CN103333589A - Water-based glaze paint - Google Patents
Water-based glaze paint Download PDFInfo
- Publication number
- CN103333589A CN103333589A CN2013102160195A CN201310216019A CN103333589A CN 103333589 A CN103333589 A CN 103333589A CN 2013102160195 A CN2013102160195 A CN 2013102160195A CN 201310216019 A CN201310216019 A CN 201310216019A CN 103333589 A CN103333589 A CN 103333589A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- water
- component
- agent
- tensio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based glaze paint. The water-based glaze paint is easy to operate, meets the requirement of environmental protection and achieves goals of environmental protection, good durability, energy conservation and emission reduction. The water-based glaze paint comprises component A and component B. The component A and the component B are mixed according to the mass ratio of 1:4-8, and stirred evenly. Paint films have the same glaze texture as tiles, and is easy to wipe and wash like glass. The glaze paint has advantages of strong adhesive force, high surface hardness and good chemical resistance. The glaze paint is water-based and environmentally friendly, and have good resistance to graffiti, good resistance to chemical corrosion, mildew-proofing, anti-microbial, anti-algae, good resistance to ageing in outdoors, good resistance to staining and good self-cleaning property.
Description
Technical field
The present invention relates to the wall paint technical field, be specifically related to a kind of water-based glaze finish paint.
Background technology
At present, common decorative material for wall surface has coating, wall brick, stone material, sheet material, glass etc., and wherein coating is as a kind of indispensable protective and decorative material in the building decoration, and technology is constantly progressive, and performance continues to promote, and uses very extensive.In building decoration, abandon coating, will roll up construction cost, waste natural resources, run counter to the theory of low-carbon economy.
Coating has emulsion paint, texture lacquer, fluorine carbon lacquer etc., and performance has his own strong points, the application choice difference.The advantage of emulsion paint is cheap, and decorative effect is arranged, and the engineering comprehensive cost is low, and shortcoming is that didirtresistance is poor, and the spot that mildews easily is not corrosion-resistant, and work-ing life is short, can only recoat after the several years.The advantage of texture lacquer is that the molding surface kind is more, and shortcoming is bad contamination-proof capability, sticking dust easily, and the rainwater self-cleaning is poor, stay rainprint, corrosion-resistant easily, and the surface can't clean, can't recoat.The advantage of fluorine carbon lacquer is that outdoor ageing resistance is good, and shortcoming is not environmental protection, poor adhesive force, and the ambient cure hardness of paint film is low, and the application metope chaps easily.
Water-based glaze finish paint adopts advanced watersoluble modified resin technology, uses unique production process, has obtained a kind of coating of high comprehensive performance.Water-based glaze finish paint possesses aqueous, environmental protective simultaneously, strong adhesion, the surface hardness height, anti-graffiti property is good, non-corrosibility is good, antimildew and antibacterial is good, good these the important performances of good, the anti-outdoor aging of resistant self-cleaning, coating performance can compare favourably with the ceramic tile glaze, is most important feature of the present invention, and the present invention has promoted the technical progress of a branch of coating.
Summary of the invention
In order to solve the deficiencies in the prior art, the invention provides a kind of water-based glaze finish paint.
Technical scheme of the present invention is: a kind of water-based glaze finish paint, comprise component A and component B, and the mass ratio 1:4-8 that presses of described component A and component B mixes, and stirs namely.
The further improvement of the present invention feature comprises:
Described component B comprises by mass parts: water-based amine hardener 30.00-48.00 mass parts, deionized water 24.00-38.00 mass parts, dispersion agent 0.20-0.40 mass parts, thinner 1.00-5.00 mass parts, thixotropic agent 0.20-0.60 mass parts, pigment extender 22.00-28.00 mass parts, flow agent 0.40-1.00 mass parts, tensio-active agent 0.10-0.5050 mass parts.
