CN103131376A - 一种木皮手工贴胶水 - Google Patents
一种木皮手工贴胶水 Download PDFInfo
- Publication number
- CN103131376A CN103131376A CN 201110376196 CN201110376196A CN103131376A CN 103131376 A CN103131376 A CN 103131376A CN 201110376196 CN201110376196 CN 201110376196 CN 201110376196 A CN201110376196 A CN 201110376196A CN 103131376 A CN103131376 A CN 103131376A
- Authority
- CN
- China
- Prior art keywords
- glue
- water
- polyvinyl alcohol
- vae
- mdi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种木皮手工贴胶水,是木质家具表面手工贴木皮的专用胶粘剂。以VAE共聚乳液和聚乙烯醇为主要原材料,加入助剂、添加剂共混而成。具有冷作业、单组份、固化快、粘接性好、粘接平整等特点。
Description
技术领域
本发明涉及家具制造行业的一种胶粘剂,尤其是一种用于手工冷粘接各种木皮的胶粘剂。
背景技术
现在家具制造行业中胶粘剂的使用非常广泛,但是生产制作过程中存在的突出问题是具有良好粘接性能的专用胶粘剂比较少,特别是专用于木皮粘接的产品较少,而且现有的木皮胶多用到热胶机,冷胶的手工冷粘接性不够理想,耐候性,耐水性都较差,固化时间较长,有的易起泡。
发明内容
本发明的目的是开发一种手工贴木皮专用的具良好性能的冷粘剂。
本发明的目的是这样得到实现的:
我们用4,4′二苯基甲烷二异氰酸酯(MDI)作为交联剂,交联聚乙烯醇,制备聚氨酯乳液,再用VAE乳液进行改性共混。
VAE也就是VAE共聚乳液,是醋酸乙烯-乙烯共聚乳液的简称,是以醋酸乙烯和乙烯单体为基本原料,通过乳液聚合方法共聚而成的高分子乳液。VAE乳液具有很好的机械性能,乳液粒子平均粒小,有很好的冷粘性及很快的固化速度。同时可以增加木皮的干湿强度、韧性、光泽度,提高色泽稳定性。
本发明的原料配比:
聚乙烯醇 3-7%、
水 45-65%、
MDI 5-15%、
VAE(706) 5-35%、
OP-10 0.1-0.15%、
尿素 1-5%、
轻质碳酸钙 1-5%、
磷酸氢二铵 0.1-0.15%、
抗氧化剂1010 0.005-0.01%。
原料按比例称量后,先将聚乙烯醇和水入溶解釜中,加温至90摄氏度使聚乙烯醇充分溶解(2小时)。
将聚乙烯醇溶液(PVA)和MDI、OP-10入反应釜,加温至55摄氏度,搅拌1小时至MDI完全分散于PVA中。
再加入706型VAE,45摄氏度搅拌1小时。
最后加入尿素、磷酸氢二铵、轻质碳酸钙、抗氧化剂。搅拌一小时。出料。
本发明由于采用上述技术方案,具有如下优点:
胶水适合手工冷粘贴,粘结性高,固化快,胶水层耐水、耐热、不易变形。
具体实施方式:
实施例:
聚乙烯醇 4%、
水 50%、
MDI 15%、
VAE(706) 25%、
OP-10 0.15%、
尿素 2.69%、
轻质碳酸钙 3%、
磷酸氢二铵 0.15%、
抗氧化剂1010 0.01%。
原料按比例称量后,先将聚乙烯醇和水入溶解釜中,加温至90摄氏度使聚乙烯醇充分溶解(2小时)。
将聚乙烯醇溶液(PVA)和MDI、OP-10入反应釜,加温至55摄氏度,搅拌1小时至MDI完全分散于PVA中。
再加入706型VAE,45摄氏度搅拌1小时。
最后加入尿素、磷酸氢二铵、轻质碳酸钙、抗氧化剂。搅拌一小时,待反应釜温度降至30摄氏度以下可以出料。
本发明的木皮手工贴胶水,性能堪比热胶,单组份,操作简单,粘贴木皮平整,不会起泡,在贴木皮家具制作中应用空间巨大。
Claims (4)
1.一种木皮手工贴胶水,其特征在于由4,4′二苯基甲烷二异氰酸酯(MDI)作为交联剂,交联聚乙烯醇,制备聚氨酯乳液。
2.根据权利要求1所述的木皮手工贴胶水,其特征在于用VAE乳液对制备的聚氨酯乳液进行改性。
3.根据权利要求1或2所述的木皮手工贴胶水,其特征在于各种原料的配比为:
聚乙烯醇 3-7%、
水 45-65%、
MDI 5-15%、
VAE(706) 5-35%、
OP-10 0.1-0.15%、
尿素 1-5%、
轻质碳酸钙 1-5%、
磷酸氢二铵 0.1-0.15%、
抗氧化剂1010 0.005-0.01%。
4.根据权利要求1或2或3所述的木皮手工贴胶水,其特征在于各种原料配比优选为:
聚乙烯醇 4%、
水 50%、
MDI 15%、
VAE(706) 25%、
OP-10 0.15%、
尿素 2.69%、
轻质碳酸钙 3%、
磷酸氢二铵 0.15%、
抗氧化剂1010 0.01%。