CN103114316B - 一种环境友好的镀镓用电镀液 - Google Patents

一种环境友好的镀镓用电镀液 Download PDF

Info

Publication number
CN103114316B
CN103114316B CN201310065803.0A CN201310065803A CN103114316B CN 103114316 B CN103114316 B CN 103114316B CN 201310065803 A CN201310065803 A CN 201310065803A CN 103114316 B CN103114316 B CN 103114316B
Authority
CN
China
Prior art keywords
electroplate liquid
gallium
eco
friendly plating
sodiumnitrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310065803.0A
Other languages
English (en)
Other versions
CN103114316A (zh
Inventor
田鹏
赵志刚
宋杨杨
孙露
杜文乐
于璐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Normal University
Original Assignee
Shenyang Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Normal University filed Critical Shenyang Normal University
Priority to CN201310065803.0A priority Critical patent/CN103114316B/zh
Publication of CN103114316A publication Critical patent/CN103114316A/zh
Application granted granted Critical
Publication of CN103114316B publication Critical patent/CN103114316B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种环境友好的镀镓用电镀液（g·kg-1），其由以下成份组成：硝酸N-正丁基吡啶:955～965，氯化镓：20～25，N-甲基吡咯烷酮:2～4，乙二醇：4～6，明胶：4～5，硝酸钠：4～6。此电镀液具有一些独特的性能，如较低的熔点、良好的导电性、可以忽略的蒸汽压、较宽的使用温度及特殊的溶解性等。在电镀工业中，电镀液要作为电镀废物加以废弃处理，因此，产生环境污染和处理成本。采用新电镀液进行电镀时，购买电镀液需要消耗大量成本。本发明使电镀液循环多次再利用成为可能，通过电镀液的循环使用，减少了电镀液废物、环境污染和处理成本。

Description

一种环境友好的镀镓用电镀液
技术领域:本发明涉及一种电镀液，是一种环境友好的镀镓用电镀液。
背景技术:稀散金属是指一系列稀有金属元素，包括：镓(Ga)、铟(In)、铊(Tl)、锗(Ge)、硒(Se)、碲(Te)和铼(Re)，稀散金属是我国的优势资源。从镓的用途看，其单质金属及合金具有许多特殊性能，是当今高新技术的支撑材料，已成为冶金、机械、化工、轻工、纺织、电子及医药等工业尤其是原子能、宇航、卫星通讯、能源等尖端技术领域内不可缺少的新兴材料。传统的冶炼、精炼及合金制备方法已不能完全满足当今生产稀散金属及其合金的需要，且传统的方法也存在不同程度的缺点，如高温操作、能耗高、环境污染严重等，因此需要寻求一种新的方法，一种环境友好的镀镓用电镀液的出现为此提供了一种新的可能。在电镀工业中，电镀液要作为电镀废物加以废弃处理，因此，产生环境污染和处理成本。采用新电镀液进行电镀时，购买电镀液需要消耗大量成本。
为实现上述目的，本发明采用的技术方案是：一种环境友好的镀镓用电镀液（g·kg-1）的配方：
硝酸N-正丁基吡啶:955～965
氯化镓：20～25
N-甲基吡咯烷酮:2～4
乙二醇：4～6
明胶：4～5
硝酸钠：4～6。
此电镀液具有一些独特的性能，如较低的熔点、良好的导电性、可以忽略的蒸汽压、较宽的使用温度及特殊的溶解性等。在电镀工业中，电镀液要作为电镀废物加以废弃处理，因此，产生环境污染和处理成本。采用新电镀液进行电镀时，购买电镀液需要消耗大量成本。本发明使电镀液循环多次再利用成为可能，通过电镀液的循环使用，减少了电镀液废物、环境污染和处理成本。
具体实施方式：
一种环境友好的镀镓用电镀液,使用原料：硝酸N-正丁基吡啶,氯化镓,N-甲基吡咯烷酮,乙二醇,明胶,硝酸钠。
实施例1：
硝酸N-正丁基吡啶:955
氯化镓：25
N-甲基吡咯烷酮:4
乙二醇：6
明胶：4
硝酸钠：6。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例2：
硝酸N-正丁基吡啶:955
氯化镓：24
N-甲基吡咯烷酮:4
乙二醇：6
明胶：5
硝酸钠：6。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例3：
硝酸N-正丁基吡啶:960
氯化镓：22
N-甲基吡咯烷酮:3
乙二醇：4
明胶：5
硝酸钠：6。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例4：
硝酸N-正丁基吡啶:960
氯化镓：22
N-甲基吡咯烷酮:4
乙二醇：6
明胶：4
硝酸钠：4。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例5：
硝酸N-正丁基吡啶:960
氯化镓：22
N-甲基吡咯烷酮:2
乙二醇：5
明胶：5
硝酸钠：6。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例6：
硝酸N-正丁基吡啶:960
氯化镓：22
N-甲基吡咯烷酮:3
乙二醇：5
明胶：5
硝酸钠：5。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例7：
硝酸N-正丁基吡啶:960
氯化镓：22
N-甲基吡咯烷酮:2
乙二醇：6
明胶：5
硝酸钠：5。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例8：
硝酸N-正丁基吡啶:965
氯化镓：20
N-甲基吡咯烷酮:3
乙二醇：4
明胶：4
硝酸钠：4。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
实施例9：
硝酸N-正丁基吡啶:965
氯化镓：20
N-甲基吡咯烷酮:2
乙二醇：4
明胶：4
硝酸钠：5。
取上述组分，混合成1000克的一种环境友好的镀镓用电镀液。
用本发明电镀时，要求溶液pH:6.0～7.5，溶液温度（℃）：25～30,电流密度（A/dm2）:1.5～2.5。

