌升温至80℃,恒温搅拌50min,后滴加过硫酸铵,滴加完毕,继续反应20min后升温至100℃反应2h,降温至35℃,用氨水调节溶液pH,使溶液呈中性,过滤即可得成品。
有益效果:本发明具有良好的耐水性,其干膜耐水性较好,40天后无变化,耐湿洗性大于3000次,可广泛适用于建筑外墙及金属涂装。
具体实施方式
下面结合具体实施方式对本发明作进一步详细说明。
实施例1
耐水性无皂丙烯酸乳液,包括按照质量份数计的如下原料:丙烯酸丁酯5份、丙烯酸0.1份、甲基丙烯酸甲酯12份、N-羟甲基丙烯酰胺5份、乙酰丙酮钙0.2份、2-丙烯酰胺基-2-甲基丙磺酸0.5份、过硫酸铵0.1份、有机硅憎水粉末SHP50 0.2份、水40份。
实施例2
耐水性无皂丙烯酸乳液,包括按照质量份数计的如下原料:丙烯酸丁酯25份、丙烯酸1.5份、甲基丙烯酸甲酯28份、N-羟甲基丙烯酰胺10份、乙酰丙酮钙0.8份、2-丙烯酰胺基-2-甲基丙磺酸1份、过硫酸铵0.5份、有机硅憎水粉末SHP50 0.5份、水50份。
实施例3
耐水性无皂丙烯酸乳液,包括按照质量份数计的如下原料:丙烯酸丁酯20.8份、丙烯酸1.2份、甲基丙烯酸甲酯20份、N-羟甲基丙烯酰胺8份、乙酰丙酮钙0.6份、2-丙烯酰胺基-2-甲基丙磺酸0.7份、过硫酸铵0.3份、有机硅憎水粉末SHP50 0.4份、水45份。
将实施例1-3制备的成品进行下表各项性能测试,结果见表1:
表1 性能测试数据
性能 | 实施例1 | 实施例2 | 实施例3 |
附着力(划圈法),级 | 2 | 2 | 1 |
耐水性 | 38天无变化 | 40天无变化 | 40天无变化 |
耐湿洗次数,次 | 3000 | 3100 | 3050 |
由上表可见,本发明具有较好的附着力,其干膜耐水性和耐湿洗次数均较高,与常规的丙烯酸乳液相比具有较好的性能。
上述实施例仅是对本发明产品的说明,并非对本发明做出任何形式上的限制,在不脱离本发明的技术方案范围之内,任何利用上述揭示的技术内容作出简单变换的等同方案,均属本发明的保护范围。
Claims (2)
1.耐水性无皂丙烯酸乳液,其特征在于,包括按照质量份数计的如下原料:丙烯酸丁酯5-25份、丙烯酸0.1-1.5份、甲基丙烯酸甲酯12-28份、N-羟甲基丙烯酰胺5-10份、乙酰丙酮钙0.2-0.8份、2-丙烯酰胺基-2-甲基丙磺酸0.5-1份、过硫酸铵0.1-0.5份、有机硅憎水粉末SHP50 0.2-0.5份、水40-50份。
2.根据权利要求1所述的耐水性无皂丙烯酸乳液,其特征在于,包括按照质量份数计的如下原料:丙烯酸丁酯20.8份、丙烯酸1.2份、甲基丙烯酸甲酯20份、N-羟甲基丙烯酰胺8份、乙酰丙酮钙0.6份、2-丙烯酰胺基-2-甲基丙磺酸0.7份、过硫酸铵0.3份、有机硅憎水粉末SHP50 0.4份、水45份。