CN103122471B - 一种无氰镀铟的电镀液 - Google Patents

一种无氰镀铟的电镀液 Download PDF

Info

Publication number
CN103122471B
CN103122471B CN201310065884.4A CN201310065884A CN103122471B CN 103122471 B CN103122471 B CN 103122471B CN 201310065884 A CN201310065884 A CN 201310065884A CN 103122471 B CN103122471 B CN 103122471B
Authority
CN
China
Prior art keywords
indium
electroplate liquid
cyanide plating
methyl
sodiumnitrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310065884.4A
Other languages
English (en)
Other versions
CN103122471A (zh
Inventor
田鹏
张长生
赵志刚
秦天灵
孟波
武士威
段纪东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Normal University
Original Assignee
Shenyang Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Normal University filed Critical Shenyang Normal University
Priority to CN201310065884.4A priority Critical patent/CN103122471B/zh
Publication of CN103122471A publication Critical patent/CN103122471A/zh
Application granted granted Critical
Publication of CN103122471B publication Critical patent/CN103122471B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种无氰镀铟的电镀液（g·kg-1），其由以下成份组成：硝酸1-甲基-3-乙基咪唑:960～980，乙酸铟：10～30，N-甲基吡咯烷酮:5～10，明胶：0.1～1，糊精：3.5～6，硝酸钠：1～3。一种无氰镀铟的电镀液，电镀可以获得高质量镀层，同时消除电沉积液对环境的危害已成为绿色化学和环保工业急需解决的问题，一种无氰镀铟的电镀液的出现使之成为可能。采用N-甲基吡咯烷酮作为有机光亮剂，本发明的电镀工艺可以降低成本，又有利于改善电镀质量，且安全环保。

Description

一种无氰镀铟的电镀液
技术领域:本发明涉及一种电镀液，是一种无氰镀铟的电镀液。
背景技术:从铟的用途看，其单质金属及合金具有许多特殊性能，是当今高新技术的支撑材料，已成为冶金、机械、化工、轻工、纺织、电子及医药等工业尤其是原子能、宇航、卫星通讯、能源等尖端技术领域内不可缺少的新兴材料。高纯铟的生产，在国内主要是用电解精炼法进行生产。镀铟溶液有氰化物型、硫酸盐型、氟硼酸型、氨磺酸型等，在电解中可能出现析氢效应、水解效应和乳化现象等，因此，须严格控制电解液的成分及电解条件。随着科技的发展，对稀散金属高纯铟及其合金的质量、结构、性能、种类要求也越来越高。传统的冶炼、精炼及合金制备方法已不能完全满足当今生产稀散金属及其合金的需要，且传统的方法也存在不同程度的缺点，如高温操作、能耗高、环境污染严重等，因此需要寻求一种新的方法。
发明内容：针对上述现有技术的不足，本发明提供了一种无氰镀铟的电镀液。
为实现上述目的，本发明采用的技术方案是：一种无氰镀铟的电镀液（g·kg-1）的配方：
硝酸1-甲基-3-乙基咪唑:960
乙酸铟：10～30
N-甲基吡咯烷酮:5～10
明胶：0.1～1
糊精：3.5～6
硝酸钠：1～3
用本发明电镀可以获得高质量镀层，同时消除电沉积液对环境的危害。采用N-甲基吡咯烷酮作为有机光亮剂，本发明的电镀工艺可以降低成本，又有利于改善电镀质量，且安全环保。
具体实施方式：
一种无氰镀铟的电镀液，使用原料：硝酸1-甲基-3-乙基咪唑；乙酸铟；N-甲基吡咯烷酮；明胶；糊精；硝酸钠。
实施例1：
硝酸1-甲基-3-乙基咪唑:960
乙酸铟：25
N-甲基吡咯烷酮:9
明胶：0.2
糊精：4
硝酸钠：1.8
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例2：
硝酸1-甲基-3-乙基咪唑:960
乙酸铟：25
N-甲基吡咯烷酮:9
明胶：0.5
糊精：4.5
硝酸钠：1
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例3：
硝酸1-甲基-3-乙基咪唑:960
乙酸铟：25
N-甲基吡咯烷酮:10
明胶：0.5
糊精：3.5
硝酸钠：1
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例4：
硝酸1-甲基-3-乙基咪唑:970
乙酸铟：15
N-甲基吡咯烷酮:7
明胶：0.5
糊精：6
硝酸钠：1.5
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例5：
硝酸1-甲基-3-乙基咪唑:970
乙酸铟：15
N-甲基吡咯烷酮:7
明胶：0.6
糊精：4.4
硝酸钠：3
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例6：
硝酸1-甲基-3-乙基咪唑:970
乙酸铟：15
N-甲基吡咯烷酮:8
明胶：0.8
糊精：4.2
硝酸钠：2
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例7：
硝酸1-甲基-3-乙基咪唑:970
乙酸铟：20
N-甲基吡咯烷酮:5
明胶：0.5
糊精：3.5
硝酸钠：1
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例8：
硝酸1-甲基-3-乙基咪唑:980
乙酸铟：10
N-甲基吡咯烷酮:5
明胶：0.1
糊精：3.9
硝酸钠：1
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
实施例9：
硝酸1-甲基-3-乙基咪唑:960
乙酸铟：30
N-甲基吡咯烷酮:5
明胶：0.5
糊精：3.5
硝酸钠：1
取上述组分，混合成1000克的一种无氰镀铟的电镀液。
用本发明电镀时，要求溶液pH:6.0～8.0，溶液温度（℃）：25～30，电流密度（A/dm2）:1.5～2.5。