Described component B comprises by mass parts: water-based amine hardener 39.00-36.00 mass parts, deionized water 28.00-36.00 mass parts, dispersion agent 0.20-0.3 mass parts, thinner 1.02.00-5.00 mass parts, thixotropic agent 0.20-0.40 mass parts, pigment extender 25.00-26.00 mass parts, flow agent 0.20-0.30 mass parts, tensio-active agent 0.20-0.40 mass parts part.
Described component B comprises by mass parts: water-based amine hardener 45.00 mass parts, deionized water 28.00 mass parts, dispersion agent 0.40 mass parts, thinner 2.80 mass parts, thixotropic agent 0.30 mass parts, pigment extender 22.80 mass parts, flow agent 0.40 mass parts, tensio-active agent 0.40 mass parts.
Described component A comprises by mass parts: acrylic acid epoxy resin 62.00-92.00 mass parts, thinner 0-10.00 mass parts, tensio-active agent 1.00-10.00 mass parts, catalyzer 2.00-7.00, emulsifying agent 5.00-16.00 mass parts.
Described component A comprises by mass parts: acrylic acid epoxy resin 74.00-80.00 mass parts, thinner 3.00-9.00 mass parts, tensio-active agent 3.00-7.00 mass parts, catalyzer 3.00-6.00, emulsifying agent 7.00-12.00 mass parts.
Described component A comprises by mass parts: acrylic acid epoxy resin 78.00 mass parts, thinner 8.00 mass parts, tensio-active agent 5.00 mass parts, promotor 10.00 mass parts.
Another object of the present invention is to provide the preparation method of a kind of described component B, may further comprise the steps:
Step 1, successively add water-based amine hardener, deionized water, dispersion agent, thinner, thixotropic agent after, middling speed 800rpm disperseed 15-30 minute;
Step 2, again add pigment extender after, high speed 1200rpm disperseed 35-50 minute;
Step 3, at last add flow agent and tensio-active agent successively after, middling speed 800rpm disperseed 8-20 minute.
Another object of the present invention also is to provide the preparation method of a kind of described component A, may further comprise the steps:
Step 1, successively add acrylic acid epoxy resin, emulsifying agent, catalyzer, tensio-active agent after, low speed 500rpm disperses;
Step 2, be warming up to 80 ° of C, be incubated 6 hours;
Step 3, stopped reaction are cooled to room temperature;
Step 4 adds thinner middling speed 800rpm and disperses 8-20 minute namely.
The invention has the beneficial effects as follows: the present invention has solved the contradiction between the aqueous, environmental protective of coating and physicals, chemical property, mechanical property, the ageing-resistant performance effectively.In building decoration and industrial protection, often need between multiple coating, select combination, evade shortcoming, make the most of the advantage, allow and select the difficulty that becomes, also can produce the problem that some practice of construction are used.The advantage of the comprehensive multiple coating of the present invention, aqueous, environmental protective, performance are comprehensive, easy to use, in a lot of practical applications, select a kind of coating of water-based glaze finish paint just can satisfy the requirement of multiple functions of use.The present invention is widely used for interior wall, decoration of exterior wall lacquer; reduced materials such as using the big wall brick of consumption of natural resource amount, sheet material, stone material, glass in the building decoration; be used for antifouling paste, antimicrobial paint, prolonged by the work-ing life of protection object, protection personnel safety health.For today that energy worsening shortages, environmental pollution worsen, the present invention has reached environmental protection, energy-conservation, the purpose that reduces discharging.
The over-all properties technical indicator of water-based glaze finish paint
The environmental-protecting performance index: coating type is water-base resin lacquer, two-pack, reaction-curable; VOC 8g/L; Benzene is comprehensive, free formaldehyde does not detect.
Physical performance index: 0 grade of sticking power; Surface hardness 2H, scratch resistance; Wear resistance 30mg resistance to wears; Snappiness 1mm; Antifouling property, the blank person's handwriting, one wipes namely only.
