CN103059663A - 一种超耐久自清洁反射隔热防伪涂料技术领域 - Google Patents
一种超耐久自清洁反射隔热防伪涂料技术领域 Download PDFInfo
- Publication number
- CN103059663A CN103059663A CN2012105777008A CN201210577700A CN103059663A CN 103059663 A CN103059663 A CN 103059663A CN 2012105777008 A CN2012105777008 A CN 2012105777008A CN 201210577700 A CN201210577700 A CN 201210577700A CN 103059663 A CN103059663 A CN 103059663A
- Authority
- CN
- China
- Prior art keywords
- reflective insulation
- automatically cleaning
- coating
- agent
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种超耐久自清洁反射隔热防伪涂料。该超耐久自清洁反射隔热防伪涂料包括：水、防冻剂、增稠剂、润湿剂、分散剂、消泡剂、多功能助剂、pH调节剂、杀菌剂、金红石钛白粉、环保型彩色混相无机颜料、成膜助剂、干膜防霉剂、自清洁助剂、改性氟碳乳液、遮盖性空心微乳液、高强度空心玻璃微珠、空心陶瓷微粉组分。该涂料采用的环保型彩色混相无机颜料具有卓越的耐久性、优异的反射红外线功能，具有优异的隔热降温、环保节能的效果；此外该颜料还具有仿叶绿素功能，可用于国防军事领域的防伪，同时本发明具有极佳的抗沾污、不黄变、抗碱、抗酸雨、抗盐雾、及超长耐候性、超长耐久性和自清洁功能。
Description
本发明涉及一种化工涂料领域，具体涉及一种超耐久自清洁反射隔热防伪涂料。
背景技术
由于长时间受太阳照射的建筑外表面的温度持续升高，建筑外表面是水泥、混凝土、瓷砖、金属、保温砖等建筑材料外表面的温度可以达到40-50℃，彩钢板、防水材料上温度可达到60℃，达到烫人的温度。在这样的建筑外表面高温下，居住室内、厂房车间等的气温必然的升高，给正常人类居住、材料存放、设备的安全都造成很大的影响，有可能会产生***等极大的安全隐患，如果温度过高，需要降温，同时造成了能源的极大浪费。
为了减少太阳的热辐射，通过提高反射减少对太阳光热量的吸收，因此具有隔热、反射降温、防腐等功能的涂料应运而生，成为涂料化工行业的迫切需要，这些涂料很大程度上降低了太阳热辐射危害具有极好的市场前景。但是，传统的反射隔热材料存在一定的毒性，并且化学性质不稳定、不易长期保存、热反射隔热性能随时间及环境的变化而变化等的缺陷。
发明内容
本发明的目的在于克服上述不足，提供一种环保性好，具有良好的防潮、防水、隔音、防污、防腐、持久自清洁，且具有防伪装功能及性能稳定的超耐久自清洁反射隔热防伪涂料。
本发明的目的是这样来实现的：一种超耐久自清洁反射隔热防伪涂料，该涂料按重量百分含量包括如下组分：
水 10~30%
防冻剂 1~5 %
增稠剂 1~5%
润湿剂 0.5~3%
分散剂 0.5~3%
消泡剂 0.3~3%
多功能助剂、pH调节剂 0.5~3%
杀菌剂 0.5~3%
金红石钛白粉 0~20%
环保型彩色混相无机颜料 0~20%
成膜助剂 1~3%
干膜防霉剂 0.5~3%
自清洁助剂 0~2%
改性氟碳乳液 30~50%
遮盖性空心微乳液 5~15%
空心玻璃微珠 5~25 %
