CN103123814A - 一种晶体硅太阳能背电极用导电铝浆及制备方法 - Google Patents
一种晶体硅太阳能背电极用导电铝浆及制备方法 Download PDFInfo
- Publication number
- CN103123814A CN103123814A CN 201310053994 CN201310053994A CN103123814A CN 103123814 A CN103123814 A CN 103123814A CN 201310053994 CN201310053994 CN 201310053994 CN 201310053994 A CN201310053994 A CN 201310053994A CN 103123814 A CN103123814 A CN 103123814A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminum paste
- aluminium
- weight
- silicon solar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种晶体硅太阳能背电极用导电铝浆，其特征在于，所述导电铝浆的组分及其重量份数为：铝粉95份、有机载体8-12份、玻璃粉6份，硅烷偶联剂4份、硬脂酸锌2份。本发明制备的铝浆能够有效改善铝浆印刷、干燥后铝膜在硅片上的附着力得到明显提高，铝膜致密均匀性好，结合牢。本发明制备的铝浆经烧结后能在硅基片上形成太阳能电池所需的背场效果，并且具有导电性能耗、接触电阻低，光电转换效率高的优点。
Description
技术领域
本发明属于太阳能电池导电铝浆领域，具体涉及一种晶体硅太阳能背电极用导电铝浆。
背景技术
太阳能电池是一种能将太阳能转换成电能的半导体器件，在光照条件下太阳能电池内部会产生电流，通过电极可将电能输出。具有P型硅的太阳能电池结构，其负电极通常在电池放入正面，而其正电极在背面。当光照射时，合适波长的辐射导致了半导体中产生空穴电子对。
背电场浆料是晶体硅太阳能电池背电极的重要材料，其通过丝网印刷的方法在晶体硅太阳能电池的硅片表面形成附着力强、低欧姆接触电阻的背电极栅线。铝背场浆料能够显著提高电池片的转换效率。随着硅片厚度的不断降低，电池片的翘曲度逐渐增大，我们需要不断提高铝浆的性能，来进一步提高电池片的转换效率，降低电池片的翘曲度。
发明内容
本发明的目的在于提供一种晶体硅太阳能背电极用导电铝浆。
本发明的目的可以通过以下技术方案实现：
一种晶体硅太阳能背电极用导电铝浆，其特征在于，所述导电铝浆的组分及其重量份数为：铝粉95份、有机载体8-12份、玻璃粉6份，硅烷偶联剂4份、硬脂酸锌2份；
其中，所述铝粉为球状铝粉，铝含量大于98%；
所述有机载体是将重量份数12-30的丙烯酸树脂溶解于60-80重量份的苯甲醇中；
所述玻璃粉由1.8份氧化铝、3.7份氧化锌和0.5份二氧化硅组成。
一种晶体硅太阳能背电极用导电铝浆的制备方法，其特征在于它包括以下步骤：
（1）有机载体的制备：将重量份数12-30的丙烯酸树脂溶解于60-80重量份的苯甲醇中，恒温水浴加热完全溶解，筛网过滤；
（2）玻璃粉的制备：按重量份取1.8份氧化铝、3.7份氧化锌和0.5份二氧化硅混合均匀，加热至熔融，保温1小时，球磨20小时，筛网过滤备用；
（3）铝浆：按重量份取铝粉95份、有机载体10份、玻璃粉6份、硅烷偶联剂4份、硬脂酸锌2份，用高速搅拌机搅拌30分钟，然后用三辊研磨机进行研磨，轧压，得到晶体硅太阳能背电极用导电铝浆。
本发明的有益效果：本发明制备的铝浆能够有效改善铝浆印刷、干燥后铝膜在硅片上的附着力得到明显提高，铝膜致密均匀性好，结合牢。本发明制备的铝浆经烧结后能在硅基片上形成太阳能电池所需的背场效果，并且具有导电性能耗、接触电阻低，光电转换效率高的优点。
具体实施方式
下面结合具体实施例对本发明作进一步描述。
实施例1
铝粉：球状铝粉，铝含量大于98%；
有机载体：将重量份数12-30的丙烯酸树脂溶解于60-80重量份的苯甲醇中，恒温水浴加热完全溶解，筛网过滤；
玻璃粉：按重量份取1.8份氧化铝、3.7份氧化锌和0.5份二氧化硅混合均匀，加热至熔融，保温1小时，球磨20小时，筛网过滤备用；
铝浆：按重量份取铝粉95份、有机载体10份、玻璃粉6份、硅烷偶联剂4份、硬脂酸锌2份，用高速搅拌机搅拌30分钟，然后用三辊研磨机进行研磨，轧压，得到晶体硅太阳能背电极用导电铝浆。
Claims (2)
1.一种晶体硅太阳能背电极用导电铝浆，其特征在于，所述导电铝浆的组分及其重量份数为：铝粉95份、有机载体8-12份、玻璃粉6份，硅烷偶联剂4份、硬脂酸锌2份；
其中，所述铝粉为球状铝粉，铝含量大于98%；
所述有机载体是将重量份数12-30的丙烯酸树脂溶解于60-80重量份的苯甲醇中；
所述玻璃粉由1.8份氧化铝、3.7份氧化锌和0.5份二氧化硅组成。
2.一种晶体硅太阳能背电极用导电铝浆的制备方法，其特征在于它包括以下步骤：
（1）有机载体的制备：将重量份数12-30的丙烯酸树脂溶解于60-80重量份的苯甲醇中，恒温水浴加热完全溶解，筛网过滤；
（2）玻璃粉的制备：按重量份取1.8份氧化铝、3.7份氧化锌和0.5份二氧化硅混合均匀，加热至熔融，保温1小时，球磨20小时，筛网过滤备用；
（3）铝浆：按重量份取铝粉95份、有机载体10份、玻璃粉6份、硅烷偶联剂4份、硬脂酸锌2份，用高速搅拌机搅拌30分钟，然后用三辊研磨机进行研磨，轧压，得到晶体硅太阳能背电极用导电铝浆。