CN103388043B - Converter low silicon smelting method - Google Patents
Converter low silicon smelting method Download PDFInfo
- Publication number
- CN103388043B CN103388043B CN201310310634.2A CN201310310634A CN103388043B CN 103388043 B CN103388043 B CN 103388043B CN 201310310634 A CN201310310634 A CN 201310310634A CN 103388043 B CN103388043 B CN 103388043B
- Authority
- CN
- China
- Prior art keywords
- serpentine
- molten iron
- add
- silica
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of converter low silicon smelting method, it is characterized in that adding with silica and magnesia the serpentine as main component at initial smelting period, silicone content in molten iron is improved to 0.20% 0.30%, adding serpentine and be equivalent to add the content of silicon in molten iron, the directly silica in serpentine of the calcium oxide in lime is combined slagging.The present invention refines early stage and adds serpentine; calcium oxide in the lime directly silica in serpentine is combined slagging thus solves slagization and do not open; process returns dry phenomenon and steel adhesion on oxygen lance phenomenon; magnesia in serpentine can play and protect the effect of furnace lining to add content of magnesia in slag simultaneously; making slag splashing effect strengthen, life of converter is extended.
Description
Technical field
The invention belongs to steelmaking technical field.
Background technology
In converter smelting technical field, in molten iron, silicone content (0.08%-0.20%) is low, easily occurs that slagization is not opened, and little being very easy to occurs returning dry phenomenon the quantity of slag, adds metal loss;Furnace lining is washed away aggravation by oxygen stream, and steel adhesion on oxygen lance is seriously difficult to clear up, and adds the amount of labour;Difficulty is added in daily smelting.
Summary of the invention
It is an object of the invention to provide a kind of converter low silicon smelting method, low to solve prior art molten iron silicon, easily occur that slagization is not opened little being very easy to of the quantity of slag and occurred that returning dry phenomenon adds metal loss, furnace lining is washed away aggravation by oxygen stream, steel adhesion on oxygen lance is seriously difficult to clear up, and adds the amount of labour.The problems such as difficulty are added in daily smelting.
The technical solution adopted for the present invention to solve the technical problems is to add with silica and magnesia the serpentine as main component at initial smelting period, silicone content in molten iron is improved to 0.20%-0.30%, adding serpentine and be equivalent to add the content of silicon in molten iron, the directly silica in serpentine of the calcium oxide in lime is combined slagging.It is specifically filled a prescription:
Dolomite: 13-15 kg/ton steel, molten iron: 900-1030 kg/ton steel, lime: 36-43 kg/ton steel, serpentine: often increase by 0.01% silicon, need to add 0.55 kilogram-0.65 kilogram of serpentine.
Above-mentioned do not add serpentine before in molten iron silicone content be 0.08%-0.20%.
After increase serpentine, in molten iron, silicone content is 0.2%-0.30%.
Using the positive effect of the present invention is that refining early stage adds serpentine; calcium oxide in the lime directly silica in serpentine is combined slagging thus solves slagization and do not open; process returns dry phenomenon and steel adhesion on oxygen lance phenomenon; magnesia in serpentine can play and protect the effect of furnace lining to add content of magnesia in slag simultaneously; making slag splashing effect strengthen, life of converter is extended.
Detailed description of the invention
Embodiment 1
In the molten iron bought on market, silicone content is 0.10%, the serpentine as main component is added with silica and magnesia at initial smelting period, silicone content in molten iron is improved to 0.22%, adding serpentine and be equivalent to add the content of silicon in molten iron, the directly silica in serpentine of the calcium oxide in lime is combined slagging.It is specifically filled a prescription: dolomite: 13 kg/ton steel, molten iron: 950 kg/ton steel, lime: 37 kg/ton steel, serpentine: 7.2 kilograms.
Wherein after increase serpentine, in molten iron, silicone content is 0.22%.
Its smelting process is same as the prior art.
Embodiment 2
In the molten iron bought on market, silicone content is 0.15%, the serpentine as main component is added with silica and magnesia at initial smelting period, silicone content in molten iron is improved to 0.25%, adding serpentine and be equivalent to add the content of silicon in molten iron, the directly silica in serpentine of the calcium oxide in lime is combined slagging.It is specifically filled a prescription: dolomite: 14 kg/ton steel, molten iron: 990 kg/ton steel, lime: 40 kg/ton steel, serpentine: 6 kilograms.
Wherein after increase serpentine, in molten iron, silicone content is 0.25%.
Its smelting process is same as the prior art.
Embodiment 3
In the molten iron bought on market, silicone content is 0.17%, the serpentine as main component is added with silica and magnesia at initial smelting period, silicone content in molten iron is improved to 0.28%, adding serpentine and be equivalent to add the content of silicon in molten iron, the directly silica in serpentine of the calcium oxide in lime is combined slagging.It is specifically filled a prescription: dolomite: 14.5 kg/ton steel, molten iron: 1020 kg/ton steel, lime: 42 kg/ton steel, serpentine: 6.93 kilograms.
Wherein after increase serpentine, in molten iron, silicone content is 0.28%.
Its smelting process is same as the prior art.
Claims (1)
1. a converter low silicon smelting method, it is characterized in that adding with silica and magnesia the serpentine as main component at initial smelting period, silicone content in molten iron is improved to 0.22%-0.30%, adding serpentine and be equivalent to add the content of silicon in molten iron, the directly silica in serpentine of the calcium oxide in lime is combined slagging;It is specifically filled a prescription: dolomite: 13-15 kg/ton steel, molten iron: 900-1030 kg/ton steel, lime: 36-43 kg/ton steel, serpentine: often increase by 0.01% silicon, needs to add 0.55 kilogram-0.65 kilogram of serpentine;Above-mentioned do not add serpentine before in molten iron silicone content be 0.08%-0.20%.