CN102952441A - 一种隔热防水涂料 - Google Patents
一种隔热防水涂料 Download PDFInfo
- Publication number
- CN102952441A CN102952441A CN201110242834XA CN201110242834A CN102952441A CN 102952441 A CN102952441 A CN 102952441A CN 201110242834X A CN201110242834X A CN 201110242834XA CN 201110242834 A CN201110242834 A CN 201110242834A CN 102952441 A CN102952441 A CN 102952441A
- Authority
- CN
- China
- Prior art keywords
- heat
- waterproof coating
- coating
- insulating waterproof
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种隔热防水涂料,由如下组分组成:高性能有机硅乳液10%-15%、纯丙乳液23%-25%、钛白粉18%-22%、滑石粉3%-5%、硅藻土2%-3.5%、重质碳酸钙3%-5.1%、煅烧高岭土1.7%-2.2%、陶瓷微珠7%-10%、空心玻璃珠8%-10%、水6%-12%、多功能助剂0.6%-1.2%、疏水剂1.5%-3.2%、助溶剂0.3%-1.0%、消泡剂0.2%-0.3%。该涂料具有隔热、防水、防火、自洁、隔音降噪、保温、节能的效果。
Description
技术领域
本发明涉及一种隔热防水涂料,特别提供一种集隔热、防水、防火、自洁、隔音降噪、保温、节能于一体的涂料,属于精细化工技术领域。
背景技术
乳胶漆的是符合健康环保需求,但常常碰到的麻烦是吸水性强,用于建筑物的装饰保护涂层时,会发生吸水变色。如果基材是水泥组成,进入的水分在干燥时会将其中的盐碱带到墙面,在漆膜表面堆积,不仅降低了水泥的使用寿命,加快对其腐蚀,变形和老化,而且使漆膜变色,破坏。在一些很低PVC配方的建筑涂料中,漆膜比较致密,虽然水分的进入受限制,但一些缓慢进入的水分在迁移过程中透出不平衡,漆膜表面或者漆膜和基材间很容易发生起泡现象,造成漆膜破坏或脱落。漆膜吸水的另一个不良后果是水分和漆膜表面大量的接触会将污染物带入涂层的微孔中或者粘附于漆膜表面形成难看的污迹。
隔热涂料因其具有良好的隔热性能和简单的施工过程,在现代工业和生产中的作用越来越大。在建筑物的表面涂上隔热涂料,能明显降低室内温度,使人们在炎热的夏天有一个良好的工作环境。建筑热反射型隔热涂料具有优异的隔热保温功能,是当今建筑节能材料的研究热点。随着建筑隔热涂料的大力推广,开发经济、方便和隔热效果良好的建筑反射隔热涂料对社会节能具有重大的现实意义。
按照隔热原理,目前的隔热涂料可分为阻隔型隔热涂料、反射型隔热涂料和辐射型隔热涂料。这三类隔热涂料都存在其优缺点,在研究过程中,可以将它们综合起来,充分发挥各自的特点,进行优势互补。目前,随着研究开发的不断深入,技术工艺的不断成熟,集三种隔热功能为一体的高效薄层隔热防腐一体化的水性隔热涂料将成为未来隔热涂料研究的主要方向。
目前,还没有文献报道一种集隔热、防水、防火、自洁、隔音降噪、保温、节能于一体的隔热防水涂料。
发明内容
