CN103160890A - 一种无氰镀银电镀液 - Google Patents
一种无氰镀银电镀液 Download PDFInfo
- Publication number
- CN103160890A CN103160890A CN 201110423948 CN201110423948A CN103160890A CN 103160890 A CN103160890 A CN 103160890A CN 201110423948 CN201110423948 CN 201110423948 CN 201110423948 A CN201110423948 A CN 201110423948A CN 103160890 A CN103160890 A CN 103160890A
- Authority
- CN
- China
- Prior art keywords
- parts
- cyanide
- silver plating
- free
- plating solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无氰镀银电镀液,由以下成分按质量配比为:硝酸银30-50,安四乙酸二钠200-350g/L,亚硫酸钠40-60g/L,硝酸钠10-20g/L,硼酸20-30g/L,亚硝酸钠1-2g/L,余量水。工艺环境为:PH值6-9,镀液稳定控制在30-45°C,金属件速度控制在1-1.5m/min,电流密度2-4A/dm2。本发明配方合理,无氰化物对环境和人体无害,镀银溶液稳定性好,生产的产品表面光洁度高,镀银层结合强度高。
Description
技术领域
本发明属电镀化学技术领域,具体涉及一种无氰镀银电镀液。
背景技术
镀银金属件有着良好的导电性广泛应用于电工和电子元件行业,目前普遍采用含有氰化物的镀银溶液具有稳定性好,镀层均匀结晶细腻,表面光洁度高等特点,但氰化物是剧毒物质,对环境和人体危害,属于国家限制的工艺。
发明内容
本发明的目的在于提供一种配方合理,镀银溶液稳定性好,成本低所生产的产品质量好的无氰镀银电镀液。
本发明的技术解决方案是:
一种无氰镀银电镀液,其特征在于,由以下成分按质量配比为:硝酸银30-50,安四乙酸二钠200-350g/L,亚硫酸钠40-60 g/L,硝酸钠10-20 g/L,硼酸20-30 g/L,亚硝酸钠1-2 g/L,余量水。
工艺环境为:PH值6-9,镀液稳定控制在30-45°C,金属件速度控制在1-1.5m/min,电流密度2-4A/dm2。
本发明配方合理,无氰化物对环境和人体无害,镀银溶液稳定性好,生产的产品表面光洁度高,镀银层结合强度高。
具体实施方式:
实施例1
一种无氰镀银电镀液,由以下成分按质量配比为:硝酸银40,安四乙酸二钠300g/L,亚硫酸钠50 g/L,硝酸钠15 g/L,硼酸20 g/L,亚硝酸钠1 g/L,余量水。工艺环境为:PH值8,镀液稳定控制在40°C,金属件速度控制在1.5m/min,电流密度3A/dm2。
Claims (2)
1.一种无氰镀银电镀液,其特征在于,由以下成分按质量配比为:硝酸银30-50,安四乙酸二钠200-350g/L,亚硫酸钠40-60 g/L,硝酸钠10-20 g/L,硼酸20-30 g/L,亚硝酸钠1-2 g/L,余量水。
2.根据权利要求1所述的一种无氰镀银电镀液,其特征在于:工艺环境为:PH值6-9,镀液稳定控制在30-45°C,金属件速度控制在1-1.5m/min,电流密度2-4A/dm2。