空心陶瓷微粉 0~10%
上述各组分之和为100%。
优选的技术方案为，所述防冻剂为丙二醇，所述增稠剂为丙烯酸乳液；
所述润湿剂为聚乙二醇辛基苯基醚（TRITON X-100），所述分散剂（TRITON CF-10），所述消泡剂为二氧化硅衍生物（SN-154）；
所述多功能助剂、pH调节剂为2- 氨基 -2- 甲基 -1- 丙醇（AMP95）；
所述杀菌剂为ACTICIDE HF，即：5-氯-2-甲基-4-异噻唑啉-3酮，2-甲基-4异噻唑啉-3-酮和甲醛浓缩液的混合物；
所述金红石钛白粉为R902+，它经特殊表面处理，具有超长耐候性、易分散、高白度、高遮盖力和优异的光反射性能；
所述环保型彩色混相无机颜料具有卓越的耐久性、优异的反射红外线功能，具有优异的隔热降温、环保节能的效果；此外该颜料还具有仿叶绿素功能，可用于国防军事的防伪涂料领域。
所述成膜助剂为TEXANOL，即：2,2,4-三甲基-1,3-戊二醇单异丁酸酯，改善涂料的聚结性、耐候性耐、擦洗性及展色性，同时具有良好的储存稳定性。
所述自清洁助剂可以为自清洁助剂BYK-9131，其作用为疏水并且不吸尘，极易被雨水冲刷干净，具有“持久自清洁”的效果；
所述改性氟碳乳液具有极佳的耐水性及超长耐候性，并且抗沾污、不黄变、抗碱、抗酸雨、抗盐雾、漆膜光亮、丰满、流动性好。
所述遮盖性空心微乳液具有中空结构，其外部壳层聚合物与空腔内的空气对光的折射系数不同，所以入射光能被有效散射，从而使漆膜的反射隔热效果显著提高，同时可以降低粒径较大的空心玻璃珠的用量，使涂膜的外观得到改善，具有优异的白度以及良好的涂布性能，可以用作白色颜料、抗紫外线添加剂和手感改性剂等。
所述高强度空心玻璃微珠导热系数低，λ=0.023W/m·K，起到很好的隔热和降噪音的作用，具有高效的填充性，低吸油量，密度低，但粒径较大，表面状态一般。
所述空心陶瓷微粉导热系数低，λ=0.023W/m·K，起到很好的隔热和降噪音的作用，高效的填充性，低吸油量，密度较高，但粒径小，表面状态好。
本发明是将航天飞机所使用的空间高科技材料转为民用的一种全新涂料。其开发目的是为了永久解决房屋反射隔热保温的烦恼问题。该涂料除了具有良好的防潮、防水、隔音、防污、防腐外装饰作用外，还具有很强的隔热保温作用，使房屋及容器冬暖夏凉。该反射隔热涂料工程造价低，仅为苯板法外墙外保温工程造价的1/6，但功效相同。通过对组分的合理选择与调配，制得的反射隔热涂料具有如下优点：
（1）节能40%。涂料中含用高科技技术生产的极细高强度遮盖性空心微乳液、高强度空心玻璃微珠、空心陶瓷微粉、导热系数低，λ=0.023W/m·K，具有极强的隔热保温作用，对光和热具有很高的阻断及反射作用；环保型彩色混相无机颜料具有卓越的耐久性、优异的反射红外线功能，具有优异的隔热降温、环保节能的效果；在炎热的夏季可抵抗太阳光和环境热对建筑物的烘烤，使室内温度显著降低，大大减少使用空调时间，明显减少空调费用。在冬季，人和物体的散热，主要是以远红外线辐射方式进行，若是在建筑物内部或外部采用这种高效热反射涂料，即可将大部分红外线辐射热反射回室内，冬季减少热穿墙损耗30%以上，达到冬暖夏凉的效果。由于这种涂料可节能40%，每个家庭住户每年可节省空调电费500元以上。
（2）超耐久。涂料采用全新合成材料和技术，使用了超耐久的改性氟碳乳液、金红石钛白粉、环保型彩色混相无机颜料等具有极佳的抗沾污、不黄变、抗碱、抗酸雨、抗盐雾、及超长耐候性、超长耐久性，使用后形成一层柔韧的防护面，不开裂、不起皮、不粉化，寿命长达25年以上，可长期有效地保护建筑，即使在积水很重的情况下，仍不漏水。
