CN103319881A - 尼龙6/聚苯醚/碳纤维合金专用料 - Google Patents
尼龙6/聚苯醚/碳纤维合金专用料 Download PDFInfo
- Publication number
- CN103319881A CN103319881A CN 201210075444 CN201210075444A CN103319881A CN 103319881 A CN103319881 A CN 103319881A CN 201210075444 CN201210075444 CN 201210075444 CN 201210075444 A CN201210075444 A CN 201210075444A CN 103319881 A CN103319881 A CN 103319881A
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- nylon
- polyphenyl ether
- alloy material
- fiber alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种尼龙6/聚苯醚/碳纤维合金专用料，由下述组分按重量公斤组成：尼龙6100公斤，聚苯醚100-120公斤，碳纤维60-80公斤，偶联剂2-4公斤，抗氧剂10100.1-0.3公斤，增韧剂1-3公斤。本发明制备的尼龙6/聚苯醚/碳纤维合金专用料，具有较好的缺口抗冲击性能和弯曲强度，综合性能好，可替代用于结构部件的金属材料，可显著降低材料成本和加工费用，主要应用于机械结构部件或电气零部件。
Description
技术领域
本发明涉及一种塑料合金，尤其涉及一种尼龙6/聚苯醚/碳纤维合金专用料。
背景技术
尼龙6，又叫PA6，聚酰胺6。尼龙6的化学物理特性和尼龙66很相似，然而，它的熔点较低，而且工艺温度范围很宽。它的抗冲击性和抗溶解性比尼龙66塑料要好,但吸湿性也更强。因为塑件的许多品质特性都要受到吸湿性的影响，因此使用尼龙6设计产品时要充分考虑到这一点。为了提高尼龙6的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。对于没有添加剂的产品，尼龙6塑胶原料的收缩率在1%到1.5%之间。加入玻璃纤维添加剂可以使收缩率降低到0.3%（但和流程相垂直的方向还要稍高一些）。成型组装的收缩率主要受材料结晶度和吸湿性影响。实际的收缩率还和塑件设计、壁厚及其它工艺参数成函数关系。尼龙6注塑干燥处理由于尼龙6很容易吸收水分，因此加工前的干燥特别要注意。如果材料是用防水材料包装供应的，则容器应保持密闭。如果湿度大于0.2%，建议在80C以上的热空气中干燥16小时。如果材料已经在空气中暴露超过8小时，建议进行105C，8小时以上的真空烘干。尼龙6注塑工艺参数熔料温度：240-250℃，对于增强品种为250~280℃。
发明内容
为解决现有技术存在的不足，本发明所要解决的技术问题是提供一种尼龙6/聚苯醚/碳纤维合金专用料。
本发明的技术方案为：
一种尼龙6/聚苯醚/碳纤维合金专用料，由下述组分按重量份组成：尼龙6 100份，聚苯醚 100-120份，碳纤维 60-80份，偶联剂2-4份，抗氧剂1010 0.1-0.3份，增韧剂1-3份。
将上述各组分搅拌混合均匀，采用常规方法造粒，即可制得本发明的尼龙6/聚苯醚/碳纤维合金专用料。
聚苯醚是本世纪60年代发展起来的高强度工程塑料，化学名称为聚2,6—二甲基—1,4—苯醚，简称PPO（Polyphenylene Oxide）或PPE（Polypheylene ether），又称为聚亚苯基氧化物或聚苯撑醚。具有优良的综合性能，最大的特点是在长期负荷下，具有优良的尺寸稳定性和突出的电绝缘性，使用温度范围广，可在－127～121℃范围内长期使用。具有优良的耐水、耐蒸汽性能，制品具较高的拉伸强度和抗冲强度，抗蠕变性也好。此外，有较好的耐磨性和电性能。主要用于代替不锈钢制造外科医疗器械。在机电工业中可制作齿轮、鼓风机叶片、管道、阀门、螺钉及其他紧固件和连接件等，还用于制作电子、电气工业中的零部件，如线圈骨架及印刷电路板等。
偶联剂，在塑料配混中，改善合成树脂与无机填充剂或增强材料的界面性能的一种塑料添加剂。又称表面改性剂。它在塑料加工过程中可降低合成树脂熔体的粘度，改善填充剂的分散度以提高加工性能，进而使制品获得良好的表面质量及机械、热和电性能。具体的，再在本发明中，可以是硅烷偶联剂或钛酸酯偶联剂。
本发明制备的尼龙6/聚苯醚/碳纤维合金专用料，具有较好的缺口抗冲击性能和弯曲强度，综合性能好，可替代用于结构部件的金属材料，可显著降低材料成本和加工费用，主要应用于机械结构部件或电气零部件。
具体实施方式：
一种尼龙6/聚苯醚/碳纤维合金专用料：
尼龙6 100公斤，聚苯醚 110公斤，碳纤维 70公斤，偶联剂3公斤，抗氧剂1010 0.2公斤，增韧剂2公斤。
将上述各组分搅拌混合均匀，熔融混炼、挤出造粒，即可制得本发明的尼龙6/聚苯醚/碳纤维合金专用料。混合工序可以在通用的混合机中进行，控制转速在300-400转/分钟，熔融混炼、挤出造粒工序可在通用的螺杆挤出机中进行。
经测试：
缺口冲击强度=31KJ/m2；
拉升强度=60 MPa；
弯曲强度=80MPa；
热变形温度（1.82MPa）=170℃。
本发明制备的尼龙6/聚苯醚/碳纤维合金专用料，具有较好的缺口抗冲击性能和弯曲强度，综合性能好，可替代用于结构部件的金属材料，可显著降低材料成本和加工费用，主要应用于机械结构部件或电气零部件。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (1)
1.一种尼龙6/聚苯醚/碳纤维合金专用料，由下述组分按重量公斤组成：尼龙6 100公斤，聚苯醚 100-120公斤，碳纤维 60-80公斤，偶联剂2-4公斤，抗氧剂1010 0.1-0.3公斤，增韧剂1-3公斤。