CN103334176A - 一种蓄能型长余辉发光纤维 - Google Patents

一种蓄能型长余辉发光纤维 Download PDF

Info

Publication number
CN103334176A
CN103334176A CN2013102928299A CN201310292829A CN103334176A CN 103334176 A CN103334176 A CN 103334176A CN 2013102928299 A CN2013102928299 A CN 2013102928299A CN 201310292829 A CN201310292829 A CN 201310292829A CN 103334176 A CN103334176 A CN 103334176A
Authority
CN
China
Prior art keywords
luminescent
energy
fiber
type long
storing type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102928299A
Other languages
English (en)
Inventor
原田士郎
许忠
王加相
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lumica Special Fiber (lianyungang) Co Ltd
Original Assignee
Lumica Special Fiber (lianyungang) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lumica Special Fiber (lianyungang) Co Ltd filed Critical Lumica Special Fiber (lianyungang) Co Ltd
Priority to CN2013102928299A priority Critical patent/CN103334176A/zh
Publication of CN103334176A publication Critical patent/CN103334176A/zh
Pending legal-status Critical Current

Abstract

本发明是一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy发光粉体1-15％；聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种0-5%；其余为聚对苯二甲酸乙二醇酯，补齐100%。本发明配方合理，它因是把蓄光材料混合配置在内部的复合纺纱，所以对使用的针不会产生划痕，克服并解决了单纯纺纱的缺陷。其发光纤维发光效果好、发光性能稳定，具有高强度发光性能。可以用来制作毛毯、毛布、地毯、窗帘等生活用品，也可以用来制作缆绳、手套、袜子等日常用品，还可以用于制作衣物、玩具、刺绣或者其它特殊用途。

Description

一种蓄能型长余辉发光纤维
技术领域
本发明涉及一种纤维，特别是一种蓄能型长余辉发光纤维。
背景技术
发光纤维是指受光或放射线照射能发出比照射光波长更长的可见光的纤维。现有技术中常见的发光纤维有：（1）在低折射玻璃中空纤维内充以高折射率的液态发光材料；（2）以发光玻璃作芯材的纤维；（3）以发光塑料作芯材的纤维。现有技术中的发光纤维主要存在着发光时间短，制作复杂，发光效果不稳定等缺点。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种配方合理、发光效果好、发光性能稳定的蓄能型长余辉发光纤维。
本发明所要解决的技术问题是通过以下的技术方案来实现的。本发明是一种蓄能型长余辉发光纤维，其特点是，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体母粒    1-15％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种0-5%；
其余为聚对苯二甲酸乙二醇酯，补齐100%。
本发明所述的蓄能型长余辉发光纤维中：聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯为可选材料，可以为零，当选用其中的一种或几种时，其含量或者混合含量占原料总量为0.5-5%。
本发明所述的蓄能型长余辉发光纤维，各原料的重量百分比优选为：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    8-12％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种2-3%；
其余为聚对苯二甲酸乙二醇酯，补齐100%。
本发明所述的蓄能型长余辉发光纤维，最优选的各原料的重量百分比为：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体     10％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种2%；
聚对苯二甲酸乙二醇酯  88%。
本发明所述的蓄能型长余辉发光纤维，另一最优选的各原料的重量百分比为：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体母粒   10％；
聚对苯二甲酸乙二醇酯  90%。
本发明所述的蓄能型长余辉发光纤维中，各原料均优选为粉状，且其粒径均不大于10微米。
与现有技术相比，本发明蓄能型长余辉发光纤维具有以下优点：
1．本发明蓄能型长余辉发光纤维配方合理，它因是把蓄光材料混合配置在内部的复合纺纱，所以对使用的针不会产生划痕，克服并解决了单纯纺纱的缺陷。
2．本发明蓄能型长余辉发光纤维发光效果好、发光性能稳定；它在日光下照射5分钟，或者在荧光下照射15分钟，即可发光5小时左右，具有高强度发光性能。本发明蓄能型长余辉发光纤维可以用来制作毛毯、毛布、地毯、窗帘等生活用品，也可以用来制作缆绳、手套、袜子等日常用品，还可以用于制作衣物、玩具、刺绣或者其它特殊用途。
附图说明
图1为本发明蓄能型长余辉发光纤维的一种余辉亮度曲线图。
具体实施方式
以下进一步描述本发明的具体技术方案，以便于本领域的技术人员进一步地理解本发明，而不构成对其权利的限制。
实施例1，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    1％；
聚对苯二甲酸乙二醇酯 99%。
实施例2，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    15％；
聚对苯二甲酸乙二醇酯  85%。
实施例3，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    1％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种0.5%；
聚对苯二甲酸乙二醇酯  98.5%。
实施例4，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    15％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种  5%；
聚对苯二甲酸乙二醇酯  80%。
实施例5，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    8％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种2%；
聚对苯二甲酸乙二醇酯  90%。
实施例6，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体    12％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种  3%；
聚对苯二甲酸乙二醇酯  85%。
实施例7，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体     10％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种2%；
聚对苯二甲酸乙二醇酯  88%。
实施例8，一种蓄能型长余辉发光纤维，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy 发光粉体     10％；
聚对苯二甲酸丁二酯   2%；
聚对苯二甲酸乙二醇酯  88%。
以下是发明人做的用本实施例的蓄能型长余辉发光纤维做余辉实验及其结果。照射条件为：常用光源D65，1000lux，照射时间为30分钟，结果参照图1。该蓄能型长余辉发光纤维达到亮度3 mcd/m2的时间为7小时左右，达到亮度0.3 mcd/m2的时间为15小时左右，从本发明蓄能型长余辉发光纤维的余辉实验可以看出本发明蓄能型长余辉发光纤维的高强度发光性能。
实施例9，实施例1-8任何一项所述的蓄能型长余辉发光纤维中：各原料均为粉状，且其粒径均不大于10微米。

Claims (6)

1.一种蓄能型长余辉发光纤维，其特征在于，该纤维由以下重量百分比的原料混合均匀制成发光纤维母粒后再进行熔融纺丝制成：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体母粒    1-15％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种0-5%；
其余为聚对苯二甲酸乙二醇酯，补齐100%。
2.根据权利要求1所述的蓄能型长余辉发光纤维，其特征在于，原料聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种占原料总量的0.5-5%。
3.根据权利要求1所述的蓄能型长余辉发光纤维，其特征在于，各原料的重量百分比为：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体母粒    8-12％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种2-3%；
其余为聚对苯二甲酸乙二醇酯，补齐100%。
4.根据权利要求1所述的蓄能型长余辉发光纤维，其特征在于，各原料的重量百分比为：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体母粒     10％；
聚对苯二甲酸丁二酯、聚酰胺、聚丙烯、聚乙烯中的一种或几种2%；
聚对苯二甲酸乙二醇酯  88%。
5.根据权利要求1所述的蓄能型长余辉发光纤维，其特征在于，各原料的重量百分比为：
SrAl2O4:Eu.Dy或Sr4Al14O25:Eu.Dy 发光粉体母粒     10％；
   聚对苯二甲酸乙二醇酯  90%。
6.根据权利要求1或2或3所述的蓄能型长余辉发光纤维，其特征在于：各原料均为粉状，且其粒径均不大于10微米。
CN2013102928299A 2013-07-12 2013-07-12 一种蓄能型长余辉发光纤维 Pending CN103334176A (zh)