CN103131954A - 抗断裂钢索螺栓的制备方法 - Google Patents
抗断裂钢索螺栓的制备方法 Download PDFInfo
- Publication number
- CN103131954A CN103131954A CN2013100421542A CN201310042154A CN103131954A CN 103131954 A CN103131954 A CN 103131954A CN 2013100421542 A CN2013100421542 A CN 2013100421542A CN 201310042154 A CN201310042154 A CN 201310042154A CN 103131954 A CN103131954 A CN 103131954A
- Authority
- CN
- China
- Prior art keywords
- bolt
- treatment
- rod material
- fracture
- bar material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了抗断裂钢索螺栓的制备方法,加工步骤包括:a、铸造杆料,杆料毛坯中化学成分重量百分比为:0.132%≤C≤0.260%,0.62%≤Si≤1.30%,0.25%≤Mn≤0.35%,0.010%≤P≤0.030%,0.010%≤S≤0.030%,1.10%≤Cr≤1.50%,痕量≤B≤0.0018%,0.012%≤Cu≤0.030%,余量为铁及不可避免的杂质;b、经过铸造成型后的杆料做酸洗处理;依照螺栓的线径要求,对其进行抽线,以使所述杆料收缩到螺栓所需的线径;将收缩线径后的杆料切断至螺栓所需的长度,在常温下将切断后的杆料放入覆盖有草木灰的模具型腔内,以镦锻力使杆料形成螺栓所需的头部和杆部尺寸;利用精密车床在杆料杆部的外周面车削形成螺纹。本发明的抗断裂钢索螺栓的制备方法,采用冷挤压工艺螺栓加工,提高了螺栓的强度,达到了高强度螺栓所需的硬度值、强度值,解决了高强度下螺栓的延迟断裂和疲劳断裂,在使用中连接可靠,不易折断,提高了螺栓寿命。
Description
技术领域
本发明涉及到螺栓的加工方法,尤其是一种抗断裂钢索螺栓的制备方法。
背景技术
钢索螺栓是机械行业中常用的紧固件,目前的加工方式一般为车削的成型,强度往往难以保证,有时在使用中产生掉头、杆部断裂等不安全现象,对工业生产危害很大。因此对高强度螺栓生产方法加以研究和改进,确保高强度螺栓的质量稳定性,对技术和经济的发展具有重要作用。此外,螺栓处于相对潮湿的环境中时,容易生锈腐蚀,最终导致断裂或裂纹,形成潜在的事故源。
鉴于此,有必要提供一种钢索螺栓制备方法,生产更耐腐蚀、更耐磨损的高强度螺栓。
发明内容
本发明的目的在于避免现有技术中的不足之处,而提供一种抗断裂钢索螺栓的制备方法。
本发明的目的通过以下技术方案如下:
抗断裂钢索螺栓的制备方法,其特征在于,加工步骤包括:
a、铸造杆料,杆料毛坯中化学成分重量百分比为: 0.132%≤C≤0.260%,0.62%≤Si≤1.30%,0.25%≤Mn≤0.35%,0.010%≤P≤0.030%,0.010%≤S≤0.030%,1.10%≤Cr≤1.50%,痕量≤B≤0.0018%,0.012%≤Cu≤0.030%,余量为铁及不可避免的杂质;
b、经过铸造成型后的杆料做酸洗处理;依照螺栓的线径要求,对其进行抽线,以使所述杆料收缩到螺栓所需的线径;将收缩线径后的杆料切断至螺栓所需的长度,在常温下将切断后的杆料放入覆盖有草木灰的模具型腔内,以镦锻力使杆料形成螺栓所需的头部和杆部尺寸;利用精密车床在杆料杆部的外周面车削形成螺纹,车床上的刀具为陶瓷车刀,工件转动速度保证在3050-3150r.P.M,并由盘头部相对的一端开始进刀,切削液采用水基切削液;
