CN103028853B - 电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法 - Google Patents
电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法 Download PDFInfo
- Publication number
- CN103028853B CN103028853B CN201210581972.5A CN201210581972A CN103028853B CN 103028853 B CN103028853 B CN 103028853B CN 201210581972 A CN201210581972 A CN 201210581972A CN 103028853 B CN103028853 B CN 103028853B
- Authority
- CN
- China
- Prior art keywords
- steel plate
- honeycomb
- powder
- spot welding
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法,所述方法包括以下工艺过程:取一蜂窝钢板,该蜂窝钢板孔壁密布有孔,将C粉与Ti粉按化学计量配置,再加入C粉与Ti粉总量10~20%wt的Ni粉,混匀后制成混合料,用液压机在挤压模具中将混合料压成孔隙率为25~35%的预制块,从挤压模具中顶出预制块后,放入所述蜂窝钢板的蜂窝孔中,然后一起放在钢板基体表面,300℃±10℃一起预热后,保温20min±5min,用交流电阻点焊机点焊焊合,点焊配以尺寸与蜂窝钢板的蜂窝孔相配的蜂窝形电极,最后用带极堆焊机在其表面堆焊上一层合金钢,即成蜂窝陶瓷夹层板。本发明,蜂窝涂层与钢板基体及表层金属均为冶金结合,结合强度高。
Description
技术领域
本发明涉及一种在钢板表面制备蜂窝陶瓷夹层板方法。属表面工程技术领域。
背景技术
蜂窝陶瓷夹层钢板具有很好的抗冲击性能,采用已有技术在钢板表面制备的蜂窝陶瓷夹层钢板大多采用胶粘结合,结合强度低,高温性能差,使用寿命低。
发明内容
本发明的目的在于克服上述不足,提供一种结合强度高、高温性能好、使用寿命长的电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法。
本发明的目的是这样实现的:一种电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法,所述方法包括以下工艺过程:取一蜂窝钢板,该蜂窝钢板孔壁密布有小孔,将C粉与Ti粉按化学计量配置,再加入C粉与Ti粉总量10~20%wt的Ni粉,混匀后制成混合料,用液压机在挤压模具中将混合料压成孔隙率为25~35%的预制块,从挤压模具中顶出预制块后,放入所述蜂窝钢板的蜂窝孔中,然后一起放在钢板基体表面,300℃±10℃一起预热后,保温20min±5 min,用交流电阻点焊机点焊焊合,点焊配以尺寸与蜂窝钢板的蜂窝孔相配的蜂窝形电极,最后用带极堆焊机在其表面堆焊上一层合金钢,即成蜂窝陶瓷夹层板。
本发明的有益效果是:
自蔓延反应产生大量的气体,孔壁带有排气孔的蜂窝板,点焊加压时除起到模具作用外还起到排气作用。本发明,蜂窝涂层与钢板基体及表层金属均为冶金结合,结合强度高、高温性能好、使用寿命长。电阻点焊辅助自蔓延反应热压使涂层致密。涂层中的蜂窝钢板具有阻止裂纹扩展,增加韧性的作用。该夹层钢板具有抗冲击优点。点焊时利用了自蔓延反应热,两种热量叠加节省了能源,降低了原材料成本,工艺过程简单。
具体实施方式
最佳实施例
取孔径为8mm,孔深2mm,壁厚0.5mm规格的蜂窝钢板,该蜂窝钢板孔侧壁密布有¢2mm的孔,将粒度为200目的C粉与Ti粉按原子比为1:1配置,再加入C粉与Ti粉总量10~20%wt的Ni粉,混匀后制成混合料,用液压机在蜂窝型钢模具中将混合料压成孔隙率为25~35%的预制块,从挤压模具中顶出预制块后,放入所述蜂窝钢板的蜂窝孔中,然后一起放在钢板基体表面,300℃±10℃一起预热后,保温20min±5 min,用交流电阻点焊机点焊焊合蜂窝钢板和钢板基体,点焊配以尺寸与蜂窝钢板的蜂窝孔相配的蜂窝形电极,电极压力50kN,电流18kA,焊接时间10s。最后用带极堆焊机在其表面堆焊上一层合金钢,即成蜂窝陶瓷夹层板。
Claims (2)
1.一种电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法,其特征在于:所述方法包括以下工艺过程:取一蜂窝钢板,该蜂窝钢板孔侧壁密布有孔,将C粉与Ti粉按化学计量配置,再加入C粉与Ti粉总量10~20%wt的Ni粉,混匀后制成混合料,用液压机在挤压模具中将混合料压成孔隙率为25~35%的预制块,从挤压模具中顶出预制块后,放入所述蜂窝钢板的蜂窝孔中,然后一起放在钢板基体表面,300℃±10℃一起预热后,保温20min±5 min,用交流电阻点焊机点焊焊合,点焊配以尺寸与蜂窝钢板的蜂窝孔相配的蜂窝形电极,最后用带极堆焊机在其表面堆焊上一层合金钢,即成蜂窝陶瓷夹层板。
2.根据权利要求1所述的一种电阻点焊辅助自蔓延在钢板表面制备蜂窝陶瓷夹层板方法,其特征在于:所述电极压力50kN,电流18kA,焊接时间10s±2 s。