鉴于现有技术的不足,本发明的目的在于提供一种集隔热、防水、防火、自洁、隔音降噪、保温、节能于一体的隔热防水涂料。
本发明的目的是这样实现的:
一种隔热防水涂料,包含如下重量百分比的组分:
高性能有机硅乳液10%-15% | 纯丙乳液23%-25% |
钛白粉18%-22% | 滑石粉3%-5% |
硅藻土2%-3.5% | 重质碳酸钙3%-5.1% |
煅烧高岭土1.7%-2.2% | 陶瓷微珠7%-10% |
空心玻璃珠8%-10% | 水6%-12% |
多功能助剂0.6%-1.2% | 助溶剂0.3%-1.0% |
消泡剂0.2%-0.3% | 疏水剂1.5%-3.2%。 |
上述的隔热防水涂料,其中,钛白粉、滑石粉、硅藻土、重质碳酸钙或煅烧高岭土的细度研磨至700-800目。
上述的隔热防水涂料,其中,陶瓷微珠或空心玻璃珠的细度研磨至250-350目。
上述的隔热防水涂料,所述的多功能助剂优选为烷基酸聚氧乙烯醚。
上述的隔热防水涂料,所述的助溶剂优选为浓度96%-98%的丙二醇。
上述的隔热防水涂料,所述的消泡剂优选为浓度25%-33%的甲基硅油。
上述的隔热防水涂料,所述的钛白粉为金红石型钛白粉。
本发明涉及的隔热防水涂料适合用于民用领域,如写字楼、医院、酒店、学校、住宅、仓库、大型超市、工厂等建筑物外墙及屋顶的隔热保温。同时更适合工业领域。如铁皮厂房、金属构件、油罐、粮库储罐、冷冻厂、移动油罐车的绝热保护。
与现有技术相比,本发明涉及的隔热防水涂料具有如下优点和显著的进步:
(1)反射99.5%的红外线与90%以上的可见光,并隔绝紫外线。在夏天阳光直射的情况下将绝大部分红外线和可见光反射回去,其次高达86﹪的半球发射率又将涂层表面的热量发射回大气环境中,特别是到了晚上当大气环境温度降低时陶瓷颗粒特殊的发射性又将墙体及室内的蓄热发射到室外,这样室内就不会觉的闷热,特别是金属构建的房屋效果尤为明显,如铁皮厂房、仓库、油罐、粮库储罐、冷冻厂、移动油罐车等。本身极低的热传导系数进一步起到隔热功效。在冬天作为内墙使用的SSM圣姗姆隔热涂料可以把屋内发散的热辐射回来,起到冬暖夏凉的作用。在空调环境中节约大量能源费用。
(2)具有独特 “荷叶般表面效应” 的疏水自洁功能,雨水带着浮尘一起滚落,出污泥而不染,即使经过冲水试验,表面仍保持干燥无水污迹,大大提高因浮尘长时间的积累在隔热涂料表面而降低反射功能。
(3)本发明涉及的隔热防水涂料是一种“长寿”涂料,使用年限可达10~15年,且年限之内的隔热效果基本没有变化。这就相应延长了涂层的隔热效果,降低重复涂装的频率。从长远角度来看,与重涂次数较多、价格相对较低的涂料相比,本发明涉及的隔热防水涂料可有效降低施工成本;同时重涂次数的减少本身节能,可减轻环境负担。
(4)超强附着力和耐侯性,可以确保该涂料适用任何内外墙表面,金属彩钢板,混凝土,腻子,橡胶,木材、玻璃等。
(5)环保、无毒,V.O.C.排放量仅67g/L,显著优于国家标准(我国的内墙涂料V.O.C.排放标准为200g/L。外墙涂料V.O.C.排放标准为700g/L)。
(6)抗化学腐蚀,当成膜时本发明的隔热涂料的微粒排列紧密,形成低孔隙率,使涂层表面形成对潮汽及致腐蚀离子有阻挡作用的保护膜,起到很好的防护作用。
(7)最新复合绝热腔体技术的隔热涂料形成的连续的”绝热”层,可以实现持久的热阻隔,大大降低热传递的发生及声音的绝缘性,起到很好的隔热和降噪音的作用。