Claims (10)

1.一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:960g·kg-1
乙酸铟：10～30g·kg-1
N-甲基吡咯烷酮:5～10g·kg-1
明胶：0.1～1g·kg-1
糊精：3.5～6g·kg-1
硝酸钠：1～3g·kg-1。
2.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:960g·kg-1
乙酸铟：25g·kg-1
N-甲基吡咯烷酮:9g·kg-1
明胶：0.2g·kg-1
糊精：4g·kg-1
硝酸钠：1.8g·kg-1。
3.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:960g·kg-1
乙酸铟：25g·kg-1
N-甲基吡咯烷酮:9g·kg-1
明胶：0.5g·kg-1
糊精：4.5g·kg-1
硝酸钠：1g·kg-1。
4.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:960g·kg-1
乙酸铟：25g·kg-1
N-甲基吡咯烷酮:10g·kg-1
明胶：0.5g·kg-1
糊精：3.5g·kg-1
硝酸钠：1g·kg-1。
5.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:970g·kg-1
乙酸铟：15g·kg-1
N-甲基吡咯烷酮:7g·kg-1
明胶：0.5g·kg-1
糊精：6g·kg-1
硝酸钠：1.5g·kg-1。
6.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:970g·kg-1
乙酸铟：15g·kg-1
N-甲基吡咯烷酮:7g·kg-1
明胶：0.6g·kg-1
糊精：4.4g·kg-1
硝酸钠：3g·kg-1。
7.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:970g·kg-1
乙酸铟：15g·kg-1
N-甲基吡咯烷酮:8g·kg-1
明胶：0.8g·kg-1
糊精：4.2g·kg-1
硝酸钠：2g·kg-1。
8.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:970g·kg-1
乙酸铟：20g·kg-1
N-甲基吡咯烷酮:5g·kg-1
明胶：0.5g·kg-1
糊精：3.5g·kg-1
硝酸钠：1g·kg-1。
9.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:980g·kg-1
乙酸铟：10g·kg-1
N-甲基吡咯烷酮:5g·kg-1
明胶：0.1g·kg-1
糊精：3.9g·kg-1
硝酸钠：1g·kg-1。
10.如权利要求1所述的一种无氰镀铟的电镀液，其特征在于：一种无氰镀铟的电镀液的配方由以下组成：
硝酸1-甲基-3-乙基咪唑:960g·kg-1
乙酸铟：30g·kg-1
N-甲基吡咯烷酮:5g·kg-1
明胶：0.5g·kg-1
糊精：3.5g·kg-1
硝酸钠：1g·kg-1。
CN201310065884.4A 2013-03-01 2013-03-01 一种无氰镀铟的电镀液 Expired - Fee Related CN103122471B (zh)