Claims (10)

1.一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:955～965g·kg-1
氯化镓：20～25g·kg-1
N-甲基吡咯烷酮:2～4g·kg-1
乙二醇：4～6g·kg-1
明胶：4～5g·kg-1
硝酸钠：4～6g·kg-1。
2.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:955g·kg-1
氯化镓：25g·kg-1
N-甲基吡咯烷酮:4g·kg-1
乙二醇：6g·kg-1
明胶：4g·kg-1
硝酸钠：6g·kg-1。
3.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:955g·kg-1
氯化镓：24g·kg-1
N-甲基吡咯烷酮:4g·kg-1
乙二醇：6g·kg-1
明胶：5g·kg-1
硝酸钠：6g·kg-1。
4.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:960g·kg-1
氯化镓：22g·kg-1
N-甲基吡咯烷酮:3g·kg-1
乙二醇：4g·kg-1
明胶：5g·kg-1
硝酸钠：6g·kg-1。
5.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:960g·kg-1
氯化镓：22g·kg-1
N-甲基吡咯烷酮:4g·kg-1
乙二醇：6g·kg-1
明胶：4g·kg-1
硝酸钠：4g·kg-1。
6.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:960g·kg-1
氯化镓：22g·kg-1
N-甲基吡咯烷酮:2g·kg-1
乙二醇：5g·kg-1
明胶：5g·kg-1
硝酸钠：6g·kg-1。
7.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:960g·kg-1
氯化镓：22g·kg-1
N-甲基吡咯烷酮:3g·kg-1
乙二醇：5g·kg-1
明胶：5g·kg-1
硝酸钠：5g·kg-1。
8.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:960g·kg-1
氯化镓：22g·kg-1
N-甲基吡咯烷酮:2g·kg-1
乙二醇：6g·kg-1
明胶：5g·kg-1
硝酸钠：5g·kg-1。
9.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:965g·kg-1
氯化镓：20g·kg-1
N-甲基吡咯烷酮:3g·kg-1
乙二醇：4g·kg-1
明胶：4g·kg-1
硝酸钠：4g·kg-1。
10.如权利要求1所述的一种环境友好的镀镓用电镀液，其特征在于：一种环境友好的镀镓用电镀液的配方由以下组成：
硝酸N-正丁基吡啶:965g·kg-1
氯化镓：20g·kg-1
N-甲基吡咯烷酮:2g·kg-1
乙二醇：4g·kg-1
明胶：4g·kg-1
硝酸钠：5g·kg-1。
CN201310065803.0A 2013-03-01 2013-03-01 一种环境友好的镀镓用电镀液 Expired - Fee Related CN103114316B (zh)