(8)具有完美的粘结力和涂膜延展性能,即使涂膜弯曲180度,不会有任何破损,使涂层具有更佳的防水,防污,防腐蚀性能。即使经过冲水试验,表面仍保持干燥无水迹。当本发明的涂料用于层顶有很好的防水性。用于墙面时,防止水分进入涂层产生变色,粉化,起泡脱落,大大延长漆膜的使用破例;另一方面,污染物(酱油、墨水、番茄酱等)液滴难入,灰尘颗粒可被水滴带走,具有好的耐沾污性。
具体实施方式
以下是本发明的具体实施例,对本发明的技术方案做进一步作描述,但是本发明的保护范围并不限于这些实施例。凡是不背离本发明构思的改变或等同替代均包括在本发明的保护范围之内。
实施例1-3 隔热防水涂料的制备
组分含量:
实施例1 | 实施例2 | 实施例3 | |
高性能有机硅乳液 | 10% | 12% | 15% |
纯丙乳液 | 23% | 25% | 25% |
钛白粉 | 22% | 18% | 20% |
滑石粉 | 3% | 5% | 4% |
硅藻土 | 2% | 3.5% | 3.4% |
重质碳酸钙 | 3% | 5.1% | 4.3% |
煅烧高岭土 | 1.7% | 2.2% | 2% |
陶瓷微珠 | 10% | 8% | 7% |
空心玻璃珠 | 10% | 8% | 9% |
水 | 10.5% | 10.5% | 5.9% |
多功能助剂 | 1.1% | 0.8% | 0.6% |
助溶剂 | 0.9% | 0.2% | 0.3% |
消泡剂 | 0.3% | 0.2% | 0.3% |
疏水剂 | 2.5% | 1.5% | 3.2% |
制备工艺:
首先将金红石型氧化钛、滑石粉、硅藻土、重质碳酸钙、煅烧高岭土研磨至细度700-800目,陶瓷微珠、空心玻璃珠的细度至250-350目。
按上述配方将多功能助剂、助溶剂、疏水剂与一部分水在容器中搅拌混合均匀;在慢速搅拌下,加入钛白粉、重质碳酸钙、滑石粉、硅藻土和煅烧高岭土等颜填料,高速搅拌20min后,检测细度,要求细度小于40μm。达到细度要求后,依配方在慢速搅拌下将高性能有机硅乳液、纯丙乳液和消泡剂加入到已分散好的颜料分散液中,以800转/分的速度搅拌45分钟;搅拌均匀后,在200转/分状态下,缓慢添加空心玻璃珠和陶瓷珠粉料,搅拌该混合体系,直至分散均匀,然后添加余量水。 其中,各实施例的消泡剂、多功能助剂、助溶剂、疏水剂分别为:
实施例1 | 实施例2 | 实施例3 | |
多功能助剂 | 烷基酸聚氧乙烯醚 | 烷基酸聚氧乙烯醚 | 烷基酸聚氧乙烯醚 |
助溶剂 | 96%的丙二醇 | 97%的丙二醇 | 98%的丙二醇 |
消泡剂 | 25%的甲基硅油 | 30%的甲基硅油 | 33%的甲基硅油 |
疏水剂 | 奥洁士S2型疏水剂 | 奥洁士S2型疏水剂 | 奥洁士S2型疏水剂 |
按照本发明实施例1-3制备的隔热防水涂料具有如有性能:
(1)特有的高反射和折射率,能有效地折射和反射太阳热能和紫外线,隔绝热 能的传导,使建筑物自动调节温度,真正做到冬暖夏凉,大大降低用户的空调电力能源消耗。
(2)独特 “荷叶般表面效应” 的疏水自洁功能,雨水带着浮尘一起滚落,出污泥而不染,即使经过冲水试验,表面仍保持干燥无水污迹,大大提高因浮尘长时间的积累在隔热涂料表面而降低反射功能。
(3)本发明涉及的隔热防水涂料是一种“长寿”涂料,使用年限可达10~15年,且年限之内的隔热效果基本没有变化。这就相应延长了涂层的隔热效果,降低重复涂装的频率。从长远角度来看,与重涂次数较多、价格相对较低的涂料相比,本发明涉及的隔热防水涂料可有效降低施工成本;同时重涂次数的减少本身节能,可减轻环境负担。
