CN103113790A - Environment-friendly paint - Google Patents
Environment-friendly paint Download PDFInfo
- Publication number
- CN103113790A CN103113790A CN2012105430666A CN201210543066A CN103113790A CN 103113790 A CN103113790 A CN 103113790A CN 2012105430666 A CN2012105430666 A CN 2012105430666A CN 201210543066 A CN201210543066 A CN 201210543066A CN 103113790 A CN103113790 A CN 103113790A
- Authority
- CN
- China
- Prior art keywords
- parts
- glycol ether
- environmental protection
- coating material
- protection coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly paint which is prepared from the following components in parts by weight: 2-6 parts of castor oil, 1-3 parts of pearl essence, 10-15 parts of glycol ether acetate, 5-10 parts of isoamyl butyrate, 5-10 parts of ethylene glycol monobutyl ether, 5-15 parts of methyl isobutyl carbinol, 3-6 parts of methyl cellulose, 1-2 parts of tourmaline, 10-15 parts of titanium white, 20-25 parts of butyl glycidyl ether, 1-2 parts of alum, 3-8 parts of kaolin, 10-15 parts of potassium silicate, 10-15 parts of styrene-acrylic emulsion, 1-5 parts of lime and 5-10 parts of chloroprene rubber. The paint provided by the invention contains less harmful substances, has favorable air permeability, and can enable anions in the paint to be dispersed uniformly and adsorbed firmly.
Description
Technical field
The invention belongs to paint field, relate to a kind of environmental protection coating material.
Background technology
Easily distribute objectionable impurities due to interior wall coating in house decoraton, HUMAN HEALTH is produced larger harm, can discharge far interior wall coating therefore those skilled in the art provide several in recent years, to reach the purpose of antibiotic health.But these coating need to increase the performances such as its tack, still have some pollution in the raw material of increase, and 30 ℃ are not good enough with upward stability, the easy efflorescence of coatingsurface, and cost is high.
Summary of the invention
The objective of the invention is, a kind of environmental protection coating material is provided, its low cost of manufacture contains hazardous substance few.
the present invention for achieving the above object, be achieved through the following technical solutions: a kind of environmental protection coating material, component and the proportioning of this coating are as follows, in weight part: Viscotrol C 2-6 part, pearlescence 1-3 part, ethylene glycol ether acetate 10-15 part, isoamyl butyrate 5-10 part, butyl glycol ether 5-10 part, methyl isobutyl carbinol 5-15 part, methylcellulose gum 3-6 part, tourmalinite 1-2 part, titanium dioxide 10-15 part, butylglycidyl ether 20-25 part, alum 1-2 part, kaolin 3-8 part, potassium silicate 10-15 part, benzene emulsion 10-15 part, lime is 1-5 part, chloroprene rubber 5-10 part.
The preparation method of described a kind of environmental protection coating material comprises the steps:
1. get by weight Viscotrol C, ethylene glycol ether acetate, pearlescence, isoamyl butyrate, butyl glycol ether, methyl isobutyl carbinol, methylcellulose gum, titanium dioxide, butylglycidyl ether, alum, potassium silicate, chloroprene rubber and benzene emulsion, inserting stirs under 60-80 ℃ in reactor, and to make compound standby;
2. get by weight tourmalinite, kaolin and lime pulverizing standby to nano level;
3. step mixed material heating is 1. added step nano level raw material 2. again after 60-80 ℃, stirred 10-12 hour, obtain environmental protection coating material.
Interior wall coating of the present invention can discharge far infrared and negative ion at normal temperatures, and it is few to contain hazardous substance, its good permeability, and can make negative ion Uniform Dispersion and absorption in coating firm, make and take negative oxygen ion and be absorbed by the body, thereby the promotion body metabolism, and can make negative ion better the various viruses of absorption, bacterium, in and the toxic gases such as formaldehyde, toluene.The present invention compared with similar products, cost is low.
Embodiment
Embodiment 1
A kind of environmental protection coating material, component and the proportioning of this coating are as follows, in weight part: 2 parts of Viscotrol C, 1 part of pearlescence, 10 parts of ethylene glycol ether acetates, 5 parts of isoamyl butyrates, 5 parts of butyl glycol ethers, 5 parts of methyl isobutyl carbinols, 3 parts of methylcellulose gum, 1 part, tourmalinite, 10 parts of titanium dioxides, 20 parts of butylglycidyl ethers, 1 part, alum, 3 parts of kaolin, 10 parts of potassium silicates, 10 parts of benzene emulsions, lime are 1 part, 5 parts of chloroprene rubbers.
