CN103044899A - 一种聚合物凝胶及其制备方法 - Google Patents
一种聚合物凝胶及其制备方法 Download PDFInfo
- Publication number
- CN103044899A CN103044899A CN2012105689878A CN201210568987A CN103044899A CN 103044899 A CN103044899 A CN 103044899A CN 2012105689878 A CN2012105689878 A CN 2012105689878A CN 201210568987 A CN201210568987 A CN 201210568987A CN 103044899 A CN103044899 A CN 103044899A
- Authority
- CN
- China
- Prior art keywords
- polymer gel
- weight part
- gel
- polyether glycol
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚合物凝胶及其制备方法，以聚醚多元醇、锌催化剂、增塑剂、异氰酸酯为原料，通过调整原料配方与配比参与聚合反应生成性能优越的凝胶。本发明的优点在于：通过本发明配方和生产方法制作的凝胶，手感细腻柔软，澄清透明，冰凉度好，韧性高，更适用于加工高质量的凝胶枕头。
Description
技术领域
本发明涉及一种聚合物凝胶及其制备方法。
背景技术
凝胶是指颗粒大小在1埃到10埃之间的混合物。高分子溶液和某些溶胶，在适当的条件下，整个体系会转变成一种弹性的半固体状态的稠厚物质，失去流动性。这种现象称为胶凝作用,所形成的产物叫做凝胶或冻胶。溶胶或溶液中的胶体粒子或高分子在一定条件下互相连接，形成空间网状结构，结构空隙中充满了作为分散介质的液体，这样一种特殊的分散体系称作凝胶。没有流动性。内部常含有大量液体。
市售的凝胶的缺陷：澄清透明度差，韧性差，长时间保存会发硬。该特性限制了凝胶在较高档次产品上的应用。
发明内容
本发明的目的是提供一种聚合物凝胶及其制备方法，这种聚合物凝胶可用于制备凝胶枕。
为了解决上述技术问题，本发明采用的技术方案为：一种聚合物凝胶，其特征在于：所述聚合物凝胶配方以重量份计如下：聚醚多元醇，羟值32-35mgKOH/g，分子量为5000，50-80重量份，催化剂0.2-0.5重量份，增塑剂10-30重量份，异氰酸酯10-30重量份。
进一步地，所述聚醚多元醇为5020或330N。
进一步地，所述催化剂为锌催化剂。
进一步地，所述增塑剂为环己烷1.2二甲酸二异壬基酯。
一种聚合物凝胶的制备方法，步骤为：（1）原料准备：将聚醚多元醇、催化剂、增塑剂加入反应器中，以500r/min的速度搅拌混合，时间为30min中，混合均匀后转入注塑缸，而异氰酸酯置于另一注塑缸中，待用；（2）聚合反应：将上述两注塑缸内的物料，通过各自的导流管由泵抽入预混罐，以2000r/min搅拌速度瞬间混合均匀后，流入模具中聚合反应，反应温度为40-60℃，塑化时间为7-12min，结束后出料的成品。
进一步地，步骤（1）中所述注塑缸温度均控制为30-40℃。
本发明的优点在于：通过本发明配方和生产方法制作的凝胶，手感细腻柔软，澄清透明，冰凉度好，韧性高，更适用于加工高质量的凝胶制品。
具体实施方式
为了使公众能充分了解本发明的技术实质和有益效果，申请人将对本发明的具体实施方式详细描述，但申请人对实施例的描述不是对技术方案的限制，任何依据本发明构思作形式而非实质的变化都应当视为本发明的保护范围。
本发明的一种聚合物凝胶配方如下：聚醚多元醇，羟值32-35mgKOH/g，分子量为5000，50-80重量份，催化剂0.2-0.5重量份，增塑剂10-30重量份，异氰酸酯10-30重量份。
所述聚醚多元醇为5020或330N；所述催化剂为锌催化剂；所述增塑剂为环己烷1,2二甲酸二异壬基酯。
将上述聚醚多元醇、催化剂、增塑剂加入反应器中，以500r/min的速度搅拌混合，时间为30min中，混合均匀后转入注塑缸，而异氰酸酯置于另一注塑缸中，待用，所述注塑缸温度均控制为30-40℃；将上述两注塑缸内的物料，通过各自的导流管由泵抽入预混罐，以2000r/min搅拌速度瞬间混合均匀后，流入模具中聚合反应，反应温度为40-60℃，塑化时间为7-12min，结束后出料的成品。
实施例1
一种聚合物凝胶配方如下：聚醚多元醇5020 50重量份，锌催化剂0.2重量份，环己烷1.2二甲酸二异壬基酯10重量份，异氰酸酯10重量份，制备过程同上所述。
实施例2
一种聚合物凝胶配方如下：聚醚多元醇330N 80重量份，锌催化剂0.5重量份，环己烷1.2二甲酸二异壬基酯30重量份，异氰酸酯30重量份，制备过程同上所述。
实施例3
一种聚合物凝胶配方如下：聚醚多元醇330N 65重量份，锌催化剂0.3重量份，环己烷1.2二甲酸二异壬基酯20重量份，异氰酸酯20重量份，制备过程同上所述。
按照上述实施1-3制备的聚合物凝胶，手感细腻柔软，澄清透明，冰凉度好，韧性高，更适用于加工高质量的凝胶枕头。
对比例4
配方为，聚醚多元醇3050A65重量份，锡催化剂0.3重量份，环己烷1.2二甲酸二异壬基酯20重量份，异氰酸酯20重量份，制备过程同上所述。
按照对比例制备的聚合物凝胶，手感坚硬，显浑浊，比较脆，舒适度差。
Claims (4)
1.一种聚合物凝胶，其特征在于：所述聚合物凝胶配方以重量份计如下：聚醚多元醇，羟值32-35mgKOH/g，分子量为5000，50-80重量份，锌催化剂0.2-0.5重量份，环己烷1,2二甲酸二壬基酯增塑剂10-30重量份，异氰酸酯10-30重量份。
2.根据权利要求1所述的一种聚合物凝胶，其特征在于：所述聚醚多元醇为5020或330N。
3.一种制备权利要求1所述的聚合物凝胶的方法，其特征在于：（1）原料准备：将聚醚多元醇、催化剂、增塑剂按比例加入反应器中，以500r/min的速度搅拌混合，时间为30min中，混合均匀后转入注塑缸；而异氰酸酯置于另一注塑缸中，待用；（2）聚合反应：将上述两注塑缸内的物料，通过各自的导流管由泵抽入预混罐，以2000r/min搅拌速度瞬间混合均匀后，导流入模具中聚合反应，反应温度为40-60℃，塑化时间为7-12min，结束后出料的成品。
4.根据权利要求3所述的一种聚合物凝胶的制备方法，其特征在于：步骤（1）中所述注塑缸温度均控制为30-40℃。