CN103275550A - Soybean oil type offset printing ink - Google Patents
Soybean oil type offset printing ink Download PDFInfo
- Publication number
- CN103275550A CN103275550A CN2013102121434A CN201310212143A CN103275550A CN 103275550 A CN103275550 A CN 103275550A CN 2013102121434 A CN2013102121434 A CN 2013102121434A CN 201310212143 A CN201310212143 A CN 201310212143A CN 103275550 A CN103275550 A CN 103275550A
- Authority
- CN
- China
- Prior art keywords
- parts
- soybean oil
- printing ink
- offset printing
- type offset
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses soybean oil type offset printing ink which consists of the following raw materials in parts by weight: 10-25 parts of organic pigment, 5-10 parts of filler, 25-35 parts of soybean oil, 15-25 parts of linseed oil, 1-5 parts of vinyl chloride-vinyl acetate resin, 25-35 parts of modified phenolic resin, 0.5-1 part of antioxidant and 0.1-0.5 part of gelatinizing agent. Compared with the prior art, a great quantity of volatile organic compounds in the traditional ink are reduced, more vegetable oil is adopted, and the soybean oil type offset printing ink has better environmental protection property and resource reproducibility.
Description
Technical field
The present invention relates to a kind of soybean oil type offset printing printing ink.
Background technology
The printing ink of printing industry use at present, great majority are to make binder with resin and oil series solvent, mix with pigment dyestuff, filler, auxiliary agent etc. again, and contain more multiring aromatic hydrocarbon substance in the oil series solvent, wherein contain carcinogenic composition,, residual quantity is big on printed matters such as books and periodicals, newspaper, picture album, the survival time is long, does not reach the requirement of human safety and feature of environmental protection aspect.Soybean oil can not only be improved printing quality, and can reduce the discharging of volatile organic matter (VOC), and is renewable resources, and the safety and environmental protection performance is improved greatly.
Summary of the invention
The technical problem that solves:At the deficiencies in the prior art, the invention provides a kind of safety and environmental protection, the measured soybean oil type offset printing printing ink of printing quality.
Technical scheme:The invention provides a kind of soybean oil type offset printing printing ink, it is made up of the raw material of following parts by weight: pigment dyestuff 10-25 part, filler 5-10 part, soybean oil 25-35 part, Toenol 1140 15-25 part, vinyl chloride-vinyl acetate resin 1-5 part, modified phenolic resins 25-35 part, oxidation inhibitor 0.5-1 part, gelatinizing agent 0.1-0.5 part.
As preferred version, above-described soybean oil type offset printing printing ink, it is made up of the raw material of following parts by weight: pigment dyestuff 15-20 part, filler 6-9 part, soybean oil 25-30 part, Toenol 1140 15-20 part, vinyl chloride-vinyl acetate resin 2-4 part, modified phenolic resins 25-30 part, oxidation inhibitor 0.5-0.8 part, 0.5 part of gelatinizing agent.
Described pigment dyestuff is benzidine yellow G R, fuchsin 6B or phthalocyanine blue B; Described filler is calcium carbonate, high territory or brilliant white; Described modified phenolic resins is polyamide modified resol or epoxy modified phenolic resin; Described vinyl chloride-vinyl acetate resin has urges the effect of doing, and can shorten the required time of ink setting, thereby improve the film forming properties of printing ink.
Beneficial effect:The present invention has reduced volatile organic compound ingredients a large amount of in traditional printing ink, more adopts vegetables oil, and the feature of environmental protection is better, has the resource recyclability.Printing effect is good, and safety in utilization is good, and the waste vegetable oil printing ink residue ratio after deinking is handled is easier to degraded, is convenient to recycle, good energy-conserving effect.
Embodiment
Mode below by embodiment further specifies the present invention, and therefore scope of the present invention is not confined to following embodiment.
Embodiment 1
With 10 parts of benzidine yellow G R, 5 parts of calcium carbonate, 25 parts of soybean oil, 15 parts of Toenol 1140s, 1 part of vinyl chloride-vinyl acetate resin, 25 parts of polyamide modified resol, 0.5 part of oxidation inhibitor, 0.1 a part gelatinizing agent is mixed into Ji Mo, it is pre-dispersed to use the high speed dispersion agent to carry out, and grinds with three-roll grinder and sand mill again, treat that fineness reaches standard after, enter high-speed mixing equipment adjustment again, the qualified adding auxiliary agent of index can be packed.
