CN103360947A - 一种涤纶树脂沥青涂料 - Google Patents
一种涤纶树脂沥青涂料 Download PDFInfo
- Publication number
- CN103360947A CN103360947A CN2013103068340A CN201310306834A CN103360947A CN 103360947 A CN103360947 A CN 103360947A CN 2013103068340 A CN2013103068340 A CN 2013103068340A CN 201310306834 A CN201310306834 A CN 201310306834A CN 103360947 A CN103360947 A CN 103360947A
- Authority
- CN
- China
- Prior art keywords
- polyester resin
- component
- parts
- prepared
- bituminous composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种涤纶树脂沥青涂料,由组份A和组份B按重量比为5∶1组成;其中组份A是由涤纶树脂18份、膨润土0.5份、硫酸锌5份、石粉25份、200#溶剂油5份、烧焦沥青液60份制备而成,所述组份B为聚酰胺。本发明中的涤纶树脂是由废弃物废涤纶块与混合脂肪酸等作为原料制备的,涤纶料取代了大量的化工原料,如甘油,减少了环境污染,并减少了生产成本。既发挥了涤纶树脂优异的成膜性能和防腐蚀性能,又较好地解决了沥青材料高温流淌、低温冷脆等难题,同时提高了涂料的防锈与防腐蚀性能。
Description
技术领域
本发明涉及涂料化工技术领域,具体涉及一种涤纶树脂沥青涂料。
背景技术
涤纶是合成纤维中的一个重要品种,是以精对苯二甲酸(PTA)或对苯二甲酸二甲酯(DMT)和乙二醇(EG)为原料经酯化或酯交换和缩聚反应而制得的成纤高聚物——聚对苯二甲酸乙二醇酯(PET)。涤纶的用途很多,从而产生了大废涤纶,由于工业上废涤纶块难以降解,只能用深埋方式进行处理。以废涤纶块在高温下醇解,继而与树脂合成物进行聚合反应,对醇酸树脂进行改性。涤纶在醇溶液中,经过高温加热可发生分解反应,分解为对苯二甲酸酐和乙二醇。具体反应为:
为了提高废涤纶的使用价格,目前人们废涤纶用来做为油漆的基料,如中国专利申请200710022171.4 公开了一种加水稀释型调和漆基料及其制备方法,其基料主要由废涤纶油酸、苯酐、季戊四醇份和松香组成,其中油酸占总原料的重量比可达12.5-80%,油酸使用的量较大,加大了生产的成本。
另外,中国专利申请200610076881.0 公开了一种利用废弃物生产油漆的技术工艺,是将废旧聚酯农药瓶、地沟油、废聚酯粉末、溶剂油和添加剂一同反应制成,但制得的油漆产品效果差,达不到使用的目的。
发明内容
本发明的目的就是要提供一种成本低且能防锈、防腐的涤纶树脂沥青涂料。
为了达到上述目的,本发明提供一种涤纶树脂沥青涂料,其特征在于:由组份A和组份B按重量比为5:1组成;其中组份A是由下列组份按重量份制备而成:
所述组份B为聚酰胺。
进一步,所述组份A是由下列组份按重量份制备而成:
进一步,所述聚酰胺为750低分子聚酰胺。
进一步,所述溶剂为200#溶剂油。
更进一步,所述涤纶树脂是由下列组份按重量份制备而成:
混合脂肪酸20-25份;
马来酸酐0-2份;
废涤纶块20-30份;
季戊四醇 4-5份;
甘油0-2份;
催化剂0-0.1份。
更进一步,所述催化剂为氢氧化锂或醋酸铅。
本发明的涤纶树脂沥青涂料的制备方法是先按配方加入各组份于反应釜中进行搅拌混合、研磨制备出组份A,再按组份A和组份B的重量比为5:1的比例进行搅拌混合、静置过滤即得涤纶树脂沥青涂料。