c、热处理
将精密车床车削成型的螺栓外螺纹在740℃±10℃下,用淬火油进行淬火,再将淬火后的螺栓在500℃下进行回火,持续时间80-100分钟,将螺栓的光杆段在800℃±20℃下,用水性淬火液进行淬火,再将淬火后的螺栓在550℃下进行回火,持续时间60-70分钟,最后进行渗碳处理,将渗碳剂送入回火炉内,在1100~1150 ℃温度范围内渗碳处理80~120min,所述的渗碳剂是将钾长石细粉35~50Wt%、石墨粒 15~30Wt%及碳酸盐或/和碳酸氢盐35~50Wt%搅拌混合均匀后得到;
d、深冷处理:将热处理后螺栓装入剩有液氮的容器内,液氮浓度≥99.9%,进行深冷处理,时间为11-12小时;
e、钝化处理,将深冷处理后的螺栓浸入温度为100-120℃的钝化处理液中处理5-6min,所述钝化处理液是由下述重量配比的物质制备而成:4~6份水溶性钼酸盐、10~12份乌洛托品、80~100份碱性硅溶胶、80~100份水溶性丙烯酸树脂,80-100份水;
f、磷化处理,将钝化处理后的螺栓放入60-80℃磷化处理液中浸泡3-5min;
g、渗铬处理,将磷化处理后的螺栓放入25%盐酸溶液润湿的铬铁粉中加热,加热到700-800℃,保持60-70min,再进行清洗、风干,即得成品螺栓。
本发明的抗断裂钢索螺栓的制备方法,采用冷挤压工艺螺栓加工,提高了螺栓的强度,达到了高强度螺栓所需的硬度值、强度值,解决了高强度下螺栓的延迟断裂和疲劳断裂,在使用中连接可靠,不易折断,提高了螺栓寿命,满足了社会上各行业对高强度螺栓的使用需求。
本发明的有益效果在于:
1、本发明细化了材质的整形加工工艺,使线材硬度适中,表面具有良好的磷化皮膜,润滑性能好,线材无氢脆,可塑性好;
2、本发明螺栓进行了多次冷镦挤压成型,提高了高强度螺栓整体强度,螺栓精度高,质量好,生产效率高,无切削无废料,单位成本大大下降。得到了整体金属流向方向一致的螺栓,大大提高了其抗拉强度;
3、热处理工艺的发明突破了螺栓传统热处理的合金钢材的极限,其超强超韧性的特色已领先国内紧固件行业水平。
具体实施方式
结合以下实施例对本发明作进一步描述:
抗断裂钢索螺栓的制备方法,加工步骤包括:
a、铸造杆料,杆料毛坯中化学成分重量百分比为: 0.132%≤C≤0.260%,0.62%≤Si≤1.30%,0.25%≤Mn≤0.35%,0.010%≤P≤0.030%,0.010%≤S≤0.030%,1.10%≤Cr≤1.50%,痕量≤B≤0.0018%,0.012%≤Cu≤0.030%,余量为铁及不可避免的杂质;
b、经过铸造成型后的杆料做酸洗处理;依照螺栓的线径要求,对其进行抽线,以使所述杆料收缩到螺栓所需的线径;将收缩线径后的杆料切断至螺栓所需的长度,在常温下将切断后的杆料放入覆盖有草木灰的模具型腔内,以镦锻力使杆料形成螺栓所需的头部和杆部尺寸;利用精密车床在杆料杆部的外周面车削形成螺纹,车床上的刀具为陶瓷车刀,工件转动速度保证在3050-3150r.P.M,并由盘头部相对的一端开始进刀,切削液采用水基切削液;
c、热处理
将精密车床车削成型的螺栓外螺纹在740℃±10℃下,用淬火油进行淬火,再将淬火后的螺栓在500℃下进行回火,持续时间80-100分钟,将螺栓的光杆段在800℃±20℃下,用水性淬火液进行淬火,再将淬火后的螺栓在550℃下进行回火,持续时间60-70分钟,最后进行渗碳处理,将渗碳剂送入回火炉内,在1100~1150 ℃温度范围内渗碳处理80~120min,所述的渗碳剂是将钾长石细粉35~50Wt%、石墨粒 15~30Wt%及碳酸盐或/和碳酸氢盐35~50Wt%搅拌混合均匀后得到;合计百分之百。
