CN103289521A - 一种高强度耐热的粉末涂料及其制备方法 - Google Patents

一种高强度耐热的粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103289521A
CN103289521A CN2013101409957A CN201310140995A CN103289521A CN 103289521 A CN103289521 A CN 103289521A CN 2013101409957 A CN2013101409957 A CN 2013101409957A CN 201310140995 A CN201310140995 A CN 201310140995A CN 103289521 A CN103289521 A CN 103289521A
Authority
CN
China
Prior art keywords
powder
powder coating
coating
titanium dioxide
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101409957A
Other languages
English (en)
Inventor
田益坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Original Assignee
ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd filed Critical ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Priority to CN2013101409957A priority Critical patent/CN103289521A/zh
Publication of CN103289521A publication Critical patent/CN103289521A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度耐热的粉末涂料及其制备方法，其组成原料为：环氧树脂E-06、干性油醇酸树脂、间二甲苯、2-乙基-4甲基咪唑、钛白粉、氮化铝粉末、聚乙烯醚、间苯二酚、甲基丙烯酸甲酯、柠檬酸和成膜树脂；本发明粉末涂料为绿色环保型涂料，无毒，耐高温，不含溶剂，无VOC排放，而且本发明采用环氧树脂E-06为主要原料，同时添加了成膜树脂，增强粉末涂料的成膜性，改进了粉末涂料的表面流平，具有高保光性，耐热时间长，提高了粉末涂料的装饰性；制备得到的成品合格率高，可实现工业化大生产。

Description

一种高强度耐热的粉末涂料及其制备方法
技术领域
本发明涉及粉末涂料领域，尤其涉及一种高强度耐热的粉末涂料及其制备方法。
背景技术
    随着我国经济的持续稳定增长以及人民生活水平的不断提高，金属构件的粉末涂装业务也不断增加，尤其是家用电器、仪器仪表、交通设施、铝型材、各种车辆以及日用五金等行业，粉末涂层能给金属提供优良的防腐保护及装饰性能，但由于用于上述领域的现有涂料的抗污染性能不理想，涂层上经常附着各类灰尘、污垢甚至是油污；抗粘贴能力也不理想，且现有粉末涂料形成的涂层在户外长期暴晒、雨淋等自然条件影响下易出现起泡、开裂、剥离等现象，因此，涂层的机械性能也不理想。
发明内容
本发明所要解决的技术问题是克服现有技术的不足，提供一种高强度耐热的粉末涂料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
高强度耐热的粉末涂料，其组成原料的重量份为：环氧树脂E-06  46-50、干性油醇酸树脂3-5、间二甲苯1.6-1.8、2-乙基-4甲基咪唑1.0-1.5、钛白粉1-2、氮化铝粉末3-4、聚乙烯醚3.5-5.5、间苯二酚3.5-4.5、甲基丙烯酸甲酯1-2、柠檬酸4-7和成膜树脂2.3-2.8。
高强度耐热的粉末涂料，其组成原料的重量份为：环氧树脂E-06   48、干性油醇酸树脂4、间二甲苯1.7、2-乙基-4甲基咪唑1.2、钛白粉1.5、氮化铝粉末3.5、聚乙烯醚4.5、间苯二酚4、甲基丙烯酸甲酯1.5、柠檬酸6和成膜树脂2.5。
高强度耐热的粉末涂料的制备方法，包括以下步骤：
（1）成膜树脂的制备：按组成配方尿素3-5、氯化石蜡5-7、聚对苯二甲酸二乙酯3-5、二氧化钛粉4-6、银粉0.2-0.3、松香0.3-0.5、己二酸丙二醇聚酯3-5、苯乙烯2-3、2、4-二氯过氧化苯甲酰0.2-0.3和氧化锌0.3-0.5；制成方法如下：
a：将氯化石蜡、聚对苯二甲酸二乙酯、二氧化钛粉、松香、己二酸丙二醇聚酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、2、4-二氯过氧化苯甲酰、氧化锌、银粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：70±5℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成200-220目的粉末，包装入库，粉末固化条件为：固化温度150-180℃，保温18-22分钟。
本发明的优点：
本发明粉末涂料为绿色环保型涂料，无毒，耐高温，不含溶剂，无VOC 排放，而且本发明采用环氧树脂E-06为主要原料，同时添加了成膜树脂，增强粉末涂料的成膜性，改进了粉末涂料的表面流平，具有高保光性，耐热时间长，提高了粉末涂料的装饰性；制备得到的成品合格率高，可实现工业化大生产。
具体实施方式
实施例1：高强度耐热的粉末涂料，其组成原料的重量份（kg）为：环氧树脂E-06  48、干性油醇酸树脂4、间二甲苯1.7、2-乙基-4甲基咪唑1.2、钛白粉1.5、氮化铝粉末3.5、聚乙烯醚4.5、间苯二酚4、甲基丙烯酸甲酯1.5、柠檬酸6和成膜树脂2.5。
高强度耐热的粉末涂料的制备方法，包括以下步骤：
（1）成膜树脂的制备：按组成配方（kg）尿素4、氯化石蜡6、聚对苯二甲酸二乙酯4、二氧化钛粉5、银粉0.25、松香0.4、己二酸丙二醇聚酯4、苯乙烯2.5、2、4-二氯过氧化苯甲酰0.25和氧化锌0.4；制成方法如下：
a：将氯化石蜡、聚对苯二甲酸二乙酯、二氧化钛粉、松香、己二酸丙二醇聚酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、2、4-二氯过氧化苯甲酰、氧化锌、银粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：70±5℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成200-220目的粉末，包装入库，粉末固化条件为：固化温度150-180℃，保温18-22分钟。
    将该粉末涂料采用静电喷涂施工方法作用于经喷涂处理的冰箱外壳表面上，经180℃的充分固化，自然冷却至室温，放置24h后，测定涂层性能，其涂层冲击强度≥ 93.5cm，耐盐雾时间≥ 425h，人工加速老化时间≥ 3120h，耐热性能≥570℃，天然曝晒13个月不起泡、不生锈、不开裂、不剥离。

