CN103266499A - 防电弧面料 - Google Patents
防电弧面料 Download PDFInfo
- Publication number
- CN103266499A CN103266499A CN2013101572395A CN201310157239A CN103266499A CN 103266499 A CN103266499 A CN 103266499A CN 2013101572395 A CN2013101572395 A CN 2013101572395A CN 201310157239 A CN201310157239 A CN 201310157239A CN 103266499 A CN103266499 A CN 103266499A
- Authority
- CN
- China
- Prior art keywords
- fiber
- aramid
- fibre
- meta
- modified acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防电弧面料,属于防护面料技术领域。其原料及其重量%为:改性聚丙烯腈纤维34-45%、棉纤维32-45%、间位芳纶纤维5-15%、对位芳纶纤维3-10%和抗静电纤维1-3%。由于将改性聚丙烯腈纤维与棉纤维两者之间的重量比合理地控制为1∶0.82-1.27范围,因而既能体现理想的抗伸断裂强度以及抗撕破强力,又能表现出优异的阻燃效果;由于棉纤维取量合理,因而能体现优异的吸湿效果而藉以满足穿着舒适的要求;面料的克重为200-290g/㎡时的耐电弧性能达到8cal/cm2。
Description
技术领域
本发明属于防护面料技术领域,具体涉及一种防电弧面料。
背景技术
如电气领域的技术人员所知,电弧是一种气体放电现象,是电流通过某些介质如空气所产生的瞬间火花。电弧产生并且持续的时间虽然极短,但是速度极快并且能量极大,核心温度可达2000℃左右,因此由电弧产生的瞬间而引发的高能量聚集会对处于电弧介面附近的作业人员造成伤害乃至致命。因为在电弧事故中,即使发生一点火焰或震荡力照样会使日常穿着的衣服崩裂,使处于电弧介面附近的工作人员的身体直接暴露于高热火焰或熔融的金属环境中。鉴此,通常要求防电弧面料具有良好的机械强度和抗爆裂能力。
不少材料可以作为防电弧面料,如阻燃棉纤维、芳纶纤维、腈氯纶纤维、防静电纤维,等等,并且关于防电弧面料的技术信息可以在公开的中国专利文献中见诸,典型的如发明专利申请公开号CN1930334A推荐的“防电弧和防火的变性聚丙烯腈/棉/芳族聚酰胺纤维共混物”,该专利申请方案采用40-75重量%的变性聚丙烯纤维、10-40重量%的棉纤维和1-40重量%的芳族聚酰胺纤维;又如公布号CN102859055A提供的“具有改善舒适性的用于防暴燃和电弧的结晶间位芳族聚酰胺共混物”,该专利申请方案采用50-80重量%的间位芳族聚酰胺纤维、10-30重量%的阻燃人造丝纤维、10-20重量%的改性聚丙烯腈纤维、0-5重量%的对位芳族聚酰胺纤维和0-3重量%的防静电纤维。应该说,这两项专利申请方案在一定程度上能够体现其说明书中记载的技术效果。
上述CN1930334A由于棉纤维以及改性聚丙烯腈纤维的重量%分别选择为10-40%和40-75%,因此存在以下两点欠缺:其一,湿传输效果并不能达到其说明书第3页倒数第2行至第4页第1行的技术效果;其二,当改性聚丙烯纤维与棉纤维两者之间的重量%大于1∶1.27时,实验表明面料的拉伸断裂强度以及抗撕破强力会显著下降,然而当改性聚丙烯纤维与棉纤维两者之间的重量%小于1∶0.82时,实验证明面料的极限氧指数会降低而难于达到期望的阻燃效果。
上述CN1028590A由于将改性聚丙烯腈纤维的重量%选择为10-20%并且摒弃了棉纤维,因此湿传输效果无法体现。
鉴于上述已有技术,有必要加以改进,为此本申请人作了有益的探索和反复的实验,终于形成了下面将要介绍的技术方案。
发明内容
本发明的任务在于提供一种有助于体现良好的湿传输效果、有利于保障理想的拉伸断裂强力和抗撕破强力以及有便于体现优异的阻燃效果的防电弧面料。
本发明的任务是这样来完成的,一种防电弧面料,其原料及其重量%为:改性聚丙烯腈纤维34-45%、棉纤维32-45%、间位芳纶纤维5-15%、对位芳纶纤维3-10%和抗静电纤维1-3%。
在本发明的一个具体的实施例中,所述的改性聚丙烯腈纤维为45%、棉纤维为45%、间位芳纶为5%、对位芳纶为3%和抗静电纤维为2%。
在本发明的另一个具体的实施例中,所述的改性聚丙烯腈纤维为45%、棉纤维为35.8%、间位芳纶纤维为9.2%、对位芳纶纤维为9%和抗静电纤维为1%。
在本发明的又一个具体的实施例中,所述的改性聚丙烯腈纤维为37%、棉纤维为45%、间位芳纶纤维为8%、对位芳纶纤维为7%和抗静电纤维为3%。
在本发明的再一个具体的实施例中,所述的改性聚丙烯腈纤维为40%、棉纤维为45%、间位芳纶纤维为10%、对位芳纶纤维为4%和抗静电纤维为1%。