The preparation method of environmental protection coating material comprises the steps:
1. get by weight Viscotrol C, ethylene glycol ether acetate, pearlescence, isoamyl butyrate, butyl glycol ether, methyl isobutyl carbinol, methylcellulose gum, titanium dioxide, butylglycidyl ether, alum, potassium silicate, chloroprene rubber and benzene emulsion, inserting stirs under 60 ℃ in reactor, and to make compound standby;
2. get by weight tourmalinite, kaolin and lime pulverizing standby to nano level;
3. add again step nano level raw material 2. with after step mixed material heating to 60 1. ℃, stirred 12 hours, obtain environmental protection coating material.
The equipment that uses in the inventive method is known technology.
Embodiment 2
A kind of environmental protection coating material, component and the proportioning of this coating are as follows, in weight part: 6 parts of Viscotrol C, 3 parts of pearlescences, 15 parts of ethylene glycol ether acetates, 10 parts of isoamyl butyrates, 10 parts of butyl glycol ethers, 15 parts of methyl isobutyl carbinols, 6 parts of methylcellulose gum, 2 parts, tourmalinite, 15 parts of titanium dioxides, 25 parts of butylglycidyl ethers, 2 parts, alum, 8 parts of kaolin, 15 parts of potassium silicates, 15 parts of benzene emulsions, lime are 5 parts, 10 parts of chloroprene rubbers.
The preparation method of described a kind of environmental protection coating material comprises the steps:
1. get by weight Viscotrol C, ethylene glycol ether acetate, pearlescence, isoamyl butyrate, butyl glycol ether, methyl isobutyl carbinol, methylcellulose gum, titanium dioxide, butylglycidyl ether, alum, potassium silicate, chloroprene rubber and benzene emulsion, inserting stirs under 80 ℃ in reactor, and to make compound standby;
2. get by weight tourmalinite, kaolin and lime pulverizing standby to nano level;
3. add again step nano level raw material 2. with after step mixed material heating to 80 1. ℃, stirred 10 hours, obtain environmental protection coating material.
Embodiment 3
A kind of environmental protection coating material, component and the proportioning of this coating are as follows, in weight part: 3 parts of Viscotrol C, 2 parts of pearlescences, 12 parts of ethylene glycol ether acetates, 8 parts of isoamyl butyrates, 7 parts of butyl glycol ethers, 10 parts of methyl isobutyl carbinols, 5 parts of methylcellulose gum, 2 parts, tourmalinite, 12 parts of titanium dioxides, 23 parts of butylglycidyl ethers, 1 part, alum, 5 parts of kaolin, 13 parts of potassium silicates, 11 parts of benzene emulsions, lime are 3 parts, 6 parts of chloroprene rubbers.
The preparation method of described a kind of environmental protection coating material comprises the steps:
1. get by weight Viscotrol C, ethylene glycol ether acetate, pearlescence, isoamyl butyrate, butyl glycol ether, methyl isobutyl carbinol, methylcellulose gum, titanium dioxide, butylglycidyl ether, alum, potassium silicate, chloroprene rubber and benzene emulsion, inserting stirs under 70 ℃ in reactor, and to make compound standby;
2. get by weight tourmalinite, kaolin and lime pulverizing standby to nano level;
3. add again step nano level raw material 2. with after step mixed material heating to 70 1. ℃, stirred 11 hours, obtain environmental protection coating material.
Claims (2)
1. environmental protection coating material, it is characterized in that: component and the proportioning of this coating are as follows, in weight part: Viscotrol C 2-6 part, pearlescence 1-3 part, ethylene glycol ether acetate 10-15 part, isoamyl butyrate 5-10 part, butyl glycol ether 5-10 part, methyl isobutyl carbinol 5-15 part, methylcellulose gum 3-6 part, tourmalinite 1-2 part, titanium dioxide 10-15 part, butylglycidyl ether 20-25 part, alum 1-2 part, kaolin 3-8 part, potassium silicate 10-15 part, benzene emulsion 10-15 part, lime are 1-5 part, chloroprene rubber 5-10 part.
2. a method for preparing environmental protection coating material as claimed in claim 1, is characterized in that: comprise the steps:
1. get Viscotrol C, ethylene glycol ether acetate, pearlescence, isoamyl butyrate, butyl glycol ether, methyl isobutyl carbinol, methylcellulose gum, titanium dioxide, butylglycidyl ether, alum, potassium silicate, chloroprene rubber and benzene emulsion by described weight part, inserting stirs under 60-80 ℃ in reactor, and to make compound standby;
2. get tourmalinite, kaolin and lime pulverizing by described weight part standby to nano level;
3. step mixed material heating is 1. added step nano level raw material 2. again after 60-80 ℃, stirred 10-12 hour, obtain environmental protection coating material.