Claims (3)

1.一种高强度耐热的粉末涂料，其特征在于其组成原料的重量份为：环氧树脂E-06  46-50、干性油醇酸树脂3-5、间二甲苯1.6-1.8、2-乙基-4甲基咪唑1.0-1.5、钛白粉1-2、氮化铝粉末3-4、聚乙烯醚3.5-5.5、间苯二酚3.5-4.5、甲基丙烯酸甲酯1-2、柠檬酸4-7和成膜树脂2.3-2.8。
2.根据权利要求1所述的高强度耐热的粉末涂料，其特征在于其组成原料的重量份为：环氧树脂E-06  48、干性油醇酸树脂4、间二甲苯1.7、2-乙基-4甲基咪唑1.2、钛白粉1.5、氮化铝粉末3.5、聚乙烯醚4.5、间苯二酚4、甲基丙烯酸甲酯1.5、柠檬酸6和成膜树脂2.5。
3.一种如权利要求1所述的高强度耐热的粉末涂料的制备方法，其特征在于包括以下步骤：
（1）成膜树脂的制备：按组成配方尿素3-5、氯化石蜡5-7、聚对苯二甲酸二乙酯3-5、二氧化钛粉4-6、银粉0.2-0.3、松香0.3-0.5、己二酸丙二醇聚酯3-5、苯乙烯2-3、2、4-二氯过氧化苯甲酰0.2-0.3和氧化锌0.3-0.5；制成方法如下：
a：将氯化石蜡、聚对苯二甲酸二乙酯、二氧化钛粉、松香、己二酸丙二醇聚酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、2、4-二氯过氧化苯甲酰、氧化锌、银粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：70±5℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成200-220目的粉末，包装入库，粉末固化条件为：固化温度150-180℃，保温18-22分钟。
CN2013101409957A 2013-04-23 2013-04-23 一种高强度耐热的粉末涂料及其制备方法 Pending CN103289521A (zh)