(4)超强附着力和耐侯性,可以确保该涂料适用任何内外墙表面,金属彩钢板,混凝土,腻子,橡胶,木材、玻璃等。
(5)环保、无毒,V.O.C.排放量仅67g/L,显著优于国家标准(我国的内墙涂料V.O.C.排放标准为200g/L。外墙涂料V.O.C.排放标准为700g/L)。
(6)抗化学腐蚀,当成膜时本发明的隔热涂料的微粒排列紧密,形成低孔隙率,使涂层表面形成对潮汽及致腐蚀离子有阻挡作用的保护膜,起到很好的防护作用。
(7)最新复合绝热腔体技术的隔热涂料形成的连续的”绝热”层,可以实现持久的热阻隔,大大降低热传递的发生及声音的绝缘性,起到很好的隔热和降噪音的作用。
(8)具有完美的粘结力和涂膜延展性能,即使涂膜弯曲180度,不会有任何破损,使涂层具有更佳的防水,防污,防腐蚀性能。即使经过冲水试验,表面仍保持干燥无水迹。当本发明的涂料用于层顶有很好的防水性。用于墙面时,防止水分进入涂层产生变色,粉化,起泡脱落,大大延长漆膜的使用破例;另一方面,污染物(酱油、墨水、番茄酱等)液滴难入,灰尘颗粒可被水滴带走,具有好的耐沾污性。
其主要的热工性能见表1。
表1 热工性能(物理性能)指标表
技术指标 | 实施例1 | 实施例2 | 实施例3 |
反射系数 | 87% | 86% | 90% |
太阳光吸收率 | 13% | 13% | 11% |
隔热效率 | 降低14.5℃ | 降低13.7℃ | 降低15.8℃ |
断裂强度 | 0.33kgf/sq mm | 0.35kgf/sq mm | 0.35kgf/sq mm |
极限强度 | 0.34kgf/sq mm | 0.35kgf/sq mm | 0.37kgf/sq mm |
伸长率(弹性系数) | 118% | 119% | 120% |
含固率 | 54% | 58% | 55% |
胶粘强度 | 1.6Mpa | 1.9Mpa | 2.0Mpa |
吸水率(防水率) | 0.5g/d㎡/day | 0.5g/d㎡/day | 0.6g/d㎡/day |
水吸收降低率 | 82% | 84% | 88% |
透气率 | 11 g/d㎡/day | 11 g/d㎡/day | 12g/d㎡/day |
氯离子渗透降低率 | 95% | 94% | 97% |
Claims (7)
1.一种隔热防水涂料,其特征在于:包含如下重量百分比的组分:
高性能有机硅乳液10%-15% 纯丙乳液23%-25%
钛白粉18%-22% 滑石粉3%-5%
硅藻土2%-3.5% 重质碳酸钙3%-5.1%
煅烧高岭土1.7%-2.2% 陶瓷微珠7%-10%
空心玻璃珠8%-10% 水6%-12%
多功能助剂0.6%-1.2% 助溶剂0.3%-1.0%
消泡剂0.2%-0.3% 疏水剂1.5%-3.2%。
2.根据权利要求1所述的隔热防水涂料,其特征在于:所述的钛白粉、滑石粉、硅藻土、重质碳酸钙或煅烧高岭土的细度至700-800目。
3.根据权利要求1所述的隔热防水涂料,其特征在于:所述的陶瓷微珠或空心玻璃珠的细度至250-350目。
4.根据权利要求1所述的隔热防水涂料,其特征在于:所述的多功能助剂为烷基酸聚氧乙烯醚。
5.根据权利要求1所述的隔热防水涂料,其特征在于:所述的助溶剂为浓度96%-98%的丙二醇。
6.根据权利要求1所述的隔热防水涂料,其特征在于:所述的消泡剂为浓度25%-33%的甲基硅油。
7.根据权利要求1所述的隔热防水涂料,其特征在于:所述的钛白粉为金红石型钛白粉。