CN103289502A - 一种酚醛树脂粉末涂料及其制备方法 - Google Patents

一种酚醛树脂粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103289502A
CN103289502A CN2013101409923A CN201310140992A CN103289502A CN 103289502 A CN103289502 A CN 103289502A CN 2013101409923 A CN2013101409923 A CN 2013101409923A CN 201310140992 A CN201310140992 A CN 201310140992A CN 103289502 A CN103289502 A CN 103289502A
Authority
CN
China
Prior art keywords
powder
powder coating
resol
coating
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101409923A
Other languages
English (en)
Other versions
CN103289502B (zh
Inventor
田益坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGSHAN HONGLIMEI NEW MATERIAL TECHNOLOGY Co.,Ltd.
Original Assignee
ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd filed Critical ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310140992.3A priority Critical patent/CN103289502B/zh
Publication of CN103289502A publication Critical patent/CN103289502A/zh
Application granted granted Critical
Publication of CN103289502B publication Critical patent/CN103289502B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种酚醛树脂粉末涂料及其制备方法，其组成原料为：酚醛树脂、PA6、氧化铝、间二甲苯、三乙醇胺、金葱粉、高岭土粉末、流平剂、苯乙基苯丙基酚聚氧乙烯醚、抗氧剂1520、丙三醇、聚乙烯吡咯烷酮和成膜树脂；本发明粉末涂料为绿色环保型涂料，无毒，耐高温，不含溶剂，无VOC排放，而且本发明采用酚醛树脂为主要原料，同时添加了成膜树脂和氧化铝，增强粉末涂料的成膜性，改进了粉末涂料的表面流平，具有高保光性，提高了粉末涂料的装饰性；制备得到的成品合格率高，可实现工业化大生产。

Description

一种酚醛树脂粉末涂料及其制备方法
技术领域
本发明涉及粉末涂料领域，尤其涉及一种酚醛树脂粉末涂料及其制备方法。
背景技术
    随着我国经济的持续稳定增长以及人民生活水平的不断提高，金属构件的粉末涂装业务也不断增加，尤其是家用电器、仪器仪表、交通设施、铝型材、各种车辆以及日用五金等行业，粉末涂层能给金属提供优良的防腐保护及装饰性能，但由于用于上述领域的现有涂料的抗污染性能不理想，涂层上经常附着各类灰尘、污垢甚至是油污；抗粘贴能力也不理想，且现有粉末涂料形成的涂层在户外长期暴晒、雨淋等自然条件影响下易出现起泡、开裂、剥离等现象，因此，涂层的机械性能也不理想。
发明内容
本发明所要解决的技术问题是克服现有技术的不足，提供一种酚醛树脂粉末涂料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
酚醛树脂粉末涂料，其组成原料的重量份为：酚醛树脂35-40、PA6  13-15、氧化铝2-4、间二甲苯1.4-1.8、三乙醇胺1.3-1.5、金葱粉1.4-1.6、高岭土粉末28-32、流平剂1-2、苯乙基苯丙基酚聚氧乙烯醚2.5-3.0、抗氧剂1520  2.3-2.8、丙三醇1.2-1.5、聚乙烯吡咯烷酮2-4和成膜树脂3-4。
酚醛树脂粉末涂料，其组成原料的重量份为：酚醛树脂38、PA6  14、氧化铝3、间二甲苯1.6、三乙醇胺1.4、金葱粉1.5、高岭土粉末30、流平剂1.5、苯乙基苯丙基酚聚氧乙烯醚2.8、抗氧剂1520  2.5、丙三醇1.4、聚乙烯吡咯烷酮3和成膜树脂3.5。
酚醛树脂粉末涂料的制备方法，包括以下步骤：
（1）成膜树脂的制备：按组成配方尿素3-5、氯化石蜡5-7、聚对苯二甲酸二乙酯3-5、氮化铝粉末4-6、银粉0.2-0.3、松香0.3-0.5、己二酸丙二醇聚酯3-5、苯乙烯2-3、2、4-二氯过氧化苯甲酰0.2-0.3和氧化锌0.3-0.5；制成方法如下：
a：将氯化石蜡、聚对苯二甲酸二乙酯、氮化铝粉末、松香、己二酸丙二醇聚酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、2、4-二氯过氧化苯甲酰、氧化锌、银粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：75±8℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成200-220目的粉末，包装入库，粉末固化条件为：固化温度150-180℃，保温18-22分钟。
本发明的优点：
本发明粉末涂料为绿色环保型涂料，无毒，耐高温，不含溶剂，无VOC 排放，而且本发明采用酚醛树脂为主要原料，同时添加了成膜树脂和氧化铝，增强粉末涂料的成膜性，改进了粉末涂料的表面流平，具有高保光性，提高了粉末涂料的装饰性；制备得到的成品合格率高，可实现工业化大生产。
具体实施方式
实施例1：酚醛树脂粉末涂料，其组成原料的重量份（kg）为：酚醛树脂38、PA6  14、氧化铝3、间二甲苯1.6、三乙醇胺1.4、金葱粉1.5、高岭土粉末30、流平剂1.5、苯乙基苯丙基酚聚氧乙烯醚2.8、抗氧剂1520  2.5、丙三醇1.4、聚乙烯吡咯烷酮3和成膜树脂3.5。
酚醛树脂粉末涂料的制备方法，包括以下步骤：
（1）成膜树脂的制备：按组成配方（kg）尿素4、氯化石蜡6、聚对苯二甲酸二乙酯4、氮化铝粉末5、银粉0.25、松香0.4、己二酸丙二醇聚酯4、苯乙烯2.5、2、4-二氯过氧化苯甲酰0.25和氧化锌0.4；制成方法如下：
a：将氯化石蜡、聚对苯二甲酸二乙酯、氮化铝粉末、松香、己二酸丙二醇聚酯、苯乙烯加入不锈钢反应釜，升温至110℃，开动搅拌加入尿素、2、4-二氯过氧化苯甲酰、氧化锌、银粉；
b：然后以55℃/小时速率升温到188℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：75℃；二区温度控制在：95℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成210目的粉末，包装入库，粉末固化条件为：固化温度165℃，保温20分钟。
    将该粉末涂料采用静电喷涂施工方法作用于经喷涂处理的冰箱外壳表面上，经180℃的充分固化，自然冷却至室温，放置24h后，测定涂层性能，其涂层冲击强度≥ 89.8cm，耐盐雾时间≥ 417h，人工加速老化时间≥ 2950h，耐热性能≥527℃，天然曝晒13个月不起泡、不生锈、不开裂、不剥离。