Embodiment 2
With 15 parts of benzidine yellow G R, 6 parts of calcium carbonate, 30 parts of soybean oil, 20 parts of Toenol 1140s, 2 parts of vinyl chloride-vinyl acetate resins, 30 parts of polyamide modified resol, 0.6 part of oxidation inhibitor, 0.2 a part gelatinizing agent is mixed into Ji Mo, it is pre-dispersed to use the high speed dispersion agent to carry out, and grinds with three-roll grinder and sand mill again, treat that fineness reaches standard after, enter high-speed mixing equipment adjustment again, the qualified adding auxiliary agent of index can be packed.
Embodiment 3
With 20 parts of fuchsin 6B, 8 parts of calcium carbonate, 30 parts of soybean oil, 20 parts of Toenol 1140s, 3 parts of vinyl chloride-vinyl acetate resins, 30 parts of epoxy modified phenolic resins, 0.8 part of oxidation inhibitor, 0.3 a part gelatinizing agent is mixed into Ji Mo, it is pre-dispersed to use the high speed dispersion agent to carry out, and grinds with three-roll grinder and sand mill again, treat that fineness reaches standard after, enter high-speed mixing equipment adjustment again, the qualified adding auxiliary agent of index can be packed.
Embodiment 4
With 25 parts of phthalocyanine blue B, 9 parts of kaolin, 35 parts of soybean oil, 25 parts of Toenol 1140s, 5 parts of vinyl chloride-vinyl acetate resins, 35 parts of epoxy modified phenolic resins, 1 part of oxidation inhibitor, 0.5 a part gelatinizing agent is mixed into Ji Mo, it is pre-dispersed to use the high speed dispersion agent to carry out, and grinds with three-roll grinder and sand mill again, treat that fineness reaches standard after, enter high-speed mixing equipment adjustment again, the qualified adding auxiliary agent of index can be packed.
Embodiment 5
With 20 parts of phthalocyanine blue B, 9 parts of brilliant whites, 30 parts of soybean oil, 20 parts of Toenol 1140s, 4 parts of vinyl chloride-vinyl acetate resins, 30 parts of epoxy modified phenolic resins, 0.6 part of oxidation inhibitor, 0.5 a part gelatinizing agent is mixed into Ji Mo, it is pre-dispersed to use the high speed dispersion agent to carry out, and grinds with three-roll grinder and sand mill again, treat that fineness reaches standard after, enter high-speed mixing equipment adjustment again, the qualified adding auxiliary agent of index can be packed.
Gained ink performance detected result: viscosity (32 ℃) 10-12, degree of mobilization (mm) 29-36, set speed (min)≤8, glossiness (%) 〉=65, wear resisting property (level) 4.5.
Claims (5)
1. soybean oil type offset printing printing ink, it is characterized in that being formed by the raw material of following parts by weight: pigment dyestuff 10-25 part, filler 5-10 part, soybean oil 25-35 part, Toenol 1140 15-25 part, vinyl chloride-vinyl acetate resin 1-5 part, modified phenolic resins 25-35 part, oxidation inhibitor 0.5-1 part, gelatinizing agent 0.1-0.5 part.
2. a kind of soybean oil type offset printing printing ink according to claim 1, it is characterized in that being formed by the raw material of following parts by weight: pigment dyestuff 15-20 part, filler 6-9 part, soybean oil 25-30 part, Toenol 1140 15-20 part, vinyl chloride-vinyl acetate resin 2-4 part, modified phenolic resins 25-30 part, oxidation inhibitor 0.5-0.8 part, 0.5 part of gelatinizing agent.
3. a kind of soybean oil type offset printing printing ink according to claim 1 and 2 is characterized in that described modified phenolic resins is polyamide modified resol or epoxy modified phenolic resin.
4. a kind of soybean oil type offset printing printing ink according to claim 1 and 2 is characterized in that described filler is calcium carbonate, high territory or brilliant white.
5. a kind of soybean oil type offset printing printing ink according to claim 1 and 2 is characterized in that described pigment dyestuff is benzidine yellow G R, fuchsin 6B or phthalocyanine blue B.