CN103333598A - 一种具有高硬度、高光泽木器用亮光白面漆 - Google Patents
一种具有高硬度、高光泽木器用亮光白面漆 Download PDFInfo
- Publication number
- CN103333598A CN103333598A CN2013102647350A CN201310264735A CN103333598A CN 103333598 A CN103333598 A CN 103333598A CN 2013102647350 A CN2013102647350 A CN 2013102647350A CN 201310264735 A CN201310264735 A CN 201310264735A CN 103333598 A CN103333598 A CN 103333598A
- Authority
- CN
- China
- Prior art keywords
- component
- finish paint
- weight percentage
- light white
- white finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明是使用聚酯树脂DP315加上进口钛白粉等配成亮光白面漆为甲组分,将正丁酯、HX-90B等配制成乙组分,以正丁酯、丙二醇甲醚醋酸酯、碳酸二甲酯、EGDA和二甲苯配制成施工时的稀释剂等配成丙组分,将甲、乙、丙组分混合配制成具有高硬度、高光泽木器用亮光白面漆。本发明的亮光白面漆,经检测和试用证明,其涂层附着力强、柔韧性好、硬度高、遮盖力好、光泽高、耐黄变,施工时流平性好,能显著提高亮光白面漆长期使用时的耐磨耐划性能。
Description
技术领域
本发明涉及一种具有高硬度、高光泽木器用亮光白面漆,属于涂料制造业。
背景技术
PU亮光白面漆是一种综合性能优良的木器涂料,广泛用于木器装饰,常规配漆施工后,因普通醇酸树脂自身特性,交联度无法设计太高,硬度上升不了太高,柔韧性也会随着硬度上升而变差,随着时间的推移,漆膜容易出现掉漆、失光、失色、发暗等弊病。众所周知,聚酯树酯羟基含量高、与异氰酸酯反应交联度可做到较高,同时柔韧性也可以同时兼顾到,金红石型钛白粉是白度非常好的一种材料,而HX-90B固化剂也是耐黄变性能优异的一种材料,当这几种材料配合在一起,就生产出本发明的一种具有高硬度、高光泽木器用聚酯-聚氨酯亮光白面漆。
发明内容
本发明的目的是:提供一种具有高硬度、高光泽、耐黄变木器用亮光白面漆,迎合当今人们对涂装要求不断提高的需求。
本发明解决技术问题采用的技术方案是:一种具有高硬度、高光泽木器用亮光白面漆,涂装时甲、乙、丙组分重量比为1:(0.8~1):(0.4~0.6)。
1)50%钛白浆的制备:
其中分两次加入二甲苯,每次加入1%,分散均匀,砂磨至细度≤20um,粘度为10000~20000mPa.s(25℃);
2)甲组分的配比(重量):
3)乙组分的配比(重量):
其中醋酸正丁酯为氨酯级溶剂,HX-90、L-75、1451物料的游离HDI、游离TDI≤0.5%。
4)丙组分的配比(重量):
所述甲组分的制备包括以下步骤:
选用干净符合标准的分散缸,依次按上述重量百分含量投入50%钛白浆、聚酯树脂DP315、分散剂(BYK-110)、流平剂(EFKA-3777)、流平剂(BYK-333)、消泡剂(BYK-141)、丙二醇甲醚醋酸酯,启动分散机,低速(600~800RPM)分散均匀后,高速(1200~1500RPM)分散10~15min,至细度≤20um,用醋酸正丁酯调节粘度至1500~2500mPa.s(25℃),制得甲组分。