（3）防腐性强。涂料不受动物尿、电池酸、漂白剂、防冻化学品、40%盐酸液损伤、防酸、防碱、防酸雨。
（4）隔音阻燃。涂料隔音阻燃性能较好，明显减少外部噪音，使室内安静舒适，并可阻断燃烧。
（5）具有仿叶绿素功能，可用于国防军事领域的防伪。
（6）持久自清洁。自清洁助剂的添加使涂料形成的涂膜更疏水并且不吸尘，极易被雨水冲刷干净，具有“持久自清洁”的效果，使涂料的反射隔热和防伪性能等更持久和稳定。
（7）完全无毒。涂料使用专门配方，水性涂料无毒无味，对人和环境无害。
（8）使用简单。涂料不需稀释调和便可使用，喷、滚、刷均可，装饰效果优于一般乳胶漆。
具体实施方式
下面结合附实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例一
一种超耐久自清洁反射隔热防伪涂料，该涂料按重量百分含量包括如下组分：
水 11.5%
丙二醇 4%
丙烯酸增稠剂CR 1%
润湿剂TRITON X-100 1.5%
分散剂TRITON CF-10 1.5%
消泡剂SN-154 1%
多功能助剂AMP95 0.5%
杀菌剂ACTICIDE HF 1%
成膜助剂TEXANOL 2%
干膜防霉剂ACTICDE EPW 1%
自清洁助剂BYK-9131 0
改性氟碳乳液 30%
遮盖性空心微乳液 15%
高强度空心玻璃微珠 25%
空心陶瓷微粉 5%
该涂料用作中涂，隔热性能好。
实施例二
一种超耐久自清洁反射隔热防伪涂料，该涂料按重量百分含量包括如下组分：
水 10%
丙二醇 5%
丙烯酸增稠剂CR 1%
润湿剂TRITON X-100 1 .5%
分散剂TRITON CF-10 1%
消泡剂SN-154 1%
多功能助剂AMP95 0.5%
杀菌剂ACTICIDE HF 1%
金红石钛白粉R902+ 5%
环保型彩色混相无机颜料 5%
成膜助剂 TEXANOL 十二碳酯醇 2%
干膜防霉剂ACTICDE EPW 1%
自清洁助剂BYK-9131 1%
改性氟碳乳液 35%
遮盖性空心微乳液 10%
高强度空心玻璃微珠 5%
空心陶瓷微粉 15%
该涂料用作面涂，防伪，反射隔热性能好，外观好，持久自清洁 。
实施例三
一种超耐久自清洁反射隔热防伪涂料，该涂料按重量百分含量包括如下组分：
水 28%
丙二醇 5%
丙烯酸增稠剂CR 5%
润湿剂TRITON X-100 0.5%
分散剂TRITON CF-10 0.5%
消泡剂SN-154 0.4%
多功能助剂AMP95 0.5%
杀菌剂ACTICIDE HF 0.6%
金红石钛白粉R902+ 9.5%
环保型彩色混相无机颜料 5%
成膜助剂 TEXANOL 十二碳酯醇 1%
干膜防霉剂ACTICDE EPW 1%
自清洁助剂BYK-9131 1%
改性氟碳乳液 30%
遮盖性空心微乳液 5%
高强度空心玻璃微珠 5%
空心陶瓷微粉 2%
该涂料用作面涂，封闭性好，外观好，持久自清洁。
以上涂料可应用在国防、工业、农业、储运、建筑、医疗卫生等行业的任何需要反射隔热（或保冷、保温）、军事防伪装及安全防护的场合上。
主要的适用对象为：
管道***：包括高、低温管道；自来水管、输油管、氧气及氟利昂管道；空调送风管道的绝热（隔热、保温、保冷）及防冷凝；冰箱、冰柜的保冷。
设备及容器：包括锅炉、窑炉、，化学设备；石油天然气设备，石油化工设备，烘烤设备，加热设备、冷冻设备，热回收设备、冶金与机械设备，电器设备，医疗设备，交通设备，运输容器，换热器，油箱，油罐，贮罐，危险品容器，冷库，冷藏车等的绝热及防止冷凝。
人员保护：用于机器设备或其它高/低温场所的表面绝热，防止由于接触到过高/低的温度而产生的人员伤害（如锅炉外墙）。
