CN103387350A - 环保型低碱无cl-速凝剂 - Google Patents
环保型低碱无cl-速凝剂 Download PDFInfo
- Publication number
- CN103387350A CN103387350A CN2013103324934A CN201310332493A CN103387350A CN 103387350 A CN103387350 A CN 103387350A CN 2013103324934 A CN2013103324934 A CN 2013103324934A CN 201310332493 A CN201310332493 A CN 201310332493A CN 103387350 A CN103387350 A CN 103387350A
- Authority
- CN
- China
- Prior art keywords
- environment
- accelerating chemicals
- alkali
- friendly type
- calcium powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种环保型低碱无CL-速凝剂,它由下述重量百分比的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠4~34%、铝酸钠2~14%、高铝粉煤灰5.8~63.8%、超微细钙粉尘0~75%和聚乙烯醇24-880.2~1.2%。本发明成本低廉、速凝效果良好,可用于湿法喷射混凝土,也可用于干法喷射混凝土,亦可用于非喷射施工的水泥混泥土工程中。
Description
技术领域
本发明涉及一种速凝剂,尤其涉及环保型低碱无CL-速凝剂。
背景技术
国内速凝剂是随着喷射混凝土技术的发展而发展起来的,由初始单一化工产品到多种化工产品的复合,性能也由仅仅满足施工需要而迅速发展到具有快凝、早强、无毒、粘着性强、施工度好、后期强度基本不降低,由高碱(pH值13左右)向低碱、无碱化发展。目前,强碱型价格便宜,初终凝快,但缺点是碱性高,喷射混凝土后期强度损失较多,会对生产工人的皮肤产生刺激腐蚀,遇有碱骨料反应的蛋白石、伊利石等对喷射混凝土会有破坏作用。
在日本、欧洲等发达国家,几乎不存在高碱性速凝剂,国内也开始越来越多采用低碱或无碱粉体速凝剂,但由于大部分采用化工合成再加工技术,因此价格较高,应用较少。
发明内容
本发明所要解决的技术问题是提供一种成本低廉、速凝效果良好的环保型低碱无CL-速凝剂。
为解决上述问题,本发明所述的环保型低碱无CL-速凝剂,其特征在于:它由下述重量百分比的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠4~34%、铝酸钠2~14%、高铝粉煤灰5.8~63.8%、超微细钙粉尘0~75%和聚乙烯醇24-88 0.2~1.2%。
所述氟化钠为含量≥90%的工业级氟化钠。
所述高铝粉煤灰是指三氧化二铝含量≥30%的一级粉煤灰。
所述超微细钙粉尘是指超微细钙粉尘是高炉冶炼过程中随着煤气携带出的原料粉尘及高温区激烈反应而产生的微粒径干式除尘而得到的产物。
本发明与现有技术相比具有以下优点:
1、本发明中的粉煤灰和超微细钙粉尘均属于除尘产物,二者化学成分相同或相近,其主要成分是氧化钙、氧化镁和二氧化硅。具有如下特点:⑴粒径极其微小,密度小,易飘散于大气中污染环境;⑵易反应,活性好;⑶具有一定的化学毒性。开发对其的综合利用不仅可以使宝贵的资源得到充分利用,还可以减轻对环境的污染。而采用水泥混凝土固化易飘浮有毒物质目前不仅在国内还是在国际上均认为是最可靠、最安全、最有效的措施。
2、本发明中掺加的超微细钙粉尘,由于其粒径与微硅粉相近,经过多次水泥净浆及胶砂试验发现,其不仅可提高水泥胶砂强度,还可降低水泥标准稠度(参见表1)。
表1
3、本发明与现有技术中的同类产品相比,具有制备过程简单,不需要特殊的加工设备,同时,本发明原材料价格低廉且市场供货充足,因此,生产投入小,成本低廉。
4、本发明与现有技术中的同类产品相比,在相同掺加量的情况下,采用JC477-2005标准试验,不仅初、终凝结时间均缩短,而且1d强度高出3.0MPa,28d强度保有率好(参见表2);同时本发明稳定性好,能够长期储存(至少在6个月以上)。
表2
5、由于本发明不像碱性速凝剂含有大量的碱性物质,因此,极大程度上降低了由于碱性物质的引入对混凝土造成的破坏作用,如碱骨料反应;同时由于本发明未引进含CL-的盐类,因此,大大降低了钢筋锈蚀的几率,且无刺激性,对水泥混凝土的性能无不良影响。
6、本发明可用于湿法喷射混凝土,也可用于干法喷射混凝土,亦可用于非喷射施工的水泥混泥土工程中。
具体实施方式
实施例1 环保型低碱无CL-速凝剂,它由下述重量百分比(kg/kg)的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠4%、铝酸钠14%、高铝粉煤灰5.8%、超微细钙粉尘75%和聚乙烯醇24-88 1.2%。
实施例2 环保型低碱无CL-速凝剂,它由下述重量百分比(kg/kg)的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠10%、铝酸钠11%、高铝粉煤灰18%、超微细钙粉尘60%和聚乙烯醇24-88 1%。
实施例3 环保型低碱无CL-速凝剂,它由下述重量百分比(kg/kg)的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠16%、铝酸钠8%、高铝粉煤灰30.2%、超微细钙粉尘45%和聚乙烯醇24-88 0.8%。
实施例4 环保型低碱无CL-速凝剂,它由下述重量百分比(kg/kg)的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠22%、铝酸钠6%、高铝粉煤灰41.4%、超微细钙粉尘30%和聚乙烯醇24-88 0.6%。
实施例5 环保型低碱无CL-速凝剂,它由下述重量百分比(kg/kg)的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠28%、铝酸钠4%、高铝粉煤灰52.6%、超微细钙粉尘15%和聚乙烯醇24-88 0.4%。
实施例6 环保型低碱无CL-速凝剂,它由下述重量百分比(kg/kg)的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠34%、铝酸钠2%、高铝粉煤灰63.8%、超微细钙粉尘0%和聚乙烯醇24-88 0.2%。
上述实施例1~6中,氟化钠为含量≥90%的工业级氟化钠。高铝粉煤灰是指三氧化二铝含量≥30%的一级粉煤灰。铝酸钠为工业级。
超微细钙粉尘是指超微细钙粉尘是高炉冶炼过程中随着煤气携带出的原料粉尘及高温区激烈反应而产生的微粒径干式除尘而得到的产物。
Claims (4)
1.环保型低碱无CL-速凝剂,其特征在于:它由下述重量百分比的原料混合均匀后,经粉磨、过0.08mm方空筛,使其筛余率<15%,即得速凝剂产品:氟化钠4~34%、铝酸钠2~14%、高铝粉煤灰5.8~63.8%、超微细钙粉尘0~75%和聚乙烯醇24-88 0.2~1.2%。
2.如权利要求1所述的环保型低碱无CL-速凝剂,其特征在于:所述氟化钠为含量≥90%的工业级氟化钠。
3.如权利要求1所述的环保型低碱无CL-速凝剂,其特征在于:所述高铝粉煤灰是指三氧化二铝含量≥30%的一级粉煤灰。
4.如权利要求1所述的环保型低碱无CL-速凝剂,其特征在于:所述超微细钙粉尘是指超微细钙粉尘是高炉冶炼过程中随着煤气携带出的原料粉尘及高温区激烈反应而产生的微粒径干式除尘而得到的产物。