The chemical property index: water tolerance (water, 168 hours), non-foaming, do not peel off, do not have variable color; Oil-proofness (120# industrial naptha, 72 hours), non-foaming, do not peel off, do not have variable color; Alkali resistance (20% caustic soda, 72 hours), non-foaming, do not peel off, do not have variable color; Acid resistance (10% sulfuric acid, 48 hours), non-foaming, do not peel off, do not have variable color.
Outdoor performance index: resistant self-cleaning, 1%; The 806h of anti-the artificial accelerated aging, non-foaming, do not peel off, flawless.
Fungicidal properties index: 1 grade of mildew grade.
The antiseptic property index: salt fog resistance (700 hours), no abnormal.Salt tolerant deionization water-based (3% sodium-chlor, 168 hours), no abnormal.
Annotate: technical data test basis standard GB 18582-2008, GB/T22374-2008, GB/T9755-2001, GB/T1741-2007, JG/T224-2007.
Embodiment
Embodiment 1
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:4-8 that presses of described component A and component B mixes, and stirs namely.Described component B comprises by mass parts: water-based amine hardener 30.00-48.00 mass parts, deionized water 24.00-38.00 mass parts, dispersion agent 0.2-0.8 mass parts, thinner 1.00-5.00 mass parts, thixotropic agent 0.20-0.60 mass parts, pigment extender 22.00-28.00 mass parts, flow agent 0.40-1.00 mass parts, tensio-active agent 0.10-0.50 mass parts.Described component A comprises by mass parts: acrylic acid epoxy resin 62.00-92.00 mass parts, thinner 0-10.00 mass parts, tensio-active agent 1.00-5.00 mass parts, catalyzer 2.00-7.00 mass parts.
The preparation method of above-mentioned component B may further comprise the steps:
Step 1, successively add water-based amine hardener, deionized water, dispersion agent, thinner, thixotropic agent after, middling speed 800rpm disperseed 15-30 minute;
Step 2, again add pigment extender after, high speed 1200rpm disperseed 35-50 minute;
Step 3, at last add flow agent and tensio-active agent successively after, middling speed 800rpm disperseed 8-20 minute.
The preparation method of above-mentioned component A may further comprise the steps:
Step 1, successively add acrylic acid epoxy resin, emulsifying agent, catalyzer, tensio-active agent after, low speed 500rpm disperses;
Step 2, be warming up to 80 ° of C, be incubated 6 hours;
Step 3, stopped reaction are cooled to room temperature;
Step 4 adds thinner middling speed 800rpm and disperses 8-20 minute namely.
Embodiment 2
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:4 that presses of described component A and component B mixes, and stirs namely.Described component B comprises by mass parts: water-based amine hardener 48.00 mass parts, deionized water 24.00 mass parts, dispersion agent 0.30 mass parts, thinner 5.00 mass parts, thixotropic agent 0.20 mass parts, pigment extender 22.00 mass parts, flow agent 0.40 mass parts, tensio-active agent 0.1 mass parts.Described component A comprises by mass parts: acrylic acid epoxy resin 92.00 mass parts, emulsifying agent 5.00 mass parts, thinner 0 mass parts, tensio-active agent 1.00 mass parts, catalysis 24.00 mass parts.
The preparation method of above-mentioned component B, A is with embodiment 1.
Embodiment 3
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:8 that presses of described component A and component B mixes, and stirs namely.Described component B comprises by mass parts: water-based amine hardener 30.00 mass parts, deionized water 38.00 mass parts, dispersion agent 0.20 mass parts, thinner 2.40 mass parts, thixotropic agent 0.60 mass parts, pigment extender 28.00 mass parts, flow agent 0.30 mass parts, tensio-active agent 0.50 mass parts.Described component A comprises by mass parts: acrylic acid epoxy resin 62.00 mass parts, emulsifying agent 12.00 mass parts, thinner 10.00 mass parts, tensio-active agent 5.00 mass parts, catalyzer 7.00 mass parts.