d、深冷处理:将热处理后螺栓装入剩有液氮的容器内,液氮浓度≥99.9%,进行深冷处理,时间为11-12小时;
e、钝化处理,将深冷处理后的螺栓浸入温度为100-120℃的钝化处理液中处理5-6min,所述钝化处理液是由下述重量配比的物质制备而成:4~6份水溶性钼酸盐、10~12份乌洛托品、80~100份碱性硅溶胶、80~100份水溶性丙烯酸树脂,80-100份水;
f、磷化处理,将钝化处理后的螺栓放入70℃磷化处理液中浸泡4min;
g、渗铬处理,将磷化处理后的螺栓放入25%盐酸溶液润湿的铬铁粉中加热,加热到700-800℃,保持60-70min,再进行清洗、风干,即得成品螺栓。
根据本发明的抗断裂钢索螺栓的制备方法生产的螺栓,经过检测试验其机械性能数值如下,螺栓心部硬度达42-45HRC、抗拉强度达到1120Mpa,屈服强度达到1230Mpa,延伸率大于11%,断面收缩率大于34%,冲击韧性大于57J/cm2,综合机械性能比现有工艺制造出的螺栓高10-12%。
最后应当说明的是,以上实施例仅用于说明本发明的技术方案而非对本发明保护范围的限制,尽管参照较佳实施例对本发明作了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的实质和范围。
Claims (2)
1.抗断裂钢索螺栓的制备方法,其特征在于,加工步骤包括:
a、铸造杆料,杆料毛坯中化学成分重量百分比为: 0.132%≤C≤0.260%,0.62%≤Si≤1.30%,0.25%≤Mn≤0.35%,0.010%≤P≤0.030%,0.010%≤S≤0.030%,1.10%≤Cr≤1.50%,痕量≤B≤0.0018%,0.012%≤Cu≤0.030%,余量为铁及不可避免的杂质;
b、经过铸造成型后的杆料做酸洗处理;依照螺栓的线径要求,对其进行抽线,以使所述杆料收缩到螺栓所需的线径;将收缩线径后的杆料切断至螺栓所需的长度,在常温下将切断后的杆料放入覆盖有草木灰的模具型腔内,以镦锻力使杆料形成螺栓所需的头部和杆部尺寸;利用精密车床在杆料杆部的外周面车削形成螺纹,车床上的刀具为陶瓷车刀,工件转动速度保证在3050-3150r.P.M,并由盘头部相对的一端开始进刀,切削液采用水基切削液;
c、热处理
将精密车床车削成型的螺栓外螺纹在740℃±10℃下,用淬火油进行淬火,再将淬火后的螺栓在500℃下进行回火,持续时间80-100分钟,将螺栓的光杆段在800℃±20℃下,用水性淬火液进行淬火,再将淬火后的螺栓在550℃下进行回火,持续时间60-70分钟,最后进行渗碳处理,将渗碳剂送入回火炉内,在1100~1150 ℃温度范围内渗碳处理80~120min,所述的渗碳剂是将钾长石细粉35~50Wt%、石墨粒 15~30Wt%及碳酸盐或/和碳酸氢盐35~50Wt%搅拌混合均匀后得到;
d、深冷处理:将热处理后螺栓装入剩有液氮的容器内,液氮浓度≥99.9%,进行深冷处理,时间为11-12小时;
e、钝化处理,将深冷处理后的螺栓浸入温度为100-120℃的钝化处理液中处理5-6min,所述钝化处理液是由下述重量配比的物质制备而成:4~6份水溶性钼酸盐、10~12份乌洛托品、80~100份碱性硅溶胶、80~100份水溶性丙烯酸树脂,80-100份水;
f、磷化处理,将钝化处理后的螺栓放入60-80℃磷化处理液中浸泡3-5min;
g、渗铬处理,将磷化处理后的螺栓放入25%盐酸溶液润湿的铬铁粉中加热,加热到700-800℃,保持60-70min,再进行清洗、风干,即得成品螺栓。
2.根据权利要求1所述的抗断裂钢索螺栓的制备方法,其特征在于:所述磷化处理,将钝化处理后的螺栓放入70℃磷化处理液中浸泡4min。