Claims (3)

1.一种酚醛树脂粉末涂料，其特征在于其组成原料的重量份为：酚醛树脂35-40、PA6  13-15、氧化铝2-4、间二甲苯1.4-1.8、三乙醇胺1.3-1.5、金葱粉1.4-1.6、高岭土粉末28-32、流平剂1-2、苯乙基苯丙基酚聚氧乙烯醚2.5-3.0、抗氧剂1520  2.3-2.8、丙三醇1.2-1.5、聚乙烯吡咯烷酮2-4和成膜树脂3-4。
2.根据权利要求1所述的酚醛树脂粉末涂料，其特征在于其组成原料的重量份为：酚醛树脂38、PA6  14、氧化铝3、间二甲苯1.6、三乙醇胺1.4、金葱粉1.5、高岭土粉末30、流平剂1.5、苯乙基苯丙基酚聚氧乙烯醚2.8、抗氧剂1520  2.5、丙三醇1.4、聚乙烯吡咯烷酮3和成膜树脂3.5。
3.一种如权利要求1所述的酚醛树脂粉末涂料的制备方法，其特征在于包括以下步骤：
（1）成膜树脂的制备：按组成配方尿素3-5、氯化石蜡5-7、聚对苯二甲酸二乙酯3-5、氮化铝粉末4-6、银粉0.2-0.3、松香0.3-0.5、己二酸丙二醇聚酯3-5、苯乙烯2-3、2、4-二氯过氧化苯甲酰0.2-0.3和氧化锌0.3-0.5；制成方法如下：
a：将氯化石蜡、聚对苯二甲酸二乙酯、氮化铝粉末、松香、己二酸丙二醇聚酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、2、4-二氯过氧化苯甲酰、氧化锌、银粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：75±8℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成200-220目的粉末，包装入库，粉末固化条件为：固化温度150-180℃，保温18-22分钟。
CN201310140992.3A 2013-04-23 2013-04-23 一种酚醛树脂粉末涂料及其制备方法 Active CN103289502B (zh)