The preparation method of above-mentioned component B, A is with embodiment 1.
Embodiment 4
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:5 that presses of described component A and component B mixes, and stirs namely.Described component B comprises by mass parts: water-based amine hardener 40.00 mass parts, deionized water 32.00 mass parts, dispersion agent 0.40 mass parts, thinner 3.20 mass parts, thixotropic agent 0.20 mass parts, pigment extender 26.00 mass parts, flow agent 0.20 mass parts, tensio-active agent 0.20 mass parts.Described component A comprises by mass parts: acrylic acid epoxy resin 84.00 mass parts, emulsifying agent 6.00 mass parts, thinner 4.00 mass parts, tensio-active agent 2.00 mass parts, catalyzer agent 4.00 mass parts.
The preparation method of above-mentioned component B, A is with embodiment 1.
Embodiment 5
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:6 that presses of described component A and component B mixes, and stirs namely.Described component B comprises by mass parts: water-based amine hardener 44.00 mass parts, deionized water 28.00 mass parts, dispersion agent 0.20 mass parts, thinner 2.80 mass parts, thixotropic agent 0.20 mass parts, pigment extender 24.00 mass parts, flow agent 0.40 mass parts, tensio-active agent 0.40 mass parts.Described component A comprises by mass parts: acrylic acid epoxy resin 74.00 mass parts, emulsifying agent 11.00 mass parts, thinner 10.00 mass parts, tensio-active agent 3.00 mass parts, catalyzer 2.00 mass parts.
The preparation method of above-mentioned component B, A is with embodiment 1.
Embodiment 6
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:7 that presses of described component A and component B mixes, and stirs namely.Described component B comprises by mass parts: water-based amine hardener 36.00 mass parts, deionized water 36.00 mass parts, dispersion agent 0.20 mass parts, thinner 2.00 mass parts, thixotropic agent 0.40 mass parts, pigment extender 25.00 mass parts, flow agent 0.20 mass parts, tensio-active agent 0.20 mass parts.Described component A comprises by mass parts: acrylic acid epoxy resin 68.00 mass parts, emulsifying agent 13 mass parts, thinner 8.00 mass parts, tensio-active agent 5.00 mass parts, catalyzer 6.00 mass parts.
The preparation method of above-mentioned component B, A is with embodiment 1.
Embodiment 7
A kind of water-based glaze finish paint comprises component A and component B, and the mass ratio 1:4 that presses of described component A and component B mixes, and stirs namely.Described component B comprises: water-based amine hardener 28.00kg, deionized water 28.00kg, dispersion agent 0.8kg, thinner 2.0kg, thixotropic agent 0.20kg, pigment extender 40.00kg, flow agent 0.6kg, tensio-active agent 0.4kg.Described component A comprises: acrylic acid epoxy resin 92.00kg, and emulsifying agent 5.00kg,, tensio-active agent 1.00kg, catalyzer 2.00kg.
The preparation method of above-mentioned component B, A is a kind of two group mass parts reaction-curable coating with embodiment 1 deionization water-based glaze lacquer of the present invention, respectively becomes the effect of mass parts in the coating reference formulation A group mass parts.
The 1st is modified amine curing agent, and effect is to produce curing reaction with B group mass parts; The 2nd is deionized water, adjusts the viscosity that reduces A group mass parts; The 3rd is dispersion agent, helps the dispersion of the 6th pigment extender; The 4th is thinner, helps the wetting dispersion of the 6th pigment extender; The 5th is thixotropic agent, adjusts the viscosity of A group mass parts, prevents the coating sedimentation; The 6th is pigment extender, promotes the opacifying power of coating and is used for the coating toning; The 7th is flow agent, adjusts the levelling property of A group mass parts; The 8th is tensio-active agent, reduces the surface tension of paint film.
Deionization water-based glaze lacquer is a kind of two group mass parts reaction-curable coating, respectively becomes the effect of mass parts in the coating reference formulation B group mass parts.