本发明中的涤纶树脂是由废弃物废涤纶块与混合脂肪酸等作为原料制备的,涤纶料取代了大量的化工原料,如甘油、季戊四醇、邻苯二甲酸酐、顺丁烯二酸酐,其原理是涤纶(化学名称是聚对苯二甲酸乙二醇酯)经过降解后生成对苯二甲酸和乙二醇,对苯二甲酸代替邻苯二甲酸酐和顺丁烯二酸酐,乙二醇代替季戊四醇和甘油。减少了环境污染,并减少了生产成本。
本发明将涤纶树脂与煤焦沥青相结合,既发挥了涤纶树脂优异的成膜性能和防腐蚀性能,又较好地解决了沥青材料高温流淌、低温冷脆等难题。采用价格低廉的涤纶树脂和价格低廉、施工方便的煤焦沥青配制成的涂料结合了二者的优点,提高了涂料的防腐蚀性能。
具体实施方式
下面结合实施例对本发明做进一步的阐述。
实施例一:
涤纶树脂的制备:将混合脂肪酸20份、废涤纶块30份、季戊四醇5份、甘油1份、氢氧化锂0.1份放入反应釜中,升温至260℃进行搅拌混合,保温处理两小时;
组份A的制备:将制备的涤纶树脂18 份、膨润土0.5份、硫酸锌5 份、石粉25份、200#溶剂油5份、烧焦沥青液60份;置于反应釜中升温至85℃进行搅拌混合,保温处理两小时;
将前面制备的组份A和组份B按重量比为5:1进行搅拌混合、静置过滤即得涤纶树脂沥青涂料。
实施例二:
涤纶树脂的制备:将混合脂肪酸25份、马来酸酐2份、废涤纶块20份、季戊四醇 4份放入反应釜中,升温至270℃进行搅拌混合,保温处理两小时;
组份A的制备:将制备的涤纶树脂25 份、膨润土1份、硫酸锌4份、石粉15份、200#溶剂油10 份、烧焦沥青液45份;置于反应釜中升温至85℃进行搅拌混合,保温处理两小时;
将前面制备的组份A和组份B按重量比为5:1进行搅拌混合、静置过滤即得涤纶树脂沥青涂料。
实施例三:
涤纶树脂的制备:将混合脂肪酸20份、马来酸酐1份、废涤纶块25份、季戊四醇 4.5份、甘油1份、醋酸铅0.1份放入反应釜中,升温至280℃进行搅拌混合,保温处理两小时;
组份A的制备:将制备的涤纶树脂20份、膨润土0.8份、硫酸锌4.5 份、石粉19份、200#溶剂油7份、烧焦沥青液49份;置于反应釜中升温至85℃进行搅拌混合,保温处理两小时;
将前面制备的组份A和组份B按重量比为5:1进行搅拌混合、静置过滤即得涤纶树脂沥青涂料。
实施例四
涤纶树脂的制备:将混合脂肪酸22份、马来酸酐1份、废涤纶块20-30份、季戊四醇5份、甘油2份、氢氧化锂0.01份放入反应釜中,升温至280℃进行搅拌混合,保温处理两小时;
组份A的制备:将制备的涤纶树脂18份、膨润土1份、硫酸锌4份、石粉25份、200#溶剂油5份、烧焦沥青液45份;置于反应釜中升温至85℃进行搅拌混合,保温处理两小时;
将前面制备的组份A和组份B按重量比为5:1进行搅拌混合、静置过滤即得涤纶树脂沥青涂料。
上面所述仅仅是对本发明的优选实施方式进行描述,并非对本发明的范围进行限定,在不脱离本发明设计精神前提下,本领域普通工程技术人员对本发明技术方案做出的各种变形和改进,均应落入本发明的权利要求书确定的保护范围内。
Claims (6)
1.一种涤纶树脂沥青涂料,其特征在于:由组份A和组份B按重量比为5:1组成;其中组份A是由下列组份按重量份制备而成:
所述组份B为聚酰胺。
3.根据权利要求1所述的涤纶树脂沥青涂料,其特征在于:所述聚酰胺为750低分子聚酰胺。
4.根据权利要求1或2所述的涤纶树脂沥青涂料,其特征在于:所述溶剂为200#溶剂油。
5.根据权利要求1或2所述的涤纶树脂沥青涂料,其特征在于:所述涤纶树脂是由下列组份按重量份制备而成:
混合脂肪酸20-25份;
马来酸酐0-2份;
废涤纶块20-30份;
季戊四醇 4-5份;
甘油0-2份;
催化剂0-0.1份。
6.根据权利要求5所述的涤纶树脂沥青涂料,其特征在于:所述催化剂为氢氧化锂或醋酸铅。