CN103103807A - Production technology of antimicrobial copper ammonia blended fabric - Google Patents
Production technology of antimicrobial copper ammonia blended fabric Download PDFInfo
- Publication number
- CN103103807A CN103103807A CN2012104461239A CN201210446123A CN103103807A CN 103103807 A CN103103807 A CN 103103807A CN 2012104461239 A CN2012104461239 A CN 2012104461239A CN 201210446123 A CN201210446123 A CN 201210446123A CN 103103807 A CN103103807 A CN 103103807A
- Authority
- CN
- China
- Prior art keywords
- copper ammonia
- cuprammonium
- fabric
- production technology
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production technology of antimicrobial copper ammonia blended fabric. The production technology comprises the processing steps of (1), blending copper ammonia fiber, natural silk and cotton fiber to obtain a copper ammonia blended gray fabric; (2), washing the copper ammonia blended gray fabric in a water washer with the bath ratio of 1:(30-50), and adding neutral cleaning agent, wherein the water temperature is 60 DEG C to 65 DEG C; (3), immersing the copper ammonia blended gray fabric washed by water into water with the bath ratio of 1:(10-15), adding neutral scouring agent solution with the addition amount of 5-10g per liter of water, and processing for 0.5hour to 1hour, wherein the scouring temperature is 65 DEG C to 70 DEG C; (4), putting the scoured copper ammonia blended gray fabric into a dyeing machine, adding softening agent and leveling agent; and (5), rinsing and drying, so as to finally obtain the antimicrobial copper ammonia blended fabric. The antimicrobial copper ammonia blended fabric is obtained by blending copper ammonia fiber, natural silk and cotton fiber; the antimicrobial property of the copper ammonia fiber is not likely to be destroyed, and meanwhile the antimicrobial copper ammonia blended fabric is more comfortable in wearing.
Description
Technical field
The present invention relates to a kind of fabric, especially a kind of antimicrobial copper polyurethane fabric belongs to the textile garment technical field.
Background technology
Copper ammonia fibre is a kind of regenerated celulose fibre, it is that the natural cellulosic feedstocks such as cotton linter are dissolved in the liquor ammoniae fortis of Kocide SD or alkaline cupric salt, be made into spinning solution, copper ammonia fibre element molecular compound disintegrating and regeneration goes out cellulose in coagulating bath, the hydrate cellulose of generation through after process and namely obtain copper ammonia fibre.The cross section of copper ammonia fibre is rounded, and without skin-core structure, fiber can bear highly to carry to be stretched, and the monofilament that makes is thinner, so fabric is soft, gloss is soft, and silky touch is arranged.Because copper ammonia fibre is poor to the resistivity of the oxidants such as chlorine bleaches, hydrogen peroxide, so there is certain difficulty in the fabric of copper ammonia fibre and other fiber blends in follow-up pre-treatment, dyeing and rear arrangement process.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of production technology of antibiotic cuprammonium blended yarn woven fabric is provided, this cuprammonium blended yarn woven fabric is obtained by copper ammonia fibre, silk and cotton fiber blending, can not destroy the anti-microbial property of copper ammonia fibre, has good wearability.
According to technical scheme provided by the invention, the production technology of described antibiotic cuprammonium blended yarn woven fabric is characterized in that, comprises following processing step:
(1) copper ammonia fibre, silk and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, silk and cotton fiber is 35 ~ 40:20 ~ 25:30 ~ 35;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 ℃, and washing time is 0.5 ~ 1 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:10 ~ 15, and to add mass percentage concentration be 30 ~ 35% neutral scouring agent solution, and addition is every premium on currency 5 ~ 10g, processes 0.5 ~ 1 hour, and concise temperature is 65 ~ 70 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:10 ~ 13, and every premium on currency adds 1 ~ 2g softener and 1 ~ 3g levelling agent, is warming up to 70 ~ 90 ℃, is incubated 10 ~ 15 minutes; Be warming up to again 110 ~ 120 ℃, be incubated 10 ~ 15 minutes; Be warming up to again 120 ~ 130 ℃, be incubated 30 ~ 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry obtain described antibiotic cuprammonium blended yarn woven fabric.
Programming rate in step (4) is 1 ~ 2 ℃/minute.
The production technology of antibiotic cuprammonium blended yarn woven fabric of the present invention adopts copper ammonia fibre, silk and cotton fiber blending to obtain, and can not destroy the anti-microbial property of copper ammonia fibre, has simultaneously snugness of fit preferably.
The specific embodiment
The invention will be further described below in conjunction with specific embodiment.Neutral scouring agent used in the present invention is neutral nonionic scouring agent, can be used for the pre-treatment of cotton and synthetic fabrics; The scouring agent QTQ-105 that the neutral scouring agent that adopts in the embodiment of the present invention can adopt Guangzhou universe Thailand chemical industry Co., Ltd to produce.
