CN103059799B - 常温固化雷达吸波涂料用粘结剂及制备方法 - Google Patents
常温固化雷达吸波涂料用粘结剂及制备方法 Download PDFInfo
- Publication number
- CN103059799B CN103059799B CN201210590759.0A CN201210590759A CN103059799B CN 103059799 B CN103059799 B CN 103059799B CN 201210590759 A CN201210590759 A CN 201210590759A CN 103059799 B CN103059799 B CN 103059799B
- Authority
- CN
- China
- Prior art keywords
- parts
- polyurethane prepolymer
- binding agent
- preparation
- absorbing coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (2)