所述乙组分的制备包括以下步骤:
1、加入醋酸正丁酯到兑稀釜,90℃真空脱水约30min至脱水完全。
2、加入HX-90、L-75、1451物料,开启搅拌机搅拌1小时,搅拌均匀后,压滤并转入储罐待用。
所述丙组分的制备包括以下步骤:
1、按上述丙组分的配比依次投料;
2、以400RPM分散5分钟,充分搅拌均匀,待用。
甲、乙和丙三个组分按1:(0.8~1):(0.4~0.6)的重量配比混合,制得本发明的具有高硬度、高光泽木器用亮光白面漆。
本发明相对于现有技术的有益效果是:本发明的高硬度、高光泽亮光白面漆,经检测和试用证明,其涂层的遮盖力好、附着力强、硬度高、光泽高、耐高温、耐黄变、耐水、耐化学性好、柔韧性好;施工时流平好、易喷涂,特别是在硬度、光泽高性能方面,有优异的效果。
具体实施方式
实施例1
一种具有高硬度、高光泽木器用亮光白面漆,包含甲、乙丙三种组分,其中,
1)甲组分生产重量配比:
2)乙组分的重量配比:
其中醋酸正丁酯为氨酯级溶剂,HX-90、L-75、1451物料的游离HDI、游离TDI≤0.5%。
3)丙组分的重量配比:
所述甲组分的制备包括以下步骤:
选用干净符合标准的分散缸,依次投入50%钛白浆50Kg、聚酯树脂DP31545Kg、分散剂(BYK-110)0.6Kg、流平剂(EFKA-3777)1Kg、流平剂(BYK-333)0.3Kg、消泡剂(BYK-141)0.6Kg、丙二醇甲醚醋酸酯2Kg,启动分散机,低速(600~800RPM)分散均匀后,高速(1200~1500RPM)分散10~15min,至细度≤20um,用醋酸正丁酯0.5Kg调节粘度至1500~2500mPa.s(25℃),制得甲组分。所述乙组分的制备包括以下步骤:
1、加入醋酸正丁酯到兑稀釜,90℃真空脱水约30min至脱水完全。
2、加入HX-90、L-75、1451物料,开启搅拌机搅拌1小时,搅拌均匀后,压滤并转入储罐待用。
所述丙组分的制备包括以下步骤:
1、按上述丙组分的重量配比依次投料;
2、以400RPM分散5分钟,充分搅拌均匀,待用。
甲、乙和丙三个组分按1:0.8:0.4的重量配比混合制得本发明的具有高硬度、高光泽木器用亮光白面漆。
实施例2
一种具有高硬度、高光泽木器用亮光白面漆,包含甲、乙丙三种组分,其中,
1)甲组分生产重量配比::
2)乙组分的重量配比:
其中醋酸正丁酯为氨酯级溶剂,HX-90、L-75、1451物料的游离HDI、游离TDI≤0.5%。
3)丙组分的重量配比:
所述甲组分的制备包括以下步骤:
选用干净符合标准的分散缸,依次投入FC95(50%钛白浆)65Kg、聚酯树脂DP31530.2Kg、分散剂(BYK-110)1Kg、流平剂(EFKA-3777)0.5Kg、流平剂(BYK-333)0.1Kg、消泡剂(BYK-141)0.2Kg、丙二醇甲醚醋酸酯2Kg,启动分散机,低速(600~800RPM)分散均匀后,高速(1200~1500RPM)分散10~15min,至细度≤20um,用醋酸正丁酯1Kg调节粘度至1500~2500mPa.s(25℃),制得甲组分。
所述乙组分的制备包括以下步骤:
1、加入醋酸正丁酯到兑稀釜,90℃真空脱水约30min至脱水完全。
2、加入HX-90、L-75、1451物料,开启搅拌机搅拌1小时,搅拌均匀后,压滤并转入储罐待用。
所述丙组分的制备包括以下步骤:
1、按上述丙组分的重量配比依次投料;
2、以400RPM分散5分钟,充分搅拌均匀,待用。