The 9th is acrylic acid epoxy resin, and effect is to produce curing reaction, hard, the anti-xanthochromia of paint film with A group mass parts; The 10th is thinner, adjusts the viscosity that reduces B group mass parts; The 11st is tensio-active agent, helps B, A group mass parts to mix easily; The 12nd is catalyzer, promotes the reactive behavior of B group mass parts, adds the fast response curing speed.
Use water-based glaze finish paint of the present invention, in the building decoration field, be applied to inside and outside wall paint, meet the green inner wall examination criteria, reach the index of inner, external wall coating premium grads simultaneously.As the function wall paint, be applied to hospital's antimildew and antibacterial lacquer, reach antimildew and antibacterial 1 index such as product such as grade.As the function wall paint, be applied to the anti-graffiti lacquer of school, reach 3 grades of indexs of anti-graffiti standard.
Use deionization water-based glaze lacquer of the present invention, in the industrial protection field, as aqueous woodware paint, water-based pottery lacquer, aqueous glass lacquer, meet the environmental protection tests standard, reach the coating property index of these industries simultaneously.
Use water-based glaze finish paint of the present invention, in the industrial antisepsis field, as outdoor water-repellent preservation finish paint, meet the environmental protection tests standard, reach the index of steel structure anti-corrosion paint 1 profile lacquer simultaneously.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (7)
1. a water-based glaze wall paint is characterized in that, comprises component A and component B, and described component A and component B press mass ratio 1:4-8 and mix, and stir namely.
2. a kind of water-based glaze finish paint according to claim 1, it is characterized in that, described component B comprises by mass parts: water-based amine hardener 30.00-48.00 mass parts, deionized water 24.00-38.00 mass parts, dispersion agent 0.20-0.40 mass parts, thinner 1.00-5.00 mass parts, thixotropic agent 0.20-0.60 mass parts, pigment extender 22.00-28.00 mass parts, flow agent 0.40-1.00 mass parts, tensio-active agent 0.10-0.50 mass parts.
3. a kind of water-based glaze finish paint according to claim 1, it is characterized in that, described component B comprises by mass parts: water-based amine hardener 39.00-36.00 mass parts, deionized water 28.00-36.00 mass parts, dispersion agent 0.20-0.3 mass parts, thinner 1.02.00-5.00 mass parts, thixotropic agent 0.20-0.40 mass parts, pigment extender 25.00-26.00 mass parts, flow agent 0.20-0.30 mass parts, tensio-active agent 0.20-0.40 mass parts.
4. a kind of water-based glaze finish paint according to claim 1, it is characterized in that, described component B comprises by mass parts: water-based amine hardener 45.00 mass parts, deionized water 28.00 mass parts, dispersion agent 0.40 mass parts, thinner 2.80 mass parts, thixotropic agent 0.30 mass parts, pigment extender 22.80 mass parts, flow agent 0.40 mass parts, tensio-active agent 0.40 mass parts.
5. a kind of water-based glaze finish paint according to claim 1, it is characterized in that, described component A comprises by mass parts: acrylic acid epoxy resin 62.00-92.00 mass parts, thinner 0-10.00 mass parts, tensio-active agent 1.00-10.00 mass parts, catalyzer 2.00-7.00, emulsifying agent 5.00-16.00 mass parts.
6. a kind of water-based glaze finish paint according to claim 1, it is characterized in that, described component A comprises by mass parts: acrylic acid epoxy resin 74.00-80.00 mass parts, thinner 3.00-9.00 mass parts, tensio-active agent 3.00-7.00 mass parts, catalyzer 3.00-6.00, emulsifying agent 7.00-12.00 mass parts.
7. a kind of water-based glaze finish paint according to claim 1 is characterized in that described component A comprises by mass parts: acrylic acid epoxy resin 78.00 mass parts, thinner 8.00 mass parts, tensio-active agent 5.00 mass parts, promotor 10.00 mass parts.