国防军事领域：用于敏感军事设施的防伪装和反射隔热保护。
建筑上及其他：可作为隔热保温、防潮层。在工业厂房及民用建筑上，车、船、集装箱及其它需要绝热的场所上使用。并有防水、防腐蚀作用。汽车、火车、车厢的保温节能；低温地板辐射采暖替代苯乙烯板隔热，塑料、蓬布等隔热绝热使用。
适用效果举例：
钢板粮仓、冷库——***护表面喷涂0.3-0.5mm，仓顶温度最大下降21.6℃，并可防护环境水汽对仓体***护的影响、阻碍水汽冷凝现象的产生，节能30%以上。
丙烯球罐、油罐——外表面喷涂0.3-0.5mm，上部表面温度下降近20℃，未出现温度超过50℃，的现象，减少降温淋水对罐体外表面的腐蚀，起到一定的保护作用。
楼房、厂房屋顶——屋顶喷涂0.4-0.6 mm，在32℃的环境温度下，屋顶温度最大下降18.1℃，日照时段（10：00-7：00）平均下降15.65℃，衰减倍数提高53.9%，延时增加19.75%，极大的减少了太阳热烘烤的感觉。
船舶、车辆、车厢——箱体外表面喷涂0.45-0.5mm，表面温度下降近20℃，箱内温度下降3℃以上，车箱内不感到烘烤。
管道与阀门——95℃热水管到与阀门的外表面喷涂3.0-3.5mm，表面温度下降到30℃。
各种退火炉及加热炉——外表面喷涂0.4-0.5mm，表面温度从84.2℃下降至72.4℃，减少热量损失31%以上，用手捂摸表面无严重灼烫的感觉。
低温交换塔——外表面仅喷涂0.6——1.0mm厚的材料，可以减少冷量损失50%以上，未出现冷凝现象，同时具备防潮/防腐效果。
低温容器——外表面喷涂0.4-0.5mm，可以有效抑制太阳、大地、环境辐射热对设备的影响。
储油（气）罐——储罐外表面喷涂0.4-0.5 mm，表面温度最多下降20℃以上，顶部最高温度未超过50℃。减少油气呼吸损失和淋水降温。
楼房建筑——外面喷涂0.3-0.5mm，形成一个保护罩，保持大楼内部热量或冷气，夏天顶层没有以前烘烤闷热，寒冷的冬季内墙壁很少出现结露。
国防军事领域——外面喷涂0.3-0.5mm，形成一个保护罩，具有优异的防伪功能，还可以有效抑制太阳、大地、环境辐射热的影响。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (6)
1.一种超耐久自清洁反射隔热防伪涂料，其特征在于，所述涂料按重量百分含量包括如下组分：
水 10~30%
防冻剂 1~5 %
增稠剂 1~5%
润湿剂 0.5~3%
分散剂 0.5~3%
消泡剂 0.3~3%
多功能助剂、pH调节剂 0.5~3%
杀菌剂 0.5~3%
金红石钛白粉 0~20%
环保型彩色混相无机颜料 0~20%
成膜助剂 1~3%
干膜防霉剂 0.5~3%
自清洁助剂 0~2%
改性氟碳乳液 30~50%
遮盖性空心微乳液 5~15%
高强度空心玻璃微珠 5~25 %
空心陶瓷微粉 0~10%
上述各组分之和为100%。
2.如权利要求1所述的超耐久自清洁反射隔热防伪涂料，其特征在于，所述防冻剂为丙二醇，所述增稠剂为丙烯酸乳液。
3.如权利要求1所述的超耐久自清洁反射隔热防伪涂料，其特征在于，所述润湿剂为聚乙二醇辛基苯基醚，所述消泡剂为二氧化硅衍生物。
4.如权利要求1所述的超耐久自清洁反射隔热防伪涂料，其特征在于，所述多功能助剂、pH调节剂为2- 氨基 -2- 甲基 -1- 丙醇。
5.如权利要求1所述的超耐久自清洁反射隔热防伪涂料，其特征在于，所述杀菌剂为5-氯-2-甲基-4-异噻唑啉-3酮，2-甲基-4异噻唑啉-3-酮和甲醛浓缩液的混合物。
6.如权利要求1所述的超耐久自清洁反射隔热防伪涂料，其特征在于，所述成膜助剂为2,2,4-三甲基-1,3-戊二醇单异丁酸酯。