甲、乙和丙三个组分按1:1:0.6的重量配比混合,制得本发明的具有高硬度、高光泽木器用亮光白面漆。
本发明高硬度、高光泽聚酯-聚氨酯亮光白面漆的各性能指标如下:
本发明的白面漆与市面上购回的白面漆的性能比较,见下表:
检测方法:性能指标可参照GB/T23997-2009,有害物质限量参照GB18581-2009。
由以上数据可知,本发明白面漆是一种硬度高、光泽高的装修用亮光白面漆,硬度高、光泽高等特点是一些需要耐划耐磨耐黄变色漆装修的首选。
Claims (6)
1. 一种具有高硬度、高光泽木器用亮光白面漆,包括甲、乙和丙三种组分,其中,
甲组分的组成和重量百分含量为:
50%钛白浆 50%~65%
聚酯树脂DP315 30%~45%
分散剂 BYK-110 0.6%~1%
流平剂 EFKA-3777 0.5%~1 %
流平剂 BYK-333 0.1%~0.3%
消泡剂 BYK-141 0.2%~0.6%
丙二醇甲醚醋酸酯 2%
醋酸正丁酯 0.5%~1%;
其中50%钛白浆的组成和重量百分含量为:
聚酯树脂DP315 46%
分散剂 1%
钛白粉R706或595 50%
丙二醇甲醚醋酸酯 1%
二甲苯 2%;
乙组分的组成和重量百分含量为:
脱水醋酸正丁酯 23%~37%
固化剂HX-90B 8%~12%
固化剂L-75 40%~45%
固化剂1451 15%~20%;
丙组分的组成和重量百分含量为:
二甲苯 40%~45%
醋酸正丁酯 12%~15%
丙二醇甲醚醋酸酯 29%~25%
碳酸二甲酯 12%~16%
乙二醇二乙酸酯 2%~4%。
2. 根据权利要求1所述的木器用亮光白面漆,其特征在于,甲、乙、丙组分的重量配比为1:(0.8~1):(0.4~0.6)。
3. 根据权利要求1或2所述的木器用亮光白面漆,其特征在于,50%钛白浆分散均匀,其细度≤ 20 um,其粘度在25℃时为10000~20000 mPa.s。
4. 根据权利要求1或2所述的木器用亮光白面漆,其特征在于,甲组分分散均匀,其细度≤ 20 um,其粘度在25℃时为1500~2500 mPa.s。
5. 根据权利要求1或2所述的木器用亮光白面漆,其特征在于,所述乙组分的醋酸正丁酯为氨酯级溶剂,HX-90、L-75、1451物料的游离HDI、游离TDI≤0.5%。
6. 一种制备根据权利要求1所述的木器用亮光白面漆的方法,包括如下步骤:
(1)所述甲组分的制备包括以下步骤:选用符合清洁标准的分散缸,按权利要求1所述的重量百分含量依次投入50%钛白浆、聚酯树脂DP315、分散剂BYK-110、流平剂EFKA-3777、流平剂BYK-333、消泡剂BYK-141、丙二醇甲醚醋酸酯,启动分散机,以600~800 RPM的转速分散均匀后,再以1200~1500 RPM的转速分散10~15 min,至细度≤ 20 um, 用醋酸正丁酯调节粘度,使其在25℃为1500~2500 mPa.s,制得甲组分;
(2)所述乙组分的制备包括以下步骤:
a)、按权利要求1所述的重量百分含量加入醋酸正丁酯到兑稀釜,90℃真空脱水约30min至脱水完全;
b)、按权利要求1所述的重量百分含量加入HX-90、L-75、1451物料,开启搅拌机搅拌1小时,搅拌均匀后,压滤并转入储罐待用;
(3)所述丙组分的制备包括以下步骤:
a)、按权利要求1所述的组分和重量百分含量依次投料;
b)、以400 RPM的转速分散5分钟,充分搅拌均匀,待用;
(4)将甲组分、乙组分和丙组分按1:(0.8~1):(0.4~0.6)的重量配比混合均匀,制得本发明的具有高硬度、高光泽木器用亮光白面漆。