在本发明的还有一个具体的实施例中,所述的改性聚丙烯腈纤维为36%、棉纤维为39.6%、间位芳纶纤维为15%、对位芳纶纤维为8%和抗静电纤维为1.4%。
在本发明的更而一个具体的实施例中,所述的改性聚丙烯腈纤维为45%、棉纤维为35.4%、间位芳纶纤维为12%、对位芳纶纤维为5.6%和抗静电纤维为2%。
在本发明的进而一个具体的实施例中,所述的改性聚丙烯腈纤维为34%、棉纤维为41.4%、间位芳纶纤维为12%、对位芳纶纤维为10%和抗静电纤维为2.6%。
在本发明的又更而一个具体的实施例中,所述的抗静电纤维为有机抗静电纤维。
在本发明的又进而一个具体的实施例中,所述的有机抗静电纤维由碳黑与合成纤维复合纺丝构成,所述的合成纤维为聚酰胺纤维。
本发明提供的技术方案由于将改性聚丙烯腈纤维与棉纤维两者之间的重量比合理地控制为1∶0.82-1.27范围,因而既能体现理想的抗伸断裂强度以及抗撕破强力,又能表现出优异的阻燃效果;由于棉纤维取量合理,因而能体现优异的吸湿效果而藉以满足穿着舒适的要求;面料的克重为200-290g/㎡时的耐电弧性能达到8cal/cm2。
具体实施方式
实施例1:
按重量%,改性聚丙烯腈纤维45%、棉纤维45%、间位芳纶(即芳纶1313)纤维5%、对位芳纶(即芳纶1414)纤维3%和由碳黑与聚酰胺纤维混合纺丝(也称混合纺纱,以下同)得到的抗静电纤维2%。
实施例2:
按重量%,改性聚丙烯腈纤维45%、棉纤维35.8%、间位芳纶(即芳纶1313)纤维9.2%、对位芳纶(即芳纶1414)纤维9%和由碳黑与聚酰胺纤维混合纺丝得到的抗静电纤维1%。
实施例3:
按重量%,改性聚丙烯腈纤维37%、棉纤维45%、间位芳纶(即芳纶1313)纤维8%、对位芳纶(即芳纶1414)纤维7%和由碳黑与聚酰胺纤维混合纺丝得到的抗静电纤维3%。
实施例4:
按重量%,改性聚丙烯腈纤维40%、棉纤维45%、间位芳纶(即芳纶1313)纤维10%、对位芳纶(即芳纶1414)纤维4%和由碳黑与聚酰胺纤维混合纺丝得到的抗静电纤维1%。
实施例5:
按重量%,改性聚丙烯腈纤维36%、棉纤维39.6%、间位芳纶(即芳纶1313)纤维15%、对位芳纶(即芳纶1414)纤维8%和由碳黑与聚酰胺纤维混合纺丝得到的抗静电纤维1.4%。
实施例6:
按重量%,改性聚丙烯腈纤维45%、棉纤维35.4%、间位芳纶(即芳纶1313)纤维12%、对位芳纶(即芳纶1414)纤维5.6%和由碳黑与聚酰胺纤维混合纺丝得到的抗静电纤维2%。
实施例7:
按重量%,改性聚丙烯腈纤维34%、棉纤维41.4%、间位芳纶(即芳纶1313)纤维12%、对位芳纶(即芳纶1414)纤维10%和由碳黑与聚酰胺纤维混合纺丝得到的抗静电纤维2.6%。
由上述实施例1至7得到的防电弧面料经测试(测试依据为DL/T320-2010,面料克重为200-290g/㎡)具有下表所示的技术效果:
Claims (10)
1.一种防电弧面料,其特征在于其原料及其重量%为:改性聚丙烯腈纤维34-45%、棉纤维32-45%、间位芳纶纤维5-15%、对位芳纶纤维3-10%和抗静电纤维1-3%。
2.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为45%、棉纤维为45%、间位芳纶为5%、对位芳纶为3%和抗静电纤维为2%。
3.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为45%、棉纤维为35.8%、间位芳纶纤维为9.2%、对位芳纶纤维为9%和抗静电纤维为1%。
4.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为37%、棉纤维为45%、间位芳纶纤维为8%、对位芳纶纤维为7%和抗静电纤维为3%。
5.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为40%、棉纤维为45%、间位芳纶纤维为10%、对位芳纶纤维为4%和抗静电纤维为1%。
6.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为36%、棉纤维为39.6%、间位芳纶纤维为15%、对位芳纶纤维为8%和抗静电纤维为1.4%。
7.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为45%、棉纤维为35.4%、间位芳纶纤维为12%、对位芳纶纤维为5.6%和抗静电纤维为2%。
8.根据权利要求1所述的防电弧面料,其特征在于所述的改性聚丙烯腈纤维为34%、棉纤维为41.4%、间位芳纶纤维为12%、对位芳纶纤维为10%和抗静电纤维为2.6%。
9.根据权利要求1至8任一权利要求所述的防电弧面料,其特征在于所述的抗静电纤维为有机抗静电纤维。
10.根据权利要求9所述的防电弧面料,其特征在于所述的有机抗静电纤维由碳黑与合成纤维复合纺丝构成,所述的合成纤维为聚酰胺纤维。