Embodiment one: a kind of production technology of antibiotic cuprammonium blended yarn woven fabric comprises following processing step:
(1) copper ammonia fibre, silk and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, silk and cotton fiber is 35:20:30;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:30, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3g, and water temperature is 60 ℃, and washing time is 1 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:10, and to add mass percentage concentration be 30% neutral scouring agent solution, and addition is every premium on currency 5g, processes 0.5 hour, and concise temperature is 65 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:10, and every premium on currency adds 1g softener and 1g levelling agent, is warming up to 70 ℃, is incubated 10 minutes; Be warming up to again 110 ℃, be incubated 10 minutes; Be warming up to again 120 ℃, be incubated 30 minutes; Cool to room temperature, discharge dye liquor; Described programming rate is 1 ℃/minute;
(5) rinsing, oven dry obtain described antibiotic cuprammonium blended yarn woven fabric.
Embodiment two: a kind of production technology of antibiotic cuprammonium blended yarn woven fabric comprises following processing step:
(1) copper ammonia fibre, silk and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, silk and cotton fiber is 40:25:35;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 5g, and water temperature is 65 ℃, and washing time is 0.5 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:15, and to add mass percentage concentration be 35% neutral scouring agent solution, and addition is every premium on currency 10g, processes 1 hour, and concise temperature is 70 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:13, and every premium on currency adds 2g softener and 3g levelling agent, is warming up to 90 ℃, is incubated 15 minutes; Be warming up to again 120 ℃, be incubated 15 minutes; Be warming up to again 130 ℃, be incubated 45 minutes; Cool to room temperature, discharge dye liquor; Described programming rate is 2 ℃/minute;
(5) rinsing, oven dry obtain described antibiotic cuprammonium blended yarn woven fabric.
Embodiment three: a kind of production technology of antibiotic cuprammonium blended yarn woven fabric comprises following processing step:
(1) copper ammonia fibre, silk and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, silk and cotton fiber is 36:22:32;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:40, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 4g, and water temperature is 62 ℃, and washing time is 0.6 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:12, and to add mass percentage concentration be 32% neutral scouring agent solution, and addition is every premium on currency 6g, processes 0.6 hour, and concise temperature is 68 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:12, and every premium on currency adds 1.5g softener and 2g levelling agent, is warming up to 80 ℃, is incubated 12 minutes; Be warming up to again 115 ℃, be incubated 12 minutes; Be warming up to again 125 ℃, be incubated 40 minutes; Cool to room temperature, discharge dye liquor; Described programming rate is 1.5 ℃/minute;
(5) rinsing, oven dry obtain described antibiotic cuprammonium blended yarn woven fabric.
Claims (2)
1. the production technology of an antibiotic cuprammonium blended yarn woven fabric, is characterized in that, comprises following processing step:
(1) copper ammonia fibre, silk and cotton fiber blending are obtained cuprammonium blending grey cloth, the mass ratio of copper ammonia fibre, silk and cotton fiber is 35 ~ 40:20 ~ 25:30 ~ 35;
(2) washing: cuprammonium blending grey cloth is cleaned in rinsing machine, and bath raio is 1:30 ~ 50, and adds mild detergent, and the consumption of cleaning agent is every premium on currency 3 ~ 5g, and water temperature is 60 ~ 65 ℃, and washing time is 0.5 ~ 1 hour;
(3) concise: the cuprammonium blending grey cloth after washing is immersed in water, and bath raio is 1:10 ~ 15, and to add mass percentage concentration be 30 ~ 35% neutral scouring agent solution, and addition is every premium on currency 5 ~ 10g, processes 0.5 ~ 1 hour, and concise temperature is 65 ~ 70 ℃;
(4) dyeing: the cuprammonium blending grey cloth after concise is put into dyeing machine, and bath of dye liquor is than being 1:10 ~ 13, and every premium on currency adds 1 ~ 2g softener and 1 ~ 3g levelling agent, is warming up to 70 ~ 90 ℃, is incubated 10 ~ 15 minutes; Be warming up to again 110 ~ 120 ℃, be incubated 10 ~ 15 minutes; Be warming up to again 120 ~ 130 ℃, be incubated 30 ~ 45 minutes; Cool to room temperature, discharge dye liquor;
(5) rinsing, oven dry obtain described antibiotic cuprammonium blended yarn woven fabric.
2. the production technology of antibiotic cuprammonium blended yarn woven fabric as claimed in claim 1, it is characterized in that: the programming rate in step (4) is 1 ~ 2 ℃/minute.